Joining of C/C composites by using B4C reinforced phosphate adhesive

被引：53
|
作者：
Wang, Mingchao [1 ]
Liu, Jiachen [1 ]
Du, Haiyan [1 ]
Hou, Feng [1 ]
Guo, Anran [1 ]
Liu, Shan [1 ]
Dong, Xue [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Key Lab Adv Ceram & Machining Technol, Minist Educ, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2014年 / 40卷 / 08期
基金：
中国国家自然科学基金;
关键词：
C; Fracture; Bonding; C/C composites; Heat-treatment; Mechanical characterization; CARBON-CARBON COMPOSITES; BONDING CARBON/CARBON COMPOSITES; ALUMINUM PHOSPHATE; FIBER COMPOSITES; OXIDATION; MICROSTRUCTURE; TEMPERATURE; BEHAVIOR; GLASS; PERFORMANCE;
D O I：
10.1016/j.ceramint.2014.03.123
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A B4C reinforced phosphate adhesive for bonding C/C composites was developed. The mechanical properties were tested at room temperature after bonded specimens were treated at different temperatures from room temperature to 1500 C. The results showed that the addition of B4C could greatly improve adhesive's mechanical properties due to the formation of borosilicate glass and the volume compensation came from B4C's oxidation. The shear strength of bonded specimens decreased gradually from 7.9 MPa at RT to 3.3 MPa at 900 degrees C; then it increased up to 4.1 MPa at 1300 degrees C; however, when the temperature was over 1300 degrees C, the value decreased again but still remained above 2 MPa. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：11581 / 11591
页数：11
相关论文
共 50 条
  • [31] B4C reinforced nanocrystalline aluminum composites: Synthesis, characterization, and cost analysis
    Schoenung, J.M., 2005, Institute of Metals and Materials Australasia (29):
  • [32] Structure and Properties of B4C - SiC Composites
    Yurii G. Tkachenko
    Viktor F. Britun
    Emmanuil V. Prilutskii
    Dzhemma Z. Yurchenko
    Galina A. Bovkun
    Powder Metallurgy and Metal Ceramics, 2005, 44 : 196 - 201
  • [33] Effect of B4C particle size on the mechanical properties of B4C reinforced aluminum matrix layered composite
    Xu, Guangye
    Yu, Yingshui
    Zhang, Yubo
    Li, Tingju
    Wang, Tongmin
    SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 2019, 26 (01) : 53 - 61
  • [34] Hardness and Wear Behaviours of Al Matrix Composites and Hybrid Composites Reinforced with B4C and SiC
    Yahya Hişman Çelik
    Erol Kilickap
    Powder Metallurgy and Metal Ceramics, 2019, 57 : 613 - 622
  • [35] Hardness and Wear Behaviours of Al Matrix Composites and Hybrid Composites Reinforced with B4C and SiC
    Celik, Yahya Hisman
    Kilickap, Erol
    POWDER METALLURGY AND METAL CERAMICS, 2019, 57 (9-10) : 613 - 622
  • [36] Relationship between the B4C reinforcement content and the properties of MAO films on the B4C/Al matrix composites
    Yingwei Song
    Mingyu Zhu
    Kaihui Dong
    En-Hou Han
    Surface Science and Technology, 2 (1):
  • [37] Microstructure and Mechanical Properties of Fine Structured B4C/2024 Al Composites with High B4C Content
    Zheng, Ruixiao
    Ma, Fengmei
    Zhang, Yitan
    Ma, Chaoli
    ADVANCED ENGINEERING MATERIALS, 2017, 19 (07)
  • [38] The deformation of B4C particle in the B4C/2024Al composites after high velocity impact
    Zhou, Zhisong
    Wu, Gaohui
    Jiang, Longtao
    Xu, Zhongguo
    Micron, 2014, 67 : 107 - 111
  • [39] Influence of B4C particle reinforcement on mechanical and machining properties of Al6061/B4C composites
    Karabulut, Sener
    Karakoc, Halil
    Citak, Ramazan
    COMPOSITES PART B-ENGINEERING, 2016, 101 : 87 - 98
  • [40] Synthesis of Fine B4C Powder Using B4C seeding in Carbothermal Reduction Process
    da Rocha, Rosa Maria
    Lourenco de Melo, Francisco Cristovao
    ADVANCED POWDER TECHNOLOGY VII, 2010, 660-661 : 948 - 953
12345