Fatigue of stress corrosion cracks in X65 pipeline steels

被引：31
|
作者：
Gamboa, E. [1 ]
Linton, V. [1 ]
Law, M. [2 ]
机构：
[1] Univ Adelaide, Sch Mech Engn, Adelaide, SA 5005, Australia
[2] Australian Nucl Sci & Technol Org, PMBI, Menai, NSW 2234, Australia
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2008年 / 30卷 / 05期
关键词：
SCC; pipeline fatigue; crack interaction;
D O I：
10.1016/j.ijfatigue.2007.06.006
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A section of gas pipeline containing stress corrosion cracking (SCC) was removed from service and pressure cycled. SCC cracks were shown to have extended by fatigue. Fatigue crack interaction was found to be a large factor in crack growth characteristics. Crack interaction was found to be influenced by original SCC crack inclination and layout. Fatigue crack growth was found to be independent of original SCC crack profile or aspect ratio. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码：850 / 860
页数：11
相关论文
共 50 条
  • [41] Corrosion behavior of X65 pipeline steel welded joints by hyperbaric GMAW in simulated seawater
    Zhang Z.
    Xue L.
    Li Q.
    Huang J.
    Xu C.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2021, 42 (05): : 45 - 50
  • [42] Preferential weld corrosion of X65 pipeline steel in flowing brines containing carbon dioxide
    Alawadhi, K.
    Robinson, M. J.
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2011, 46 (04) : 318 - 329
  • [43] Effect of Welding Heat Input on Stress Corrosion Cracking Behavior in Coarse Grain Heat Affected Zone of X65 Pipeline
    Yan, Yusheng
    Zhong, Shifang
    Xu, Lianyong
    Zhao, Lei
    Han, Yongdian
    Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2024, 60 (12): : 220 - 227
  • [44] Influence of synthetically generated inclusions on the stress accumulation and concentration in X65 pipeline steel
    Fehlemann, N.
    Sparrer, Y.
    Puetz, F.
    Koenemann, M.
    Muenstermann, S.
    INTERNATIONAL DEEP-DRAWING RESEARCH GROUP CONFERENCE (IDDRG 2021), 2021, 1157
  • [45] Impact of gravity on biofilm growth and corrosion of X65 pipeline steel by a sulfate reducing bacterium
    Khan, Adnan
    Xu, Lingjun
    Kijkla, Pruch
    Kumseranee, Sith
    Punpruk, Suchada
    Gu, Tingyue
    CORROSION SCIENCE, 2024, 234
  • [46] Study on H2S stress corrosion test of welded joint for X65 pipeline steel and numerical analysis
    金晓军
    霍立兴
    张玉凤
    白秉仁
    李晓巍
    曹军
    China Welding, 2004, (01) : 21 - 26
  • [47] Discerning the Fatigue Crack Growth Behavior of API X65 Steels Under Sequence Loading
    Mansor, N. I. I.
    Abdullah, S.
    Ariffin, A. K.
    LATIN AMERICAN JOURNAL OF SOLIDS AND STRUCTURES, 2017, 14 (02): : 202 - 216
  • [48] Effects of Different Parameters on Initiation and Propagation of Stress Corrosion Cracks in Pipeline Steels: A Review
    Mohtadi-Bonab, M. A.
    METALS, 2019, 9 (05)
  • [49] Effect of Zr-Ti deoxidisation on the hydrogen-induced cracking of X65 pipeline steels
    Du, Y.
    Wu, K. M.
    Cheng, L.
    Li, Y.
    Isayev, O.
    Hress, O.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (07) : 728 - 735
  • [50] Measurement of lattice and apparent diffusion coefficient of hydrogen in X65 and F22 pipeline steels
    Fallahmohammadi, E.
    Bolzoni, F.
    Lazzari, L.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2013, 38 (05) : 2531 - 2543
12345