Macrofouling induced localized corrosion of stainless steel in Singapore seawater

被引：56
|
作者：
Blackwood, Daniel J. [1 ]
Lim, Chin Sing [2 ]
Teo, Serena L. M. [2 ]
Hu Xiaoping [1 ,3 ]
Pang Jianjun [1 ,4 ]
机构：
[1] Natl Univ Singapore, Dept Mat Sci & Engn, Singapore 117574, Singapore
[2] Natl Univ Singapore, Trop Marine Sci Inst, Singapore 119227, Singapore
[3] Adv Technol & Mat, 12 Yongcheng Beilu, Beijing, Peoples R China
[4] Zhejiang Univ Water Resources & Elect Power, Sch Mech & Automot Engn, Hangzhou 310018, Zhejiang, Peoples R China
来源：
CORROSION SCIENCE | 2017年 / 129卷
关键词：
Stainless steel; Weight loss; Crevice corrosion; Microbiological corrosion; SULFATE-REDUCING BACTERIA; NATURAL SEA-WATER; CREVICE CORROSION; ADHESIVE; BIOFILMS; OYSTERS; ALLOYS;
D O I：
10.1016/j.corsci.2017.10.008
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Biofouling induced corrosion of stainless steels grades UNS 531603 and UNS 531254 was investigated at three sites off Singapore for 30 months. No corrosion was observed on grade UNS 531254, while the propensity for corrosion by shellfish of UNS 531603 is ranked as oyster > > barnacles > > green mussels. Oysters caused extensive localised corrosion, penetrating 2 mm thick plates with 12 months with tracks of corrosion several centimetres long. Shallow crevice corrosion was observed under dead barnacles, with an explanation presented for why corrosion is more severe under dead barnacles than live ones. Green mussels did not cause any corrosion.
引用
收藏
页码：152 / 160
页数：9
相关论文
共 50 条
  • [1] Localized corrosion of stainless steel
    Munro, I
    MATERIALS PERFORMANCE, 2005, 44 (07) : 48 - 50
  • [2] More on localized corrosion of stainless steel
    Qiu, JH
    MATERIALS PERFORMANCE, 2005, 44 (12) : 9 - 10
  • [3] Localized Corrosion of Mooring Chain Steel in Seawater
    Zhang, Xiaolong
    Noel-Hermes, Nanni
    Ferrari, Gabriele
    Hoogeland, Martijn
    CORROSION AND MATERIALS DEGRADATION, 2022, 3 (01) : 53 - 74
  • [4] Cavitation corrosion of duplex stainless steel in seawater
    AlHashem, A
    Caceres, PG
    Abdullah, A
    Shalaby, HM
    CORROSION, 1997, 53 (02) : 103 - 113
  • [5] Interaction of marine organisms on localized corrosion of 316L stainless steel in Dalian seawater
    Chen, Wanbin
    Wang, Mingyu
    Li, Mingyu
    Li, Kaiqiang
    Huang, Yi
    Xu, Yunze
    ANTI-CORROSION METHODS AND MATERIALS, 2023, 70 (04) : 157 - 165
  • [6] More on localized corrosion of stainless steel - Reply
    Munro, I
    MATERIALS PERFORMANCE, 2005, 44 (12) : 10 - 11
  • [7] LOCALIZED CORROSION OF CRNI STAINLESS-STEEL
    TOUSEK, J
    KOVOVE MATERIALY-METALLIC MATERIALS, 1977, 15 (05): : 592 - 602
  • [8] Localized Electrochemical Corrosion Characteristics of Carbon Steel in Seawater
    Zou, Yan
    Bai, Qiang
    Wang, Jia
    Wang, Wei
    Kong, Xiangfeng
    MATERIALS, MECHANICAL AND MANUFACTURING ENGINEERING, 2014, 842 : 104 - +
  • [9] Corrosion of Type 316 stainless steel in deaerated seawater
    不详
    MATERIALS PERFORMANCE, 2012, 51 (10) : 63 - 63
  • [10] Corrosion Behavior of Stainless Steel in Seawater in the Presence of Sulfide
    Gudic, Senka
    Vrsalovic, Ladislav
    Matosin, Ante
    Krolo, Jure
    Oguzie, Emeka Emanuel
    Nagode, Ales
    APPLIED SCIENCES-BASEL, 2023, 13 (07):
12345