An experimental study on the failure of carbon/epoxy single lap riveted joints after thermal exposure

被引：27
|
作者：
Song, Min-Hwan [2 ]
Kweon, Jin-Hwe [1 ]
Kim, Sang-Kuk [2 ]
Kim, Cheol [2 ]
Lee, Tae-Joo [2 ]
Choi, Sang-Min [2 ]
Seong, Myeong-Su [1 ]
机构：
[1] Gyeongsang Natl Univ, Sch Mech & Aerosp Engn, Res Ctr Aircraft Parts Technol, Jinju 660701, Gyeongnam, South Korea
[2] Korea Aerosp Ind Ltd, Div Res & Dev, Sacheon 664802, Gyeongnam, South Korea
来源：
COMPOSITE STRUCTURES | 2008年 / 86卷 / 1-3期
基金：
新加坡国家研究基金会;
关键词：
single lap; joint; thermal exposure; strength;
D O I：
10.1016/j.compstruct.2008.03.029
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The bearing strength of a blind riveted single lap joint of a carbon/epoxy composite after thermal exposure was Studied. Considering the maximum service temperature based on material specifications and glass transition temperature, six types of specimens were prepared and tested in accordance with ASTM D5961. Failure loads of specimens exposed to a 177 degrees C environment were above 90% compared to Sound specimens. Failure loads of 77% were obtained for specimens exposed to a 232 degrees C environment for 4 h. Bearing and rivet pulling-through failure modes were observed in all specimens. Delamination Caused by degradation of the matrix property was found in specimens exposed to temperature higher than 204 degrees C. (C) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：125 / 134
页数：10
相关论文
共 50 条
  • [21] Studies of residual stress in single-row countersunk riveted lap joints
    Li, Gang
    Shi, Guoqin
    Bellinger, Nicholas C.
    Journal of Aircraft, 1600, 43 (03): : 592 - 599
  • [22] Effect of residual epoxy on single lap joints performance
    Vadugappatty Srinivasan, Dharun
    Aggarwal, Atin
    Sridhar, I.
    Ng, Charles
    JOURNAL OF ADHESION, 2020, 96 (10): : 883 - 901
  • [23] Experimental and Numerical Study of Thermal Residual Stresses on Multimaterial Adherends in Single-Lap Joints
    Simoes, Beatriz D.
    Nunes, Paulo D. P.
    Ramezani, Farin
    Carbas, Ricardo J. C.
    Marques, Eduardo A. S.
    da Silva, Lucas F. M.
    MATERIALS, 2022, 15 (23)
  • [24] Studies of residual stress in single-row countersunk riveted lap joints
    Li, Gang
    Shi, Guoqin
    Bellinger, Nicholas C.
    JOURNAL OF AIRCRAFT, 2006, 43 (03): : 592 - 599
  • [25] The influence of circular centered defects on the performance of carbon-epoxy single lap joints
    Berry, NG
    d'Almeida, JRM
    POLYMER TESTING, 2002, 21 (04) : 373 - 379
  • [26] Progressive Failure Analysis in Adhesively, Riveted, and Hybrid Bonded Double-Lap Joints
    Solmaz, Murat Yavuz
    Topkaya, Tolga
    JOURNAL OF ADHESION, 2013, 89 (11): : 822 - 836
  • [27] Progressive failure analysis in adhesively, riveted, and hybrid bonded double-lap joints
    Topkaya, T. (tolga.topkaya@batman.edu.tr), 1600, Bellwether Publishing, Ltd. (89):
  • [28] SIMULATION OF FAILURE IN SINGLE-LAP-JOINTS ASSEMBLIES OF CARBON FIBRE TAPES
    Machado, Martin
    Fischlschweiger, Michael
    Major, Zoltan
    11TH WORLD CONGRESS ON COMPUTATIONAL MECHANICS; 5TH EUROPEAN CONFERENCE ON COMPUTATIONAL MECHANICS; 6TH EUROPEAN CONFERENCE ON COMPUTATIONAL FLUID DYNAMICS, VOLS V - VI, 2014, : 6860 - 6866
  • [29] Failure analysis of GFRP single lap joints tailored with a combination of tough epoxy and hyperelastic adhesives
    Srinivasan, D. V.
    Ravichandran, V.
    Idapalapati, S.
    COMPOSITES PART B-ENGINEERING, 2020, 200
  • [30] Performance and failure assessment of adhesively bonded non-crimp fabric carbon fiber/epoxy composite single lap joints
    Dehaghani, Ramin Chitsaz
    Cronin, Duane
    Montesano, John
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2021, 105
12345