Microstructure and mechanical properties of the Si3N4/42CrMo steel joints brazed with Ag-Cu-Ti plus Mo composite filler

被引：76

作者：

He, Y. M. ^{[1
]}

Zhang, J. ^{[1
]}

Sun, Y. ^{[1
]}

Liu, C. F. ^{[1
]}

机构：

[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2010年 / 30卷 / 15期

关键词：

Si3N4; Joining; Ag-Cu-Ti plus Mo composite filler; Microstructure; Mechanical properties; SILICON-NITRIDE; STRENGTH; CERAMICS;

D O I：

10.1016/j.jeurceramsoc.2010.07.005

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The Si3N4 ceramic was joined to 42CrMo steel using Ag-Cu-Ti + Mo composite filler. Effect of Mo particles content on the microstructure and mechanical properties of the joints were investigated. Defect-free joints were received when the Si3N4/42CrMo steel joints were brazed with Ag-Cu-Ti + Mo composite filler. The results show that a continuous reaction layer which is composed of TiN and Ti5Si3 was formed near the Si3N4 ceramic. A double reaction layer which consists of Fe2Ti and FeTi was also formed adjacent to 42CrMo steel, with Fe2Ti being located near the steel. The central part of the joint is composed of Ag based solid solution, Cu based solid solution, Mo particles and some Cu-Ti intermetallic compounds. The maximal bending strength reached 587.3 MPa with 10 vol.% Mo particles in the joint, at which the joint strength was 414.3% higher than the average strength for the case without Mo particles addition. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：3245 / 3251

页数：7

共 50 条

[1] Effect of Ti Content on Microstructure and Mechanical Properties of Si3N4/Si3N4 Joints Brazed with Ag-Cu-Ti plus Mo Composite Filler
Zhang, Jie
He, Yanming
PRICM 7, PTS 1-3, 2010, 654-656 : 2018 - 2021
[2] Microstructural characterization of Si3N4/42CrMo joint brazed with Ag-Cu-Ti plus TiNp composite filler
Wang, Tianpeng
Ivas, Toni
Leinenbach, Christian
Zhang, Jie
JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 651 : 623 - 630
[3] Effect of brazing temperature on microstructure and mechanical properties of Si3N4/Si3N4 joints brazed with Ag-Cu-Ti plus Mo composite filler
He, Y. M.
Zhang, J.
Wang, X.
Sun, Y.
JOURNAL OF MATERIALS SCIENCE, 2011, 46 (08) : 2796 - 2804
[4] Microstructure and mechanical properties of Si3N4/Si3N4 joint brazed with Ag-Cu-Ti plus SiCp composite filler
He, Y. M.
Zhang, J.
Liu, C. F.
Sun, Y.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (12): : 2819 - 2825
[5] Microstructure and mechanical properties of porous Si3N4/Invar joints brazed with Ag-Cu-Ti plus Mo/Cu/Ag-Cu multi-layered composite filler
Liu, J. Y.
Zhang, J.
Liu, C. F.
Wang, T. P.
CERAMICS INTERNATIONAL, 2017, 43 (15) : 11668 - 11675
[6] Microstructure and mechanical properties of Si3N4/42CrMo joints brazed with TiNp modified active filler
Wang, Tianpeng
Zhang, Jie
Liu, Chunfeng
Wang, Guochao
CERAMICS INTERNATIONAL, 2014, 40 (05) : 6881 - 6890
[7] Microstructure evolution of Si3N4/Si3N4 joint brazed with Ag-Cu-Ti plus SiCp composite filler
Zhang, J.
He, Y. M.
Sun, Y.
Liu, C. F.
CERAMICS INTERNATIONAL, 2010, 36 (04) : 1397 - 1404
[8] Effect of brazing temperature on microstructure and mechanical properties of Si3N4/Si3N4 joints brazed with Ag–Cu–Ti + Mo composite filler
Y. M. He
J. Zhang
X. Wang
Y. Sun
Journal of Materials Science, 2011, 46 : 2796 - 2804
[9] Microstructure and mechanical properties of BN-Si3N4 and AlON joints brazed with Ag-Cu-Ti filler alloy
Liu Mingxu
Liu, C. F.
Zhang, J.
Tao Rui
Zhang Qiang
Qi Qin
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2018, 38 (04) : 1265 - 1270
[10] Microstructure and corrosion behavior of Si3N4/316L joints brazed with Ag-Cu/Ag/Mo/Ag/Ag-Cu-Ti multilayer filler
Guo, Songsong
Sun, Liangbo
Zheng, Zhen
Fang, Jian
Wen, Yue
Liu, Chunfeng
Zhang, Jie
ELECTROCHIMICA ACTA, 2021, 379

← 1 2 3 4 5 →