Degradation and recovery of polarization under γ rays in Bi3.15Nd0.85Ti3O12 ferroelectric capacitors

被引：1
|
作者：
Liu, Tian-zhi [1 ]
Zhang, Zhi-gang [1 ]
Xie, Dan [1 ]
Dong, Yaoqi [1 ]
Ren, Tian-ling [1 ]
Liu, Li-tian [1 ]
Zhu, Jun [1 ]
机构：
[1] Tsinghua Univ, Inst Microelect, Beijing 100084, Peoples R China
来源：
INTEGRATED FERROELECTRICS | 2008年 / 98卷 / 01期
基金：
中国国家自然科学基金;
关键词：
ferroelectric; BNdT; irradiation; fatigue;
D O I：
10.1080/10584580802092472
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
Bi3.15Nd0.85Ti3O12 thin films of mixed orientations were grown on Pt/Ti/SiO2/Si substrates using the sol-gel method. The film annealed at 750 degrees C is composed of grains with sizes of 450 nm. The samples were exposed on different doses of gamma rays. The polarization of the films shows the degradation after irradiation. The remnant polarization decreased from 15 mu C/cm(2) to 7.4-9.8 mu C/cm(2) at an applied voltage of 8 V. This degradation can be recovered partially to 11 mu C/cm(2) by anneal in O-2 ambition. The irradiated capacitors did not show any significant fatigue up to 5 x 10(10) circles at frequency of 1 MHz.
引用
收藏
页码：105 / 112
页数：8
相关论文
共 50 条
  • [21] Effect of processing on the properties of Bi3.15Nd0.85Ti3O12 thin films
    Giridharan, N. V.
    Supriya, S.
    THIN SOLID FILMS, 2008, 516 (16) : 5244 - 5247
  • [22] Microstructures and impedance studies of Bi3.15Nd0.85Ti3O12 thin films
    Di Wu
    Aidong Li
    Applied Physics A, 2009, 95 : 517 - 521
  • [23] Stress impact on dielectric properties of Bi3.15Nd0.85Ti3O12 films
    Liu, Yunfei
    Kan, Yi
    Lu, Xiaomei
    Cai, Wei
    Wu, Xiaobo
    Wu, Xiumei
    Wang, Xiaofei
    Bo, HuiFeng
    Huang, Fengzhen
    Zhu, Jinsong
    APPLIED PHYSICS LETTERS, 2010, 96 (07)
  • [24] Preparation and waveguide properties of Bi3.15Nd0.85Ti3O12 thin films
    Wang, Yuehua
    Gong, Sai
    Pan, Hongliang
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2008, 41 (10)
  • [25] Enhanced ferroelectric properties of BiFeO3/Bi3.15Nd0.85Ti3O12 multilayer capacitors at room temperature applied in dielectric devices
    Xie, Dan
    Zang, Yongyuan
    YafengLuo
    Ren, Tianling
    Liu, Litian
    2008 9TH INTERNATIONAL CONFERENCE ON SOLID-STATE AND INTEGRATED-CIRCUIT TECHNOLOGY, VOLS 1-4, 2008, : 703 - 706
  • [26] Microstructures and impedance studies of Bi3.15Nd0.85Ti3O12 thin films
    Wu, Di
    Li, Aidong
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2009, 95 (02): : 517 - 521
  • [27] Multiferroic properties of Bi3.15Nd0.85Ti3O12–NiFe2O4–Bi3.15Nd0.85Ti3O12 trilayer composite thin films prepared by a sol–gel process
    Feng Yang
    Fuwei Zhang
    Cuifang Dong
    Fen Liu
    Minghua Tang
    Journal of Sol-Gel Science and Technology, 2015, 73 : 469 - 475
  • [28] Microstructural, ferroelectric, and dielectric properties of Bi3.15Nd0.85Ti3O12 ceramics -: art. no. 094101
    Qi, YJ
    Xiao, X
    Lu, CJ
    Mao, XY
    Chen, XB
    JOURNAL OF APPLIED PHYSICS, 2005, 98 (09)
  • [29] Annealing temperature-dependent piezoelectric properties of Bi3.15Nd0.85Ti3O12 ferroelectric thin films
    Chen, Y. Q.
    Zheng, X. J.
    He, L.
    Feng, X.
    PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2010, 207 (05): : 1240 - 1244
  • [30] Photovoltaic effect of ITO/Bi3.15Nd0.85Ti3O12/Pt heterojunction structure
    Liu, Xiaolian
    Wang, Guodong
    Xu, Yonghao
    Wu, Jun
    Hu, Zhongqiang
    Lu, Shiqi
    FERROELECTRICS, 2019, 553 (01) : 36 - 42
12345