High coercivity of ordered macroporous FePt films synthesized via colloidal templates

被引：24
|
作者：
Iskandar, F
Iwaki, T
Toda, T
Okuyama, K
机构：
[1] Hiroshima Univ, Grad Sch Engn, Dept Chem Engn, Higashihiroshima 7398527, Japan
[2] Japan Chem Innovat Inst, Hiroshima Joint Res Ctr Nanotechnol Particle Proj, Higashihiroshima 7398530, Japan
[3] Toda Kogyo Corp, Naka Ku, Hiroshima 7300847, Japan
来源：
NANO LETTERS | 2005年 / 5卷 / 07期
关键词：
D O I：
10.1021/nl050863w
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The preparation of a three-dimensionally (3D) ordered macroporous iron-platinum (FePt) film derived from monodisperse FePt nanoparticles (approximately 3 nm in diameter) and polystyrene latex particles (254 nm in diameter) is described. The prepared film has a hexagonally ordered porous structure and coercivity up to 10 kOe after annealing at a temperature of 600 degrees C. We also found that size of FePt particles was maintained at around 3 nm, even after annealing at a temperature of 600 degrees C.
引用
收藏
页码：1525 / 1528
页数：4
相关论文
共 50 条
  • [31] Magnetic reversal study of Au-FePt thin films with very high coercivity
    Yuan, FT
    Chen, SK
    Horng, L
    Tsai, JL
    IEEE TRANSACTIONS ON MAGNETICS, 2005, 41 (10) : 3346 - 3348
  • [32] Underlayer diffusion-induced enhancement of coercivity in high anisotropy FePt thin films
    Hu, J. F.
    Chen, J. S.
    Lim, B. C.
    Liu, B.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2008, 320 (22) : 3068 - 3070
  • [33] High coercivity FePt thin films with Ag intermediate layers deposited at 400°C
    Zhao, ZL
    Chen, JS
    Ding, J
    Yi, JB
    Liu, BH
    Wang, JP
    IEEE TRANSACTIONS ON MAGNETICS, 2005, 41 (10) : 3337 - 3339
  • [34] High coercivity and magnetic domain observation in epitaxially grown particulate FePt thin films
    Shima, T
    Takanashi, K
    Takahashi, YK
    Hono, K
    Li, GQ
    Ishio, S
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2003, 266 (1-2) : 171 - 177
  • [35] Ordered nanomaterial thin films via supported anodized alumina templates
    Es-Souni, Mohammed
    Habouti, Salah
    FRONTIERS IN MATERIALS, 2014, Frontiers Media S.A. (01):
  • [36] High coercivity SmCo5 synthesized with assistance of colloidal SiO2
    Hao Tang
    Mohammad Aref Hasen Mamakhel
    Mogens Christensen
    Scientific Reports, 11
  • [37] High coercivity SmCo5 synthesized with assistance of colloidal SiO2
    Tang, Hao
    Mamakhel, Mohammad Aref Hasen
    Christensen, Mogens
    SCIENTIFIC REPORTS, 2021, 11 (01)
  • [38] Lithographically Ordered FePt L10 Dots with High Coercivity for Logic-Conditioned Magnetic Nanostructures
    Crisan, Ovidiu
    Crisan, Alina Daniela
    CRYSTALS, 2024, 14 (01)
  • [39] High quality ordered macroporous titania films with large filling fraction
    Kuai, SL
    Bader, G
    Haché, A
    Truong, VV
    Hu, XF
    THIN SOLID FILMS, 2005, 483 (1-2) : 136 - 139
  • [40] Magnetic properties and microstructure study of high coercivity Au/FePt/Au trilayer thin films
    Chen, S. K.
    Yuan, F. T.
    Liao, W. M.
    Hsu, C. W.
    Horng, Lance
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2006, 303 (02) : E251 - E254
12345