The AC corrosion and SCC mechanism of X80 pipeline steel in near-neutral pH solution

被引：19

作者：

Wan, Hongxia ^{[1
]}

Song, Dongdong ^{[2
]}

Cai, Yong ^{[1
]}

Du, Cuiwei ^{[3
]}

机构：

[1] China Univ Petr, Dept Mat Sci & Engn, Beijing Key Lab Failure Corros & Protect Oil Gas, Beijing 102249, Peoples R China

[2] Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Peoples R China

[3] Univ Sci & Technol Beijing, Corros & Protect Ctr, Beijing 100083, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2020年 / 118卷 / 118期

基金：

中国国家自然科学基金;

关键词：

X80; steel; AC corrosion mechanism; SCC mechanism; Finite element analysis; ALTERNATING-CURRENT; CRACKING BEHAVIOR; ANODIC-DISSOLUTION; PITTING CORROSION; HYDROGEN;

D O I：

10.1016/j.engfailanal.2020.104904

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This paper studied the mechanism of alternating current (AC) promoting corrosion and improving SCC susceptibility in near-neutral pH solution. It was found that AC can result in local corrosion. X80 steel generated some pitting under the effect of full wave AC for the anodic dissolution. Some acuity pitting generated due that hydrogen induced anodic dissolution for negative half-wave AC. However, X80 steel generated some larger radius pitting for the positive half wave AC which was related to anodic dissolution. AC can facilitate ion migration from the result of crack propagation experiment. The SCC susceptibility of X80 steel in NS4 near neutral pH solution was negative half wave AC > full wave AC > positive half wave AC. The finite element results showed that AC can promote hydrogen precipitation. AC promoted X80 steel corrosion for facilitating ion migration and improved SCC susceptibility for assisting hydrogen precipitation.

引用

页数：15

共 50 条

[21] Effect of DC Currents and Strain on Corrosion of X80 Steel in a Near-Neutral Environment
Ma, Zeyu
Wu, Wei
Zhao, Pengxiong
Dan, Yong
METALS, 2021, 11 (10)
[22] Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution
Yao Yang
Y. Frank Cheng
Journal of Materials Engineering and Performance, 2016, 25 : 4988 - 4995
[23] Stress corrosion cracking of X80 steel heat-affected zone in a near-neutral pH solution containing Bacillus cereus
Liu, Bo
Yang, Jike
Du, Cuiwei
Liu, Zhiyong
Wu, Wei
Li, Xiaogang
NPJ MATERIALS DEGRADATION, 2023, 7 (01)
[24] Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution
Yang, Yao
Cheng, Y. Frank
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (11) : 4988 - 4995
[25] Nitrate-reducing-bacteria assisted hydrogen embrittlement of X80 steel in a near-neutral pH solution
Liu, Bo
Liu, Menghao
Liu, Zhiyong
Du, Cuiwei
Li, Xiaogang
CORROSION SCIENCE, 2022, 202
[26] STRESS-CORROSION CRACK INITIATION IN X-52 PIPELINE STEEL IN NEAR-NEUTRAL PH SOLUTION
Fang, B.
Eadie, R.
Elboujdaini, M.
PROCEEDINGS OF THE ASME INTERNATIONAL PIPELINE CONFERENCE 2010, VOL 1, 2010, : 347 - 356
[27] Synergistic Effects of Hydrogen and Stress on Corrosion of X100 Pipeline Steel in a Near-Neutral pH Solution
Zhang, C.
Cheng, Y. F.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (09) : 1284 - 1289
[28] Synergistic Effects of Hydrogen and Stress on Corrosion of X100 Pipeline Steel in a Near-Neutral pH Solution
C. Zhang
Y. F. Cheng
Journal of Materials Engineering and Performance, 2010, 19 : 1284 - 1289
[29] SOME FACTORS AFFECTING INITIATION OF STRESS CORROSION CRACKING OF AN X80 PIPE STEEL IN NEAR-NEUTRAL pH ENVIRONMENT
Kang, Jidong
Bibby, Darren
Gianetto, James A.
Gesing, Mark
Arafin, Muhammad
PROCEEDINGS OF THE 12TH INTERNATIONAL PIPELINE CONFERENCE, 2018, VOL 1, 2018,
[30] Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution
Zhu, Min
Du, Cuiwei
Li, Xiaogang
Liu, Zhiyong
Li, Hao
Zhang, Dawei
Corrosion Science, 2014, 87 : 224 - 232

← 1 2 3 4 5 →