Fatigue failure behavior of glass/epoxy ±55 filament wound pipes under internal pressure

被引：88
|
作者：
Tarakçioglu, N
Gemi, L
Yapici, A [1 ]
机构：
[1] Selcuk Univ, Dept Mech Engn, TR-42075 Konya, Turkey
[2] Selcuk Univ, Tech Educ Fac, TR-42075 Konya, Turkey
来源：
COMPOSITES SCIENCE AND TECHNOLOGY | 2005年 / 65卷 / 3-4期
关键词：
fatigue; filament winding;
D O I：
10.1016/j.compscitech.2004.10.002
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
In this study, fatigue behavior of filament wound composite pipes under alternating internal pressure has been investigated. GRP pipes which made of E-glass/epoxy are tested under open ended conditions. Test specimens have four layers which have +/-55degrees winding angle. Tests have been done in accordance with ASTM D-2992. This standards offers 0.42 Hz frequency and R = 0.05 stress ratio. Tests have been performed at different load levels from 30% to 70% of ultimate strength. Whitening, leakage and final failure levels of GRP pipes have been observed. Fatigue results are presented and interpreted by means of S-N curves. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：703 / 708
页数：6
相关论文
共 50 条
  • [21] Enhanced fatigue performances of hybrid nanoreinforced filament wound carbon/epoxy composite pipes
    Ustun, Tugay
    Eskizeybek, Volkan
    Avci, Ahmet
    COMPOSITE STRUCTURES, 2016, 150 : 124 - 131
  • [22] Stiffness and strength of filament-wound fiber-reinforced composite pipes under internal pressure
    Takayanagi, H
    Xia, M
    Kemmochi, K
    ADVANCED COMPOSITE MATERIALS, 2002, 11 (02) : 137 - 149
  • [23] Experimental and numerical investigation of adhesively bonded ± 55° filament wound tubular specimens under internal pressure
    Braiek, Sonia
    Ben Khalifa, Ated
    Zitoune, Redouane
    Zidi, Mondher
    ENGINEERING FRACTURE MECHANICS, 2018, 199 : 461 - 475
  • [24] Failure Analysis of Glass-Reinforced Epoxy Pipes Under Internal Hydrostatic Pressure: A Comparison With the Split Disk Test Method
    Mandavi, H. R.
    Rahimi, G. H.
    Farrokhabadi, A.
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2018, 140 (01):
  • [25] Fatigue Crack Growth Behavior of Filament Wound Composite Pipes in Corrosive Environment
    Sahin, Oemer Sinan
    Akdemir, Ahmet
    Avci, Ahmet
    Gemi, Lokman
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2009, 28 (24) : 2957 - 2970
  • [26] Fatigue behavior of filament wound E-glass/epoxy composite tubes damaged by low velocity impact
    Uyaner, Mesut
    Kara, Memduh
    Sahin, Aykut
    COMPOSITES PART B-ENGINEERING, 2014, 61 : 358 - 364
  • [27] FAILURE PRIDICTION OF GLASS FIBER-REINFORCED FLEXIBLE PIPES UNDER INTERNAL PRESSURE
    Zhang Y.
    Wang Y.-Y.
    Li C.-L.
    Lou M.
    Gongcheng Lixue/Engineering Mechanics, 2023, 40 (09): : 238 - 246
  • [28] Effects of weathering on failure pressure of filament-wound GFRP thermoset pipes
    Al-Sulaiman, F.
    Khan, Z.
    Merah, N.
    Kounain, M. A.
    Mehdi, M.
    JOURNAL OF COMPOSITE MATERIALS, 2011, 45 (06) : 645 - 655
  • [29] A failure envelope for +/-60° filament wound glass fibre reinforced epoxy tubulars
    Meijer, Garret
    Ellyin, Fernand
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2008, 39 (03) : 555 - 564
  • [30] TWISTING OF FILAMENT WOUND CYLINDERS UNDER INTERNAL-PRESSURE
    HOA, SV
    MANNARINO, G
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1989, 8 (03) : 212 - 231
12345