Fracture toughness evolution of a carbon/carbon composite after low-cycle fatigue

被引：6
|
作者：
Stepashkin, A. A. [1 ]
Ozherelkov, D. Yu [1 ]
Sazonov, Yu B. [1 ]
Komissarov, A. A. [1 ]
机构：
[1] Natl Univ Sci & Technol MISIS, Moscow 119991, Russia
来源：
ENGINEERING FRACTURE MECHANICS | 2019年 / 206卷
关键词：
Carbon/carbon composites (CCCs); Compression fatigue; Low cycle fatigue; J-Integral; CARBON-CARBON COMPOSITE; TENSILE FATIGUE; MECHANICAL-PROPERTIES; MATRIX COMPOSITES; BEHAVIOR; 2D; DAMAGE; IMPROVEMENT; FREQUENCY; STRENGTH;
D O I：
10.1016/j.engfracmech.2018.12.018
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
High fracture resistance of carbon/carbon (C/C) composites as a material for aircraft braking systems is essential for their safe service. This paper presents a study on fatigue behavior and residual mechanical properties after cyclic load of discretely-reinforced C/C composite. The influence of cyclic loads on the fracture toughness of frictional C/C composite was examined. Results of fracture toughness tests after compression fatigue load were determined using the ASTM single-notch three point bend test and correlated with fracture surface using scanning electron microscopy (SEM). It is revealed that C/C composite fracture toughness strongly depends on the fiber-matrix interfacial bonding strength. Cyclic loads below fatigue limit improve residual fracture toughness of the material up to 25% by the mechanism of interfaces weakening. Cyclic loads above fatigue limit decrease residual fracture toughness of the material by the fracture of carbon fibers. Observed results may be useful in developing friction C/C composites to enhance fracture resistance in aircraft braking systems, increasing safety and operating lifetime.
引用
收藏
页码：442 / 451
页数：10
相关论文
共 50 条
  • [31] LOW-CYCLE FATIGUE OF CARBON-STEEL IN HIGH-TEMPERATURE WATER ENVIRONMENT
    HIGUCHI, M
    SAKAMOTO, H
    TANIOKA, S
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1982, 22 (12) : B402 - B402
  • [32] SLIDING BAND DEVELOPMENT DURING LOW-CYCLE FATIGUE IN MEDIUM-CARBON STEEL
    DURYAGIN, VA
    KUSLITSKIY, AB
    PISTUN, IP
    FIZIKA METALLOV I METALLOVEDENIE, 1980, 50 (05): : 1114 - 1117
  • [33] The influence of cyclic fatigue damage on the fracture toughness of carbon-carbon composites
    Ozturk, A
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1996, 27 (08) : 641 - 646
  • [34] EFFECTS OF CARBON AND SILICON ON SOFTENING IN LOW-CYCLE FATIGUE OF AUSTENITIC STAINLESS-STEELS
    SHIBATA, K
    KOGITA, M
    CHEN, CS
    FUJITA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1988, 28 (05) : 406 - 412
  • [35] Damage Accumulation in Carbon Steel Under High-Temperature Low-Cycle Fatigue
    Romanov, A. N.
    MECHANICS, RESOURCE AND DIAGNOSTICS OF MATERIALS AND STRUCTURES (MRDMS-2020): PROCEEDING OF THE 14TH INTERNATIONAL CONFERENCE ON MECHANICS, RESOURCE AND DIAGNOSTICS OF MATERIALS AND STRUCTURES, 2020, 2315
  • [36] Low-Cycle Fatigue of the Weld Metal of a Low-Carbon Steel Welded Joint after High-Temperature Action
    S. A. Nikulin
    S. O. Rogachev
    V. A. Belov
    N. V. Shplis
    M. Yu. Zadorozhnyi
    Russian Metallurgy (Metally), 2023, 2023 : 1501 - 1509
  • [37] Fracture toughness of low carbon steels and their weldments
    Timofeev, BT
    Blumin, AA
    Anikovsky, VV
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1998, 75 (13) : 945 - 950
  • [38] Low-Cycle Fatigue of the Weld Metal of a Low-Carbon Steel Welded Joint after High-Temperature Action
    Nikulin, S. A.
    Rogachev, S. O.
    Belov, V. A.
    Shplis, N. V.
    Zadorozhnyi, M. Yu.
    RUSSIAN METALLURGY, 2023, 2023 (10): : 1501 - 1509
  • [39] Low-cycle tensile fatigue behavior of a SiC/SiC composite
    Ames Lab, Ames, United States
    Ceram Eng Sci Proc, 4 (157-165):
  • [40] NUMERICAL MODELING OF LOW-CYCLE FATIGUE OF FIBER REINFORCED COMPOSITE
    Majerski, Krzysztof
    Surowska, Barbara
    Bienias, Jaroslaw
    COMPOSITES THEORY AND PRACTICE, 2014, 14 (04): : 197 - 202
12345