Fracture toughness evolution of a carbon/carbon composite after low-cycle fatigue

被引：6
|
作者：
Stepashkin, A. A. [1 ]
Ozherelkov, D. Yu [1 ]
Sazonov, Yu B. [1 ]
Komissarov, A. A. [1 ]
机构：
[1] Natl Univ Sci & Technol MISIS, Moscow 119991, Russia
来源：
ENGINEERING FRACTURE MECHANICS | 2019年 / 206卷
关键词：
Carbon/carbon composites (CCCs); Compression fatigue; Low cycle fatigue; J-Integral; CARBON-CARBON COMPOSITE; TENSILE FATIGUE; MECHANICAL-PROPERTIES; MATRIX COMPOSITES; BEHAVIOR; 2D; DAMAGE; IMPROVEMENT; FREQUENCY; STRENGTH;
D O I：
10.1016/j.engfracmech.2018.12.018
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
High fracture resistance of carbon/carbon (C/C) composites as a material for aircraft braking systems is essential for their safe service. This paper presents a study on fatigue behavior and residual mechanical properties after cyclic load of discretely-reinforced C/C composite. The influence of cyclic loads on the fracture toughness of frictional C/C composite was examined. Results of fracture toughness tests after compression fatigue load were determined using the ASTM single-notch three point bend test and correlated with fracture surface using scanning electron microscopy (SEM). It is revealed that C/C composite fracture toughness strongly depends on the fiber-matrix interfacial bonding strength. Cyclic loads below fatigue limit improve residual fracture toughness of the material up to 25% by the mechanism of interfaces weakening. Cyclic loads above fatigue limit decrease residual fracture toughness of the material by the fracture of carbon fibers. Observed results may be useful in developing friction C/C composites to enhance fracture resistance in aircraft braking systems, increasing safety and operating lifetime.
引用
收藏
页码：442 / 451
页数：10
相关论文
共 50 条
  • [21] THE LOW-CYCLE IMPACT FATIGUE PROPERTIES OF PEARLITIC PLAIN CARBON-STEELS
    JOHNSON, DN
    JOHNSON, AA
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1985, 8 (03) : 287 - 294
  • [22] Fatigue life prediction of carbon steel with machined surface layer under low-cycle fatigue
    Hasunuma, Shota
    Oki, Shingo
    Motomatsu, Kazuaki
    Ogawa, Takeshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 123 : 255 - 267
  • [23] The fatigue properties, microstructural evolution and crack behaviors of low-carbon carbide-free bainitic steel during low-cycle fatigue
    Zhou, Qian
    Qian, Lihe
    Meng, Jiangying
    Zhao, Leijie
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 820
  • [24] Effect of hydrogen absorption on strain-induced low-cycle fatigue of low carbon steel
    Tsuchida, Y.
    Watanabe, T.
    Kato, T.
    Seto, T.
    FATIGUE 2010, 2010, 2 (01): : 555 - 561
  • [25] Low-cycle fatigue strength reduction factor of notched components for low-carbon steels
    Morimoto, A
    Saito, A
    Matsumoto, E
    LOCALIZED DAMAGE IV: COMPUTER-AIDED ASSESSMENT AND CONTROL, 1996, : 187 - 194
  • [26] Effect of Mn content on low-cycle fatigue behaviors of low-carbon bainitic steel
    Long, X. Y.
    Zhang, F. C.
    Zhang, C. Y.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 697 : 111 - 118
  • [27] Initial aspects of low-cycle fatigue fracture of martensitic steels
    Eterashvili, T.
    Dzigrashvili, T.
    Vardosanidze, M.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VI, 2007, 348-349 : 385 - +
  • [28] Criteria for Evaluating the Fracture Toughness of Carbon-Carbon Composite Materials
    Stepashkin, A. A.
    Ozherelkov, D. Yu.
    Sazonov, Yu. B.
    Komissarov, A. A.
    METAL SCIENCE AND HEAT TREATMENT, 2018, 60 (3-4) : 266 - 272
  • [29] STRENGTH, FRACTURE TOUGHNESS, AND LOW-CYCLE FATIGUE BEHAVIOR OF 17-4 PH STAINLESS-STEEL
    RACK, HJ
    KALISH, D
    METALLURGICAL TRANSACTIONS, 1974, 5 (07): : 1595 - 1605
  • [30] FRACTURE-TOUGHNESS AND LOW-CYCLE FATIGUE OF 6061/AL2O3P COMPOSITES
    HUNG, NP
    ZHOU, W
    PEH, ET
    CHAN, CS
    COMPOSITES ENGINEERING, 1995, 5 (05): : 509 - 517
12345