An evaluation of shot peening, residual stress and stress relaxation on the fatigue life of AISI 4340 steel

被引：473

作者：

Torres, MAS

Voorwald, HJC

机构：

[1] State Univ Sao Paulo, Dept Mech, UNESP, FEG, BR-12516410 Guaratingueta, SP, Brazil

[2] State Univ Sao Paulo, Dept Mat & Technol, BR-12516410 Guaratingueta, SP, Brazil

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2002年 / 24卷 / 08期

关键词：

shot peening; residual stress; 4340; steel; fatigue;

D O I：

10.1016/S0142-1123(01)00205-5

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Shot peening is a method widely used to improve the fatigue strength of materials. through the creation of a compressive residual stress field (CRSF) in their surface layers. In the present research the gain in fatigue life of AISI 4340 steel, Used in landing gear. is evaluated under four Shot peening conditions. Rotating bending fatigue tests were conducted and the CRSF was measured by an X-ray tensometry prior and during fatigue tests. It was observed that relaxation of the CRSF occurred due to the fatigue process. In addition, the fractured fatigue specimens were investigated using a scanning electron microscope in order to obtain information about the crack initiation points. The evaluation of fatigue life, relaxation of CRSF and crack sources are discussed. (C) 2002 Elsevier Science Ltd. All rights reserved.

引用

页码：877 / 886

页数：10

共 50 条

[1] Effects of Conventional and Severe Shot Peening on Residual Stress and Fatigue Strength of Steel AISI 1060 and Residual Stress Relaxation Due to Fatigue Loading: Experimental and Numerical Simulation
Erfan Maleki
Gholam Hossein Farrahi
Kazem Reza Kashyzadeh
Okan Unal
Mario Gugaliano
Sara Bagherifard
Metals and Materials International, 2021, 27 : 2575 - 2591
[2] EFFECT OF SHOT PEENING ON RESIDUAL-STRESS AND FATIGUE LIFE OF A SPRING STEEL
FARRAHI, GH
LEBRUN, JL
COURATIN, D
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (02) : 211 - 220
[3] Effects of Conventional and Severe Shot Peening on Residual Stress and Fatigue Strength of Steel AISI 1060 and Residual Stress Relaxation Due to Fatigue Loading: Experimental and Numerical Simulation
Maleki, Erfan
Farrahi, Gholam Hossein
Reza Kashyzadeh, Kazem
Unal, Okan
Gugaliano, Mario
Bagherifard, Sara
METALS AND MATERIALS INTERNATIONAL, 2021, 27 (08) : 2575 - 2591
[4] Mechanical and microstructural study of residual stresses induced by shot peening on the fatigue strength of AISI 4340 steel
Torres, M
Voorwald, H
Nascimento, M
Souza, R
Pigatin, W
ADVANCES IN MECHANICAL BEHAVIOUR, PLASTICITY AND DAMAGE, VOLS 1 AND 2, PROCEEDINGS, 2000, : 1033 - 1038
[5] Improvement in the fatigue strength of chromium electroplated AISI 4340 steel by shot peening
Voorwald, H. J. C.
Silva, M. P.
Costa, M. Y. P.
Cioffi, M. O. H.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2009, 32 (02) : 97 - 104
[6] Effect of Shot-peening Residual Stress on Fatigue Life and Relaxation of TC4
Zhang, Hongwei
Zhang, Jiaqi
Gao, Shi
Yan, Xichao
Chen, Tao
CHINA SURFACE ENGINEERING, 2024, 37 (04) : 171 - 178
[7] Fretting fatigue and shot peening: a multiaxial fatigue criterion including residual stress relaxation
Vantadori, Sabrina
Vazquez Valeo, Jesus
Zanichelli, Andrea
TRIBOLOGY INTERNATIONAL, 2020, 151
[8] Residual stress influence on fatigue lifetimes of electroplated AISI 4340 high strength steel
Voorwald, H. J. C.
Rocha, P. C. F.
Cioffi, M. O. H.
Costa, M. Y. P.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (11) : 1084 - 1097
[9] Shot peening and stress peening of AISI 4140 at elevated temperatures -: Effects on fatigue strength and stability of residual stresses
Menig, R
Schulze, V
Vöhringer, O
Wick, A
HEAT TREATING, VOLS 1 AND 2, PROCEEDINGS, 2000, : 257 - 264
[10] Optimal shot peening residual stress profile for fatigue
Aguado-Montero, S.
Vazquez, J.
Navarro, C.
Dominguez, J.
THEORETICAL AND APPLIED FRACTURE MECHANICS, 2021, 116

← 1 2 3 4 5 →