Macrofouling induced localized corrosion of stainless steel in Singapore seawater

被引：56
|
作者：
Blackwood, Daniel J. [1 ]
Lim, Chin Sing [2 ]
Teo, Serena L. M. [2 ]
Hu Xiaoping [1 ,3 ]
Pang Jianjun [1 ,4 ]
机构：
[1] Natl Univ Singapore, Dept Mat Sci & Engn, Singapore 117574, Singapore
[2] Natl Univ Singapore, Trop Marine Sci Inst, Singapore 119227, Singapore
[3] Adv Technol & Mat, 12 Yongcheng Beilu, Beijing, Peoples R China
[4] Zhejiang Univ Water Resources & Elect Power, Sch Mech & Automot Engn, Hangzhou 310018, Zhejiang, Peoples R China
来源：
CORROSION SCIENCE | 2017年 / 129卷
关键词：
Stainless steel; Weight loss; Crevice corrosion; Microbiological corrosion; SULFATE-REDUCING BACTERIA; NATURAL SEA-WATER; CREVICE CORROSION; ADHESIVE; BIOFILMS; OYSTERS; ALLOYS;
D O I：
10.1016/j.corsci.2017.10.008
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Biofouling induced corrosion of stainless steels grades UNS 531603 and UNS 531254 was investigated at three sites off Singapore for 30 months. No corrosion was observed on grade UNS 531254, while the propensity for corrosion by shellfish of UNS 531603 is ranked as oyster > > barnacles > > green mussels. Oysters caused extensive localised corrosion, penetrating 2 mm thick plates with 12 months with tracks of corrosion several centimetres long. Shallow crevice corrosion was observed under dead barnacles, with an explanation presented for why corrosion is more severe under dead barnacles than live ones. Green mussels did not cause any corrosion.
引用
收藏
页码：152 / 160
页数：9
相关论文
共 50 条
  • [31] Localized corrosion of carbon steel in seawater: Processes occurring in cathodic zones
    Duboscq, Julien
    Sabot, Rene
    Jeannin, Marc
    Refait, Philippe
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2019, 70 (06): : 973 - 984
  • [32] Effect of Surface Roughness on the Corrosion Behavior of 304 Stainless Steel in Seawater
    Liu, Xuehui
    Zhang, Huixia
    Tong, Hongtao
    Sui, Yongqiang
    Li, Xiangbo
    Hou, Jian
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024,
  • [33] THE RESISTANCE OF STAINLESS-STEEL PARTLY EMBEDDED IN CONCRETE TO CORROSION BY SEAWATER
    FLINT, GN
    COX, RN
    MAGAZINE OF CONCRETE RESEARCH, 1988, 40 (142) : 13 - 27
  • [34] Corrosion potential and cathodic reduction efficiency of stainless steel in natural seawater
    Thierry, D.
    Larche, N.
    Leballeur, C.
    Wijesinghe, S. L.
    Zixi, T.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (05): : 453 - 458
  • [35] CREVICE CORROSION BEHAVIOR OF STAINLESS-STEEL IN SEAWATER AND RELATED ENVIRONMENTS
    KAIN, RM
    CORROSION, 1984, 40 (06) : 313 - 321
  • [36] Corrosion Rate of Stainless Steel Rebar in Coral Concrete Prepared with Seawater
    Feng, Xingguo
    Lu, Xiao
    Lu, Xiangyu
    Yang, Yashi
    Luo, Feng
    Jianzhu Cailiao Xuebao/Journal of Building Materials, 2021, 24 (06): : 1322 - 1327
  • [37] Model to Study the Effect of Composition of Seawater on the Corrosion Rate of Mild Steel and Stainless Steel
    Subir Paul
    Journal of Materials Engineering and Performance, 2011, 20 : 325 - 334
  • [38] STRESS CORROSION CRACKING OF AISI 321 STAINLESS STEEL IN ACIDIC SEAWATER
    黄彦良
    侯保荣
    曹楚南
    林海潮
    ChineseJournalofOceanologyandLimnology, 1997, (04) : 373 - 377
  • [39] Stress corrosion cracking of AISI 321 stainless steel in acidic seawater
    Huang Yan-liang
    Hou Bao-rong
    Cao Chu-nan
    Lin Hai-chao
    Chinese Journal of Oceanology and Limnology, 1997, 15 (4): : 373 - 377
  • [40] Role of surface finishing on pitting corrosion of a duplex stainless steel in seawater
    BenSalahRousset, N
    Chaouachi, MA
    Chellouf, A
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 1996, 5 (02) : 225 - 231
12345