Fatigue of stress corrosion cracks in X65 pipeline steels

被引：31
|
作者：
Gamboa, E. [1 ]
Linton, V. [1 ]
Law, M. [2 ]
机构：
[1] Univ Adelaide, Sch Mech Engn, Adelaide, SA 5005, Australia
[2] Australian Nucl Sci & Technol Org, PMBI, Menai, NSW 2234, Australia
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2008年 / 30卷 / 05期
关键词：
SCC; pipeline fatigue; crack interaction;
D O I：
10.1016/j.ijfatigue.2007.06.006
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A section of gas pipeline containing stress corrosion cracking (SCC) was removed from service and pressure cycled. SCC cracks were shown to have extended by fatigue. Fatigue crack interaction was found to be a large factor in crack growth characteristics. Crack interaction was found to be influenced by original SCC crack inclination and layout. Fatigue crack growth was found to be independent of original SCC crack profile or aspect ratio. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码：850 / 860
页数：11
相关论文
共 50 条
  • [21] The Mechanism of Alternating Current Corrosion of API Grade X65 Pipeline Steel
    Ghanbari, E.
    Iannuzzi, M.
    Lillard, R. S.
    CORROSION, 2016, 72 (09) : 1196 - 1210
  • [22] Improving fatigue performance of welded joints of X65 pipeline steel by UIT
    柳锦铭
    陈通
    张玉凤
    China Welding, 2005, (02) : 135 - 139
  • [23] Characterization of Colonies of Stress Corrosion Cracks in Gas Pipelines of API 5L X65 Steel
    Ribeiro Junior, C. A.
    Magnol, R., V
    Tavares, S. S. M.
    Pardal, J. M.
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2021, 21 (04) : 1164 - 1171
  • [24] Inclined stress corrosion cracks in gas pipeline steels: morphology and implications
    Zadow, L.
    Gamboa, E.
    Lavigne, O.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (10): : 1092 - 1100
  • [25] Dynamic fracture of pipeline steel X65
    Liu, Yongning
    Feng, Yaorong
    Song, Xiaolong
    Wang, Xueyuan
    Zhuang, Chuanjing
    Ma, Qiurong
    Hsi-An Chiao Tung Ta Hsueh/Journal of Xi'an Jiaotong University, 2001, 35 (11): : 1171 - 1174
  • [26] Electrochemical Studies on the Corrosion Behavior of API X65 Pipeline Steel in Chloride Solutions
    Sherif, El-Sayed M.
    Almajid, Abdulhakim A.
    Khalil, Khalil Abdelrazek
    Junaedi, Harri
    Latief, F. H.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2013, 8 (07): : 9360 - 9370
  • [27] Effect of Microstructural Parameters on Fatigue Crack Propagation in an API X65 Pipeline Steel
    M. A. Mohtadi-Bonab
    M. Eskandari
    H. Ghaednia
    S. Das
    Journal of Materials Engineering and Performance, 2016, 25 : 4933 - 4940
  • [28] Effect of Microstructural Parameters on Fatigue Crack Propagation in an API X65 Pipeline Steel
    Mohtadi-Bonab, M. A.
    Eskandari, M.
    Ghaednia, H.
    Das, S.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (11) : 4933 - 4940
  • [29] Research on corrosion behaviour of X65 pipeline steel under dynamic AC interference
    Chen, Le
    Du, Yanxia
    Liang, Yi
    Li, Jianjun
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2021, 56 (03) : 219 - 229
  • [30] Effect of Bacteria in Soil on Microbiologically Influenced Corrosion Behavior of Underground X65 Pipeline
    Choe, Byung Hak
    Han, Sung Hee
    Kim, Dae Hyun
    Kim, Woosik
    Kim, Cheolman
    Choi, Kwang Su
    KOREAN JOURNAL OF MATERIALS RESEARCH, 2022, 32 (03): : 168 - 179
12345