Open hole fatigue testing of laser machined MD-CFRPs

被引：28
|
作者：
Kalyanasundaram, Dinesh [1 ]
Gururaja, Suhasini [2 ]
Prabhune, Prajakta [2 ]
Singh, Dilpreet [1 ]
机构：
[1] IIT, Ctr Biomed Engn, Delhi, India
[2] Indian Inst Sci IISc, Aerosp Engn, Bangalore 12, Karnataka, India
来源：
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING | 2018年 / 111卷
关键词：
Polymer-matrix composites (PMCs); Fatigue; CT analysis; Ultrasonics; Machining; FIBER-REINFORCED COMPOSITES; DAMAGE; DELAMINATION; STRENGTH; SPECIMENS; PLASTICS; LIFE; FRPS;
D O I：
10.1016/j.compositesa.2018.05.005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of fiber laser machining (FLM) on multi-directional carbon fiber reinforced plastics (MD-CFRP) with [0/90/45/ - 45]s lay-up was studied under tension-tension fatigue with stress ratio R = 0.1 for an open hole fatigue (OHF) test configuration. The FLM parameters were chosen to yield a heat affected zone (HAZ) corresponding to a damage factor of approximately 1.4. The growth of this initial damage under tension-tension fatigue was investigated using digital image correlation (DIC), and damage growth characterization was carried out using scanning acoustic microscopy (SAM) and micro computed tomography (micro-CT). The endurance limit of the MD-CFRPs was evaluated by examining the fatigue life at 70, 50 and 30% of its ultimate tensile strength. Results show a strong correlation of damage mode on the applied load levels like conventionally machined samples.
引用
收藏
页码：33 / 41
页数：9
相关论文
共 50 条
  • [41] Fatigue Behavior of 3D Braided Composites Containing an Open-Hole
    Liang, Shuangqiang
    Zhou, Qihong
    Mei, Haiyang
    Chen, Ge
    Ko, Frank
    POLYMERS, 2020, 12 (09)
  • [42] Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates
    Maneval, Victor
    Vedvik, Nils-Petter
    Echtermeyer, Andreas T.
    JOURNAL OF COMPOSITES SCIENCE, 2023, 7 (12):
  • [43] Experimental and analytical assessment of fatigue and crack propagation in cold worked open hole specimens
    Boni, L.
    Fanteria, D.
    Lanciotti, A.
    Polese, C.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2013, 36 (09) : 930 - 941
  • [44] Fatigue properties of monolithic and metal-laminated aluminium open-hole specimens
    Lanciotti, A.
    Polese, C.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2008, 31 (10) : 911 - 917
  • [45] APPLICATION OF HYPOTHESIS OF NONPROPAGATING FATIGUE CRACK TO PUSH-PULL FATIGUE TESTING OF INFINITE PLATE WITH AN ELLIPTICAL HOLE NOTCH
    FUKUHARA, H
    BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1974, 17 (103): : 12 - 21
  • [46] On Comparative Performance Testing of Prechamber and Open Chamber Laser Ignition
    Joshi, Sachin
    Loccisano, Frank
    Yalin, Azer P.
    Montgomery, Dave T.
    JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 2011, 133 (12):
  • [47] ON COMPARATIVE PERFORMANCE TESTING OF PRECHAMBER AND OPEN CHAMBER LASER IGNITION
    Joshi, Sachin
    Loccisano, Frank
    Yalin, Azer P.
    Montgomery, Dave T.
    PROCEEDINGS OF THE ASME INTERNAL COMBUSTION ENGINE DIVISION FALL TECHNICAL CONFERENCE, 2010, : 33 - 40
  • [48] Fatigue Testing of Laser Treated Endosseous Implants With an Internal Trilobe Connection
    Berg, Robert W.
    Kurtz, Kenneth S.
    Griggs, Jason A.
    Watanabe, Ikuya
    Coelho, Paulo G.
    EUROPEAN JOURNAL OF PROSTHODONTICS AND RESTORATIVE DENTISTRY, 2011, 19 (01): : 2 - 6
  • [49] Notched fatigue testing of Inconel 718 prepared by selective laser melting
    Witkin, D. B.
    Patel, D. N.
    Bean, G. E.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (01) : 166 - 177
  • [50] Fatigue properties of Scalmalloy® processed by laser powder bed fusion in as-built, chemically and conventionally machined surface condition
    Raab, Maximilian
    Bambach, Markus
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2023, 311
12345