Fatigue of steam turbine blades with damage on the leading edge

被引：18
|
作者：
Shlyannikov, V. N. [1 ]
Yarullin, R. R. [1 ]
Zakharov, A. P. [1 ]
机构：
[1] Russian Acad Sci, Res Ctr Power Engn Problems, Lobachevsky St 2-31,Post Box 190, Kazan 420111, Russia
来源：
20TH EUROPEAN CONFERENCE ON FRACTURE | 2014年 / 3卷
基金：
俄罗斯基础研究基金会;
关键词：
elastic-plastic stress analysis; low-cycle fatigue test; mechanical properties; fatigue life; turbine blades; single edge notched round specimen; protective coating;
D O I：
10.1016/j.mspro.2014.06.289
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study is concerned with the assessment of the fatigue life of cracked steam turbine blades which operate under cyclic loading conditions. The turbine blades fatigue life estimation approach includes numerical stress-strain analysis of real rotor components, experimental study of fatigue and fracture resistance material properties and determination of crack growth rate characteristics on the round bar specimens with the single edge notch. Static and cyclic tests were performed to obtain the main mechanical properties and the fatigue life characteristics of blade's material after loading history. Both specimens with the initial surface state and specimens with high velocity air fuel (HVAF) coating were tested. As a result the fatigue life characteristics of blade's material were determined as a function of operating time. The fatigue crack growth study of surface flow was performed for round bar specimens with different initial single edge notch depth. Experimental constants describing the linear parts of the fatigue fracture diagrams were determined. (C) 2014 Published by Elsevier Ltd. Open access under CC BY license.
引用
收藏
页码：1792 / 1797
页数：6
相关论文
共 50 条
  • [31] Research on the aerodynamic performance of the wind turbine blades with leading-edge protuberances
    Zhang, Yinan
    Zhao, Mingzhi
    Zhang, Mingming
    OCEAN ENGINEERING, 2023, 280
  • [32] How leading edge roughness influences rain erosion of wind turbine blades?
    Tempelis, Antonios
    Jespersen, Kristine Munk
    Dyer, Kirsten
    Clack, Ashley
    Mishnaevsky Jr, Leon, Jr.
    WEAR, 2024, 552
  • [33] COMPARATIVE EXPERIMENTAL INVESTIGATION OF LEADING EDGE COOLING CONCEPTS OF TURBINE ROTOR BLADES
    Elfner, Maximilian
    Schulz, Achmed
    Bauer, Hans-Joerg
    Lehmann, Knut
    PROCEEDINGS OF THE ASME TURBO EXPO: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, 2018, VOL 5A, 2018,
  • [34] TRAILING EDGE EROSION PREVENTION IN STEAM TURBINE LAST STAGE ROTATING BLADES
    Suerken, Norbert
    Hofbauer, Alexander
    Pfaller, Dirk
    PROCEEDINGS OF ASME TURBO EXPO 2023: TURBOMACHINERY TECHNICAL CONFERENCE AND EXPOSITION, GT2023, VOL 10, 2023,
  • [35] TURBULENCE DISTORTION EFFECT ON LEADING EDGE NOISE FROM WIND TURBINE BLADES
    Nukala, Vasishta Bhargava
    Padhy, Chinmaya Prasad
    Canadian Acoustics - Acoustique Canadienne, 2023, 51 (03): : 42 - 43
  • [36] Numerical Investigation of Turbine Blades with Leading-Edge Tubercles in Uniform Current
    Chen, Shuling
    Liu, Yan
    Han, Changzhi
    Yan, Shiqiang
    Hong, Zhichao
    WATER, 2021, 13 (16)
  • [37] Prospective challenges in the experimentation of the rain erosion on the leading edge of wind turbine blades
    Bartolome, Luis
    Teuwen, Julie
    WIND ENERGY, 2019, 22 (01) : 140 - 151
  • [38] Corrosion-Fatigue Prediction Methodology for 12% Cr Steam Turbine Blades
    Salzman, Ronald
    Gandy, David
    Rieger, Neville
    Schoenbauer, Bernd
    Tschegg, Stefanie
    Zhou, Shengqi
    Turnbull, Alan
    PROCEEDINGS OF THE ASME POWER CONFERENCE, 2013, VOL 1, 2014,
  • [39] A Bayesian approach for fatigue damage diagnosis and prognosis of wind turbine blades
    Jaramillo, Francisco
    Martin Gutierrez, Jose
    Orchard, Marcos
    Guarini, Marcelo
    Astroza, Rodrigo
    MECHANICAL SYSTEMS AND SIGNAL PROCESSING, 2022, 174
  • [40] Fatigue damage monitoring of wind turbine blades by using the kalman filter
    1600, AIAA International (59):
12345