Prediction of fatigue life in cold expanded fastener holes subjected to bolt tightening in Al alloy 7075-T6 plate

被引：34
|
作者：
Taghizadeh, H. [1 ]
Chakherlou, T. N. [1 ]
Ghorbani, H. [1 ]
Mohammadpour, A. [1 ]
机构：
[1] Univ Tabriz, Fac Mech Engn, Tabriz, Iran
来源：
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES | 2015年 / 90卷
关键词：
Cold expansion; Bolt clamping; Fatigue life; Residual stress; Finite element; CLAMPING FORCE; RESIDUAL-STRESSES; EXPANSION; BEHAVIOR; THICKNESS; JOINTS; SIZE;
D O I：
10.1016/j.ijmecsci.2014.10.026
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
In this paper, stress analysis of holed plates was implemented in order to estimate the fatigue life due to the combined effect of cold expansion and bolt tightening (clamping force). The fatigue life was divided into two phases of crack initiation life and fatigue crack growth life. The fatigue crack initiation and fatigue crack growth life estimations have been investigated numerically and the total estimated fatigue lives have been compared with the available experimental fatigue test results. To obtain the residual stress, pre-stress and strain distributions created by cold expansion and bolt clamping force, and also the stress and strain distributions under cyclic longitudinal loads, three-dimensional finite element models were employed using ANSYS software. The results obtained from the finite element analysis of cold expansion and bolt clamping were employed to predict the fatigue crack initiation life using Fatemi-Socie multiaxial fatigue criterion, and fatigue crack growth life using AFGROW computer code. The results show that there is a good agreement between the numerically predicted total fatigue life and experimental fatigue test results. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：6 / 15
页数：10
相关论文
共 50 条
  • [11] An Numerical Investigation on the Effect of the Combination of Cold Expansion and Interference Fitting on Fatigue Life Improvement of a 7075-T6 Aluminum Alloy Single Plate
    Huang, Yongjie
    Guan, Zhidong
    Li, Zengshan
    Liu, Faqi
    He, Yamei
    Dan, Hu
    2017 8TH INTERNATIONAL CONFERENCE ON MECHANICAL AND AEROSPACE ENGINEERING (ICMAE), 2017, : 632 - 638
  • [12] Fatigue Fracture Mechanism of Extruded Al Alloy 7075-T6 in High Humidity
    Kariya, K.
    Kawagoishi, N.
    Maeda, H.
    Chen, Q.
    Goto, M.
    Nu, Y.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS X, 2012, 488-489 : 45 - +
  • [13] Fretting Fatigue Life Estimation of Al 7075-T6 Using Plain Fatigue Test
    Majzoobi, G. H.
    Minaii, K.
    TRIBOLOGY TRANSACTIONS, 2014, 57 (04) : 613 - 621
  • [14] A study on the effect of different Paris constants in mixed mode (I/II) fatigue life prediction in Al 7075-T6 alloy
    Shukla, Shiv Sahaya
    Murthy, K. S. R. K.
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
  • [15] Crack growth behavior of Al alloy 7075-T6 under ultrasonic fatigue
    Faculty of Engineering, Kagoshima University, 1-21-40 Korimoto, Kagoshima-shi, Kagoshima, 890-0065, Japan
    Nihon Kikai Gakkai Ronbunshu A, 2006, 9 (1356-1363):
  • [16] Fretting fatigue behavior in 7075-T6 aluminum alloy
    Shinde, Sachin R.
    Hoeppner, David W.
    WEAR, 2006, 261 (3-4) : 426 - 434
  • [17] Influence of corrosion on the fatigue properties of Al 7075-T6
    Du, ML
    Chiang, FP
    Kagwade, SV
    Clayton, CR
    JOURNAL OF TESTING AND EVALUATION, 1998, 26 (03) : 260 - 268
  • [18] Fatigue life prediction of interference fit fastener and cold worked holes
    Fatigue and Fracture Mechanics Dep, Toulouse, France
    Int J Fatigue, 8 (515-521):
  • [19] Fatigue life prediction of interference fit fastener and cold worked holes
    Duprat, D
    Campassens, D
    Balzano, M
    Boudet, R
    INTERNATIONAL JOURNAL OF FATIGUE, 1996, 18 (08) : 515 - 521
  • [20] Equivalent crack size model for pre-corrosion fatigue life prediction of aluminum alloy 7075-T6
    Huang, Yongfang
    Ye, Xubin
    Hu, Benrun
    Chen, Lijie
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 88 : 217 - 226
12345