Fatigue failure behavior of glass/epoxy ±55 filament wound pipes under internal pressure

被引：88

作者：

Tarakçioglu, N

Gemi, L

Yapici, A ^{[1
]}

机构：

[1] Selcuk Univ, Dept Mech Engn, TR-42075 Konya, Turkey

[2] Selcuk Univ, Tech Educ Fac, TR-42075 Konya, Turkey

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 2005年 / 65卷 / 3-4期

关键词：

fatigue; filament winding;

D O I：

10.1016/j.compscitech.2004.10.002

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

In this study, fatigue behavior of filament wound composite pipes under alternating internal pressure has been investigated. GRP pipes which made of E-glass/epoxy are tested under open ended conditions. Test specimens have four layers which have +/-55degrees winding angle. Tests have been done in accordance with ASTM D-2992. This standards offers 0.42 Hz frequency and R = 0.05 stress ratio. Tests have been performed at different load levels from 30% to 70% of ultimate strength. Whitening, leakage and final failure levels of GRP pipes have been observed. Fatigue results are presented and interpreted by means of S-N curves. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：703 / 708

页数：6

共 50 条

[1] Progressive fatigue failure behavior of glass/epoxy (±75)2 filament-wound pipes under pure internal pressure
Gemi, Lokman
Tarakcioglu, Necmettin
Akdemir, Ahmet
Sahin, Oeer Sinan
MATERIALS & DESIGN, 2009, 30 (10) : 4293 - 4298
[2] The fatigue behavior of (±55°)3 filament wound GRP pipes with a surface crack under internal pressure
Tarakcioglu, N.
Samanci, A.
Arikan, H.
Akdemir, A.
COMPOSITE STRUCTURES, 2007, 80 (02) : 207 - 211
[3] Enhanced fatigue behavior under internal pressure of CNT reinforced filament wound cracked pipes
Tasyurek, Mustafa
Tarakcioglu, Necmettin
COMPOSITES PART B-ENGINEERING, 2017, 124 : 23 - 30
[4] Experimental study on compressive behavior and failure analysis of composite concrete confined by glass/epoxy ± 55° filament wound pipes
Gemi, Lokman
Koroglu, Mehmet Alpaslan
Ashour, Ashraf
COMPOSITE STRUCTURES, 2018, 187 : 157 - 168
[5] Failure analysis of (±55°)3 filament wound composite pipes with an inclined surface crack under static internal pressure
Arikan, Huseyin
COMPOSITE STRUCTURES, 2010, 92 (01) : 182 - 187
[6] Failure of ±55 degree filament wound glass/epoxy composite tubes under biaxial compression
Kaddour, AS
Soden, PD
Hinton, MJ
JOURNAL OF COMPOSITE MATERIALS, 1998, 32 (18) : 1618 - 1645
[7] Fatigue failure analysis of surface-cracked (±45°)3 filament-wound GRP pipes under internal pressure
Samanci, A.
Tarakcioglu, N.
Akdemir, A.
JOURNAL OF COMPOSITE MATERIALS, 2012, 46 (09) : 1041 - 1050
[8] FATIGUE BEHAVIOR OF GLASS-FILAMENT-WOUND EPOXY COMPOSITES IN WATER
ROMANS, JB
SANDS, AG
COWLING, JE
REPORT OF NRL PROGRESS, 1971, (MAR): : 13 - &
[9] FATIGUE BEHAVIOR OF GLASS FILAMENT-WOUND EPOXY COMPOSITES IN WATER
ROMANS, JB
SANDS, AG
COWLING, JE
INDUSTRIAL & ENGINEERING CHEMISTRY PRODUCT RESEARCH AND DEVELOPMENT, 1972, 11 (03): : 261 - &
[10] Fatigue crack growth of filament wound GRP pipes with a surface crack under cyclic internal pressure
Ahmet Samanci
Ahmet Avci
Necmettin Tarakcioglu
Ömer Sinan Şahin
Journal of Materials Science, 2008, 43 : 5569 - 5573

← 1 2 3 4 5 →