Fatigue crack growth rate under different bending to torsion ratios in 10HNAP steel

被引：0
|
作者：
Marciniak, Zbigniew [1 ]
Rozumek, Dariusz [1 ]
机构：
[1] Opole Univ Technol, Dept Mech & Machine Design, PL-45271 Opole, Poland
来源：
MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE | 2011年 / 465卷
关键词：
plane specimens; fatigue crack growth; bending with torsion;
D O I：
10.4028/www.scientific.net/KEM.465.187
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The paper contains the fatigue test results of rectangular cross-section specimens made of 10HNAP steel. The specimen height to width ratio was 1.5. Bending with torsion tests were carried out for the following ratios of bending to torsional moments M-aB / M-aT = 0.47, 0.94, 1.87 and the loading frequency 26.5 Hz. The tests were performed in a high cycle fatigue regime for the stress ratio R = - 1 and phase shift between bending and torsion loading equal to phi = 0.
引用
收藏
页码：187 / 190
页数：4
相关论文
共 50 条
  • [21] Crack growth rate under cyclic bending in the explosively welded steel/titanium bimetals
    Rozumek, Dariusz
    Banski, Robert
    MATERIALS & DESIGN, 2012, 38 : 139 - 146
  • [22] Studies of the Fatigue Crack Growth Rate and Crack Shapes in High-Strength Steel During Cyclic Bending.
    Kocanda, Stanislaw
    Likowski, Andrzej
    Mechanika Teoretyczna i Stosowana, 1979, 17 (04): : 603 - 622
  • [23] Effect of microstructure on the fatigue crack growth behavior of 9%Cr martensitic steel at different stress ratios under 630 °C
    Wang, Quanyi
    Yang, Fei
    Zou, Tongfei
    Liu, Meng
    Jiang, Yunqing
    Pei, Yubing
    Zhang, Hong
    Liu, Yongjie
    Wang, Qingyuan
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 175
  • [24] Experimental and probabilistic study of fatigue crack growth behavior of steel Q345qC under different stress ratios
    Ke, Lu
    Li, Youlin
    Li, Chuanxi
    Feng, Zheng
    Zhu, Furui
    Liang, Longming
    Mei, Shuyu
    CONSTRUCTION AND BUILDING MATERIALS, 2023, 393
  • [25] FATIGUE CRACK GROWTH IN AlCu4Mg1 UNDER NONPROPORTIONAL BENDING-WITH-TORSION LOADING
    Rozumek, D.
    Marciniak, Z.
    MATERIALS SCIENCE, 2011, 46 (05) : 685 - 694
  • [26] Fatigue crack growth in AlCu4Mg1 under nonproportional bending-with-torsion loading
    D. Rozumek
    Z. Marciniak
    Materials Science, 2011, 46 : 685 - 694
  • [27] The retardation effect of static torsion on fatigue crack growth in strip steel
    Lu, Yun-chao
    Chen, Te
    Yang, Feng-peng
    Lan, Tian
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2020, 43 (08) : 1800 - 1813
  • [28] Fatigue crack growth in titanium and aluminium alloys under bending
    Rozumek, Dariusz
    Macha, Ewald
    MATERIALS STRUCTURE & MICROMECHANICS OF FRACTURE V, 2008, 567-568 : 317 - 320
  • [29] Fatigue crack growth in round bars under rotary bending
    Brighenti, R
    Carpinteri, A
    Filippini, G
    Spagnoli, A
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 175 - 180
  • [30] Fatigue crack growth in cantilever bending under displacement control
    Abd-Allah, NM
    Megahed, MM
    Eleiche, AM
    JOURNAL OF TESTING AND EVALUATION, 2002, 30 (02) : 124 - 135
12345