Joining of C/C composites by using B4C reinforced phosphate adhesive

被引：53
|
作者：
Wang, Mingchao [1 ]
Liu, Jiachen [1 ]
Du, Haiyan [1 ]
Hou, Feng [1 ]
Guo, Anran [1 ]
Liu, Shan [1 ]
Dong, Xue [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Key Lab Adv Ceram & Machining Technol, Minist Educ, Tianjin 300072, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2014年 / 40卷 / 08期
基金：
中国国家自然科学基金;
关键词：
C; Fracture; Bonding; C/C composites; Heat-treatment; Mechanical characterization; CARBON-CARBON COMPOSITES; BONDING CARBON/CARBON COMPOSITES; ALUMINUM PHOSPHATE; FIBER COMPOSITES; OXIDATION; MICROSTRUCTURE; TEMPERATURE; BEHAVIOR; GLASS; PERFORMANCE;
D O I：
10.1016/j.ceramint.2014.03.123
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A B4C reinforced phosphate adhesive for bonding C/C composites was developed. The mechanical properties were tested at room temperature after bonded specimens were treated at different temperatures from room temperature to 1500 C. The results showed that the addition of B4C could greatly improve adhesive's mechanical properties due to the formation of borosilicate glass and the volume compensation came from B4C's oxidation. The shear strength of bonded specimens decreased gradually from 7.9 MPa at RT to 3.3 MPa at 900 degrees C; then it increased up to 4.1 MPa at 1300 degrees C; however, when the temperature was over 1300 degrees C, the value decreased again but still remained above 2 MPa. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：11581 / 11591
页数：11
相关论文
共 50 条
  • [1] Examination of wear properties of Al/B4C composites reinforced with irregularly shaped B4C
    Topcu, Ismail
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2021, 22 (03): : 276 - 282
  • [2] Adhesive wear behaviour of B4C and SiC reinforced 4147 Al matrix composites (Al/B4C-A1/SiC)
    Ipek, R
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2005, 162 : 71 - 75
  • [3] Mechanical Properties of Polypropylene Based Composites Reinforced with B4C
    Dike, A. Sinan
    Mindivan, Harun
    ADVANCED MATERIALS RESEARCH III, 2013, 685 : 19 - 23
  • [4] Silicon Carbide whiskers reinforced polymer-based adhesive for joining C/C composites
    Wang, Mingchao
    Miao, Ran
    He, Junkai
    Xu, Xiqing
    Liu, Jiachen
    Du, Haiyan
    MATERIALS & DESIGN, 2016, 99 : 293 - 302
  • [5] Effect of volume fraction and size of B4C particles on production and microstructure properties of B4C reinforced aluminium alloy composites
    Canakci, A.
    Arslan, F.
    Varol, T.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (08) : 954 - 960
  • [6] Production of B4C/Al composites
    Sahin, FC
    Ozdemir, O
    Yucel, O
    EURO CERAMICS VII, PT 1-3, 2002, 206-2 : 1045 - 1048
  • [7] Processing and mechanical properties of B4C reinforced Al matrix composites
    Topcu, I.
    Gulsoy, H. O.
    Kadioglu, N.
    Gulluoglu, A. N.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 482 (1-2) : 516 - 521
  • [8] Processing and mechanical properties of B4C reinforced Al matrix composites
    Topcu, I.
    Gulsoy, H.O.
    Kadioglu, N.
    Gulluoglu, A.N.
    Journal of Alloys and Compounds, 2009, 482 (1-2): : 516 - 521
  • [9] Combustion synthesis of dense functionally graded B4C reinforced composites
    Zlotnikov, I
    Gotman, I
    Klinger, L
    Gutmanas, EY
    FUNCTIONALLY GRADED MATERIALS VIII, 2005, 492-493 : 685 - 691
  • [10] Preparation and Properties of B4C Reinforced Al/Ti Laminated Composites
    Zhou Bingwen
    Xu Hao
    Yi Yunge
    Meng Linggang
    Ya Bin
    Zhang Huanyue
    Zhang Xingguo
    RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (01) : 335 - 340
12345