Fatigue of steam turbine blades with damage on the leading edge

被引：18
|
作者：
Shlyannikov, V. N. [1 ]
Yarullin, R. R. [1 ]
Zakharov, A. P. [1 ]
机构：
[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia
来源：
20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷
基金：
俄罗斯基础研究基金会;
关键词：
elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;
D O I：
10.1016/j.mspro.2014.06.289
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.
引用
收藏
页码：1792 / 1797
页数：6
相关论文
共 50 条
  • [41] Taking Fatigue and Creep Damage into Account in Designing Turbine Blades.
    Dambrine, B.
    Mecanique, materiaux, electricite, 1987, (419): : 54 - 58
  • [42] Fatigue damage prevention on turbine blades: study of underplatform damper shape
    Berruti, T.
    Firrone, C. M.
    Pizzolante, M.
    Gola, M. M.
    DAMAGE ASSESSMENT OF STRUCTURES VII, 2007, 347 : 159 - +
  • [43] Fatigue Damage Monitoring of Wind Turbine Blades by Using the Kalman Filter
    Namura, Nobuo
    Muto, Kazuo
    Ueki, Yosuke
    Ueta, Ryo
    Takeda, Norio
    AIAA JOURNAL, 2021, 59 (12) : 5130 - 5140
  • [44] Fatigue Damage Assessment of Turbine Runner Blades Considering Sediment Wear
    Chen, Haifeng
    Pan, Jun
    Wang, Shuo
    Ma, Jianfeng
    Zhang, Weiliang
    APPLIED SCIENCES-BASEL, 2024, 14 (11):
  • [45] FATIGUE DAMAGE AND FAILURE OF STEAM TURBINE ROTORS BY TORSIONAL VIBRATIONS
    Bovsunovskii, A. P.
    Chernousenko, O. Yu.
    Shtefan, E. V.
    Bashta, D. A.
    STRENGTH OF MATERIALS, 2010, 42 (01) : 108 - 113
  • [46] On real-time fatigue damage prediction for steam turbine
    Xu, Bo
    Sun, Yongjian
    IFAC PAPERSONLINE, 2020, 53 (02): : 640 - 645
  • [47] Fatigue damage and failure of steam turbine rotors by torsional vibrations
    A. P. Bovsunovskii
    O. Yu. Chernousenko
    E. V. Shtefan
    D. A. Bashta
    Strength of Materials, 2010, 42 : 108 - 113
  • [48] Flutter of long blades in a steam turbine
    Rzadkowski, R.
    Kubitz, L.
    Gnesin, V
    Kolodyazhnaya, L.
    JOURNAL OF VIBRATION ENGINEERING & TECHNOLOGIES, 2018, 6 (04) : 289 - 296
  • [49] Flutter of long blades in a steam turbine
    R. Rzadkowski
    L. Kubitz
    V. Gnesin
    L. Kolodyazhnaya
    Journal of Vibration Engineering & Technologies, 2018, 6 : 289 - 296
  • [50] TITANIUM FOR STEAM-TURBINE BLADES
    RUST, TM
    STELTZ, WG
    JOURNAL OF METALS, 1982, 34 (09): : 42 - 47
12345