Oxidation behaviour of a Ge-modified silicide coating on an Nb-Si based alloy in the moderate temperature range

被引：32
|
作者：
Wang, Changliang [1 ]
Shao, Wei [1 ,2 ]
Wang, Wan [1 ]
Zhou, Chungen [1 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Dept Mat Sci & Engn, Beijing 100191, Peoples R China
[2] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100124, Peoples R China
来源：
CORROSION SCIENCE | 2020年 / 163卷
基金：
中国国家自然科学基金; 国家重点研发计划;
关键词：
Intermetallics; Oxidation; Selective oxidation; MECHANICAL-PROPERTIES; TI; CR; AL; MICROSTRUCTURE; RESISTANCE; MO; HF; COMPOSITES; DEPOSITION;
D O I：
10.1016/j.corsci.2019.108249
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The oxidation characteristics of Ge-modified silicide coating on the Nb-Si based alloy within the moderate temperatures were investigated. Results show that the mass gains of the coated alloys are 0.41, 0.58 and 0.37 mg/cm(2) after oxidation at 700 degrees C, 750 degrees C and 800 degrees C for 100 h. There is no pest phenomenon at the test temperatures. The oxide scale is composed of amorphous aluminosilica and SiO2-GeO2 with TiO2 dispersed in some of SiO2-GeO2. The good oxidation resistance of the Ge-modified silicide coating at moderate temperatures is attributed to the selective oxidation of Ti and Si, as well as the formation of glassy SiO2-GeO2.
引用
收藏
页数：8
相关论文
共 50 条
  • [1] Characterization of microstructure and oxidation resistance of Y and Ge modified silicide coating on Nb-Si based alloy
    Wang, Wan
    Zhou, Chungen
    CORROSION SCIENCE, 2016, 110 : 114 - 122
  • [2] Deposition of a B-modified silicide coating for Nb-Si based alloy oxidation protection
    Shao, Wei
    Wang, Wan
    Zhou, Chungen
    CORROSION SCIENCE, 2016, 111 : 786 - 792
  • [3] Oxidation behavior of the B-modified silicide coating on Nb-Si based alloy at intermediate temperatures
    Shao, Wei
    Zhou, Chungen
    CORROSION SCIENCE, 2018, 132 : 107 - 115
  • [4] Compression deformation behavior of silicide coating on Nb-Si based alloy
    Qiao, Yanqiang
    Zhang, Weiping
    Ran, Wenxu
    Guo, Xiping
    INTERMETALLICS, 2022, 147
  • [5] Microstructure and oxidation resistance of Ti modified Si-Mo coating on Nb-Si based ultrahigh temperature alloy
    Li, Longfei
    Guo, Xiping
    CORROSION SCIENCE, 2023, 220
  • [6] Characterization of micromechanical properties of Al, Y-modified silicide coating on Nb-Si based alloy
    Ran, Wenxu
    Qiao, Yanqiang
    Guo, Xiping
    SURFACE & COATINGS TECHNOLOGY, 2022, 443
  • [7] Corrosion resistance characteristics of silicide coating on Nb-Si based alloy exposed to CMAS at high temperature
    Zhang, Weiping
    Qiao, Yanqiang
    Guo, Xiping
    SURFACE & COATINGS TECHNOLOGY, 2024, 482
  • [8] Formation and oxidation resistance of Hf and Al modified suicide coating on Nb-Si based alloy
    Wang, Wan
    Zhang, Binyu
    Zhou, Chungen
    CORROSION SCIENCE, 2014, 86 : 304 - 309
  • [9] Investigation of scale formation and degeneration of silicide coating on Nb-Si based alloy in the temperature range from 1250 °C to 1560 °C
    Zhang, Weiping
    Qiao, Yanqiang
    Guo, Xiping
    INTERMETALLICS, 2024, 172
  • [10] Oxidation and interdiffusion behavior of a germanium-modified silicide coating on an Nb–Si-based alloy
    Jin-long Li
    Wan Wang
    Chun-gen Zhou
    International Journal of Minerals Metallurgy and Materials, 2017, 24 (03) : 289 - 296