The effects of additive elements on the sliding wear behavior of Fe-base hardfacing alloys

被引：32
|
作者：
Lee, KY [1 ]
Lee, SH
Kim, Y
Hong, HS
Oh, YM
Kim, SJ
机构：
[1] Hanyang Univ, Div Mat Sci & Engn, Seoul 133791, South Korea
[2] Pusan Natl Univ, Div Mat Sci & Engn, Pusan 609735, South Korea
来源：
WEAR | 2003年 / 255卷
关键词：
hardfacing alloy; sliding wear; strain-induced phase transformation;
D O I：
10.1016/S0043-1648(03)00155-8
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The present research is aiming at the development of new Fe-base wear resistance alloy, which has been expected to the substitute for Stellite 6 in nuclear power industry. The effects of Cr and C addition on the wear resistance were investigated. The sliding wear tests were performed in air at the temperature range 25-300 degreesC, and also in pressurized water at 25-250 degreesC. The contact stress was 103 MPa in accordance with current nuclear power plant component designs. The composition of Fe-base alloy was optimized to improve the wear resistance. The sliding wear behaviors of the optimized Fe-base alloy and Stellite 6 were compared in the present study. The weight loss of new Fe-base alloy after 100 cycles sliding wear test was found to be smaller than that of Stellite 6. (C) 2003 Published by Elsevier Science B.V.
引用
收藏
页码：481 / 488
页数：8
相关论文
共 50 条
  • [41] FACTORS AFFECTING THE NITRIDATION BEHAVIOR OF FE-BASE, NI-BASE, AND CO-BASE ALLOYS IN PURE NITROGEN
    BARNES, JJ
    LAI, GY
    JOURNAL DE PHYSIQUE IV, 1993, 3 (C9): : 167 - 174
  • [42] GUIDELINES FOR THE SELECTION OF HARDFACING ALLOYS FOR SLIDING WEAR RESISTANT APPLICATIONS - REPLY
    FOROULIS, ZA
    WEAR, 1985, 105 (03) : 280 - 280
  • [43] Sliding wear behavior of Fe3Al-based alloys
    Kim, Yong-Suk
    Kim, Yong-Hwan
    Materials Science and Engineering A, 1998, A258 (1-2): : 319 - 324
  • [44] Sliding wear behavior of Fe3Al-based alloys
    Kim, YS
    Kim, YH
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 258 (1-2): : 319 - 324
  • [45] On the Microstructure and Wear Behavior of Fe-xCr-4Mn-3C Hardfacing Alloys
    Singla, Yogesh Kumar
    Chhibber, Rahul
    Arora, Navneet
    Singh, Karanpreet
    Khanna, Kishore
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2017, 70 (06) : 1555 - 1561
  • [46] Wear behavior and microstructure of Fe-C-Si-Cr-B-Ni hardfacing alloys
    Öztürk, Zeynep Taslicukur
    Materialpruefung/Materials Testing, 2021, 63 (03): : 231 - 234
  • [47] Wear behavior and microstructure of Fe-C-Si-Cr-B-Ni hardfacing alloys
    Ozturk, Zeynep Taslicukur
    MATERIALS TESTING, 2021, 63 (03) : 231 - 234
  • [48] Modeling a thermodynamic activity of sulfur in Fe-base multicomponent alloys
    Burylev, B.P.
    Tsemekhman, L.Sh.
    Mojsov, L.P.
    Metally, 2002, (04): : 17 - 19
  • [49] FE-BASE PRECIPITATION-HARDENED MAGNETIC-ALLOYS
    JIN, S
    JOURNAL OF METALS, 1981, 33 (09): : A5 - A5
  • [50] Crystallization processes of amorphous Al- and Fe-base alloys
    Fujita, H
    Tsuboi, T
    Harada, K
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1996, 60 (11) : 1031 - 1036
12345