Microstructure of the Al2O3/Al2O3 joint brazed with Cu-Zn-Ti filler metal

被引：0
|
作者：
Fang, HY [1 ]
Yang, JG [1 ]
Yu, XY [1 ]
机构：
[1] Harbin Inst Technol, Natl Key Lab Adv Welding Prod Technol, Harbin 150001, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY | 2001年 / 17卷
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microstructure and interface reactions of Al2O3 joints brazed by Cu-Zn-Ti alloy were studied by using SEM, EDS and XRD. The effects of brazing temperature and Ti content on interfacial reactions and microstructure were investigated, and the action of adding Zn into brazing alloy was also studied. TiO, Ti3Al and CuTi were formed at the interface of ceramics and the filler metal, while CuTi, Cu3Ti and alpha -Cu were found in the brazing. The thickness of the reaction layer increased with increasing of brazing temperature, under the same brazing process, the thickness increased with the Ti content.
引用
收藏
页码：S186 / S188
页数：3
相关论文
共 50 条
  • [21] Sintering behaviour and microstructures of Ti(Al,O)/Al2O3, Ti3Al(O)/Al2O3 and TiAl(O)/Al2O3 in situ composites
    Cai, ZH
    Zhang, DL
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 419 (1-2): : 310 - 317
  • [22] Microstructure evolution and bonding strength of the Al2O3/Al2O3 interface brazed via Ni-Ti intermetallic phases
    Lu, Yao
    Zhu, Meixiong
    Zhang, Qi
    Hu, Tao
    Wang, Juan
    Zheng, Kaihong
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2020, 40 (04) : 1496 - 1504
  • [23] Low cost Ti(Al,O)/Al2O3 and TixAly/Al2O3 composites
    Zhang, DL
    Cai, ZH
    Newby, M
    MATERIALS TECHNOLOGY, 2003, 18 (02) : 94 - 98
  • [24] Microstructure and mechanical property of Al2O3/Ti joint with biocompatibility
    Lin P.
    Lin T.
    He P.
    Wang M.
    Yang H.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (07): : 16 - 23
  • [25] Bond strength and microstructure investigation on Al2O3/Al/Al2O3 joints
    Ksiazek, M
    Sobczak, N
    Mikulowski, B
    Radziwilli, W
    Winiarski, B
    SURFACE AND INTERFACE ANALYSIS, 2004, 36 (08) : 673 - 676
  • [26] Effect of Al2O3 on the mechanical properties and microstructure of Ti3SiC2/Al2O3 composite
    Wang, HJ
    Jin, ZH
    Miyamoto, Y
    RARE METAL MATERIALS AND ENGINEERING, 2004, 33 (01) : 40 - 42
  • [27] Interfacial microstructure of Al2O3/Ti-6Al-4V joints brazed with (Ag72Cu28)97Ti3 filler metal
    Wu, MF
    Yu, ZS
    Liang, C
    Wang, FJ
    Qi, K
    MATERIALS SCIENCE AND TECHNOLOGY, 2002, 18 (03) : 341 - 344
  • [28] Effects of Al2O3 Particulates on the Thickness of Reaction Layer of Al2O3 Joints Brazed with Al2O3-Particulate-Contained Composite Filler Materials
    Jianguo YANG
    Journal of Materials Science & Technology, 2003, (05) : 509 - 510
  • [29] Effects of Al2O3 particulates on the thickness of reaction layer of Al2O3 joints brazed with Al2O3-particulate-contained composite filler materials
    Yang, JG
    Wu, JW
    Fang, HY
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 (05) : 509 - 510
  • [30] Microstructure and mechanical properties of Al2O3/Cu joints brazed with Ag-Cu-Ti plus Zn composite fillers
    Fan, Binbin
    Xu, Jingkun
    Lei, Huicong
    Zhao, Lin
    An, Di
    Xie, Zhipeng
    CERAMICS INTERNATIONAL, 2022, 48 (13) : 18551 - 18557
12345