Microstructure of the Al2O3/Al2O3 joint brazed with Cu-Zn-Ti filler metal

被引：0
|
作者：
Fang, HY [1 ]
Yang, JG [1 ]
Yu, XY [1 ]
机构：
[1] Harbin Inst Technol, Natl Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY | 2001年 / 17卷
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microstructure and interface reactions of Al2O3 joints brazed by Cu-Zn-Ti alloy were studied by using SEM, EDS and XRD. The effects of brazing temperature and Ti content on interfacial reactions and microstructure were investigated, and the action of adding Zn into brazing alloy was also studied. TiO, Ti3Al and CuTi were formed at the interface of ceramics and the filler metal, while CuTi, Cu3Ti and alpha -Cu were found in the brazing. The thickness of the reaction layer increased with increasing of brazing temperature, under the same brazing process, the thickness increased with the Ti content.
引用
收藏
页码：S186 / S188
页数：3
相关论文
共 50 条
  • [31] Nanoindentation hardness, texture and microstructure of α-Al2O3 and κ-Al2O3 coatings
    Ruppi, S.
    Larsson, A.
    Flink, A.
    THIN SOLID FILMS, 2008, 516 (18) : 5959 - 5966
  • [32] Electron energy-loss spectroscopy at Cu/Al2O3 and Ti/Al2O3 interfaces
    Scheu, C
    Dehm, G
    Mullejans, H
    Ruhle, M
    INTERGRANULAR AND INTERPHASE BOUNDARIES IN MATERIALS, PT 1, 1996, 207 : 181 - 184
  • [33] EELS investigation of CVD α-Al2O3, κ-Al2O3 and γ-Al2O3 coatings
    Larsson, A
    Zackrisson, J
    Halvarsson, M
    Ruppi, S
    MICROBEAM ANALYSIS 2000, PROCEEDINGS, 2000, (165): : 235 - 236
  • [34] Quantitative analysis of Al2O3 particles in Al3Ti/Al2O3/Al composites
    Swiderska-Sroda, A
    Wejrzanowski, T
    Kurzydlowski, KJ
    Wyrzykowski, JW
    MATERIALS CHARACTERIZATION, 2003, 51 (2-3) : 141 - 146
  • [35] Fabrication of Cu dispersed Al2O3 nanocomposites using Al2O3/CuO and Al2O3/Cu-nitrate mixtures
    Oh, ST
    Lee, JS
    Sekino, T
    Niihara, K
    SCRIPTA MATERIALIA, 2001, 44 (8-9) : 2117 - 2120
  • [36] Processing and characterization of Al2O3 and Al2O3/Cu alloy composites
    McCuiston, RC
    Danforth, SC
    Niesz, DE
    ELECTROACTIVE POLYMERS AND RAPID PROTOTYPING, 2002, 698 : 257 - 261
  • [37] Microstructure and modifications of Cu/Al2O3 interfaces
    Scheu, C
    Stein, W
    Klein, S
    Wagner, T
    Tomsia, AP
    Rühle, M
    ZEITSCHRIFT FUR METALLKUNDE, 2001, 92 (07): : 707 - 711
  • [38] Bonding of Al2O3 to Cu with Ti foil
    陈铮
    方芳
    赵其章
    楼宏青
    李志章
    China Welding, 1998, (01) : 71 - 77
  • [39] EXAFS Characterization of Ti/Al2O3 Supports and Co/Ti/Al2O3 Catalysts
    Fay, M. J.
    Proctor, A.
    Hoffmann, D. P.
    Houalla, M.
    Mikrochimica Acta, 122 (3-4):
  • [40] EXAFS characterization of Ti/Al2O3 supports and Co/Ti/Al2O3 catalysts
    Fay, MJ
    Proctor, A
    Hoffmann, DP
    Houalla, M
    Hercules, DM
    MIKROCHIMICA ACTA, 1996, 122 (3-4) : 311 - 321
12345