High coercivity of ordered macroporous FePt films synthesized via colloidal templates

被引：24
|
作者：
Iskandar, F
Iwaki, T
Toda, T
Okuyama, K
机构：
[1] Hiroshima Univ, Grad Sch Engn, Dept Chem Engn, Higashihiroshima 7398527, Japan
[2] Japan Chem Innovat Inst, Hiroshima Joint Res Ctr Nanotechnol Particle Proj, Higashihiroshima 7398530, Japan
[3] Toda Kogyo Corp, Naka Ku, Hiroshima 7300847, Japan
来源：
NANO LETTERS | 2005年 / 5卷 / 07期
关键词：
D O I：
10.1021/nl050863w
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
The preparation of a three-dimensionally (3D) ordered macroporous iron-platinum (FePt) film derived from monodisperse FePt nanoparticles (approximately 3 nm in diameter) and polystyrene latex particles (254 nm in diameter) is described. The prepared film has a hexagonally ordered porous structure and coercivity up to 10 kOe after annealing at a temperature of 600 degrees C. We also found that size of FePt particles was maintained at around 3 nm, even after annealing at a temperature of 600 degrees C.
引用
收藏
页码：1525 / 1528
页数：4
相关论文
共 50 条
  • [21] Low-temperature fabrication of high-coercivity L10 ordered FePt magnetic thin films by sputtering
    Takahashi, YK
    Ohnuma, M
    Hono, K
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2001, 40 (12B): : L1367 - L1369
  • [22] Low-temperature fabrication of high-coercivity L10 ordered FePt magnetic thin films by sputtering
    Takahashi, Y.K.
    Ohnuma, M.
    Hono, K.
    2001, Japan Society of Applied Physics (40):
  • [23] Direct liquid phase synthesis of ordered L10 FePt colloidal particles with high coercivity using an Au nanoparticle seeding approach
    Tzitzios, Vasileios
    Basina, Georgia
    Tzitzios, Nikolaos
    Alexandrakis, Vasileios
    Hu, Xiaocao
    Hadjipanayis, George
    NEW JOURNAL OF CHEMISTRY, 2016, 40 (12) : 10294 - 10299
  • [24] Studies on late formation of 3D ordered macroporous materials through colloidal crystal templates
    Yang, Lili
    Ge, Dengteng
    Ding, Yanbo
    Zhao, Jiupeng
    JOURNAL OF POROUS MATERIALS, 2012, 19 (06) : 1023 - 1026
  • [25] Studies on late formation of 3D ordered macroporous materials through colloidal crystal templates
    Lili Yang
    Dengteng Ge
    Yanbo Ding
    Jiupeng Zhao
    Journal of Porous Materials, 2012, 19 : 1023 - 1026
  • [26] High-coercivity FePt nanoparticle assemblies embedded in silica thin films
    Yan, Q.
    Purkayastha, A.
    Singh, A. P.
    Li, H.
    Li, A.
    Ramanujan, R. V.
    Ramanath, G.
    NANOTECHNOLOGY, 2009, 20 (02)
  • [27] Graphitized pitch-based carbons with ordered nanopores synthesized by using colloidal crystals as templates
    Yoon, SB
    Chai, GS
    Kang, SK
    Yu, JS
    Gierszal, KP
    Jaroniec, M
    JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2005, 127 (12) : 4188 - 4189
  • [28] Electrochemical syntheses of highly ordered macroporous conducting polymers grown around self-assembled colloidal templates
    Bartlett, PN
    Birkin, PR
    Ghanem, MA
    Toh, CS
    JOURNAL OF MATERIALS CHEMISTRY, 2001, 11 (03) : 849 - 853
  • [29] Fabrication of Large-area 3-D Ordered Silver-coated Colloidal Crystals and Macroporous Silver Films Using Polystyrene Templates
    Zhu, Wen
    Wu, Yuanyuan
    Wang, Chengyin
    Zhang, Ming
    Dong, Guanxiu
    NANO-MICRO LETTERS, 2013, 5 (03) : 182 - 190
  • [30] Fabrication of Large-area 3-D Ordered Silver-coated Colloidal Crystals and Macroporous Silver Films Using Polystyrene Templates
    Wen Zhu
    Yuanyuan Wu
    Chengyin Wang
    Ming Zhang
    Guanxiu Dong
    Nano-Micro Letters, 2013, 5 : 182 - 190
12345