The AC corrosion and SCC mechanism of X80 pipeline steel in near-neutral pH solution

被引：19

作者：

Wan, Hongxia ^{[1
]}

Song, Dongdong ^{[2
]}

Cai, Yong ^{[1
]}

Du, Cuiwei ^{[3
]}

机构：

[1] China Univ Petr, Dept Mat Sci & Engn, Beijing Key Lab Failure Corros & Protect Oil Gas, Beijing 102249, Peoples R China

[2] Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Peoples R China

[3] Univ Sci & Technol Beijing, Corros & Protect Ctr, Beijing 100083, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2020年 / 118卷 / 118期

基金：

中国国家自然科学基金;

关键词：

X80; steel; AC corrosion mechanism; SCC mechanism; Finite element analysis; ALTERNATING-CURRENT; CRACKING BEHAVIOR; ANODIC-DISSOLUTION; PITTING CORROSION; HYDROGEN;

D O I：

10.1016/j.engfailanal.2020.104904

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This paper studied the mechanism of alternating current (AC) promoting corrosion and improving SCC susceptibility in near-neutral pH solution. It was found that AC can result in local corrosion. X80 steel generated some pitting under the effect of full wave AC for the anodic dissolution. Some acuity pitting generated due that hydrogen induced anodic dissolution for negative half-wave AC. However, X80 steel generated some larger radius pitting for the positive half wave AC which was related to anodic dissolution. AC can facilitate ion migration from the result of crack propagation experiment. The SCC susceptibility of X80 steel in NS4 near neutral pH solution was negative half wave AC > full wave AC > positive half wave AC. The finite element results showed that AC can promote hydrogen precipitation. AC promoted X80 steel corrosion for facilitating ion migration and improved SCC susceptibility for assisting hydrogen precipitation.

引用

页数：15

共 50 条

[31] Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution
Zhu, Min
Du, Cuiwei
Li, Xiaogang
Liu, Zhiyong
Li, Hao
Zhang, Dawei
CORROSION SCIENCE, 2014, 87 : 224 - 232
[32] Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution
Du, Cuiwei (zmii666@126.com), 1600, Elsevier Ltd (87):
[33] Corrosion behavior of X-70 pipe steel in near-neutral pH solution
Niu, L.
Cheng, Y. F.
APPLIED SURFACE SCIENCE, 2007, 253 (21) : 8626 - 8631
[34] Micro-electrochemical characterization of corrosion of welded X70 pipeline steel in near-neutral pH solution
Zhang, G. A.
Cheng, Y. F.
CORROSION SCIENCE, 2009, 51 (08) : 1714 - 1724
[35] Effect of Dissolved Oxygen on Stress Corrosion Cracking of X70 Pipeline Steel in Near-Neutral pH Solution
Liu, Z. Y.
Li, X. G.
Du, C. W.
Wang, L. X.
Huang, Y. Z.
CORROSION, 2010, 66 (01)
[36] Electrochemical potential dependence of SCC initiation in X60 pipeline steel in near-neutral pH environment
Zhang, Ci
Wang, Hantong
He, Yinsheng
Zheng, Wenyue
Wang, Yao
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 27 : 4950 - 4961
[37] Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steel
W. Chen
F. King
T. R. Jack
M. J. Wilmott
Metallurgical and Materials Transactions A, 2002, 33 : 1429 - 1436
[38] Fractal characteristics of AC corrosion morphology of X80 pipeline steel in coastal soil solution
Fu, Yu
Kou, Jie
Du, Cuiwei
ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (06) : 868 - 878
[39] Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steel
Chen, W
King, F
Jack, TR
Wilmott, MJ
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (05): : 1429 - 1436
[40] Initiation of Stress Corrosion Cracks in X80 and X100 Pipe Steels in Near-Neutral pH Environment
Jidong Kang
Wenyue Zheng
Darren Bibby
Babak Shalchi Amirkhiz
Jian Li
Journal of Materials Engineering and Performance, 2016, 25 : 227 - 240

← 1 2 3 4 5 →