Hardfacing of a Modified 9Cr-1Mo Steel Component Using a Nickel-Base Alloy

被引：13
|
作者：
Kumar, Hemant [1 ]
Albert, S. K. [1 ]
Sudha, C. [1 ]
Vijayashree, R. [1 ]
Bhaduri, A. K. [1 ]
Balasubramanian, C. [2 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Kalpakkam 603102, Tamil Nadu, India
[2] Omplas Syst, Madras 602101, Tamil Nadu, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2011年 / 64卷 / 4-5期
关键词：
PTA; Deloro-50; Inconel-625; Modified 9Cr-1Mo steel; Hardfacing;
D O I：
10.1007/s12666-011-0087-4
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
A dashpot piston made of modified 9Cr-1Mo steel is hardfaced with NiCr-B alloy by the Plasma Transferred Arc (PTA) process. During initial trials, a large number of cracks were observed in the hardface deposit when hardfacing was carried out directly on the modified 9Cr-1Mo steel substrate using a preheat temperature of 723 K. Both the deposit and the martensitic structure formed in the heat affected zone of the substrate during deposition are hard and hence were unable to absorb the thermal stresses generated, leading to cracking. Subsequently, hardfacing trials carried out with an intermediate layer of 2 mm thick Inconel-625 alloy, were successful and deposits were crack-free. Use of a relatively soft Inconel-625 between the hardface deposit and the substrate reduced martensite formation in the substrate, and thus the cracking susceptibility of the deposit.
引用
收藏
页码：339 / 343
页数：5
相关论文
共 50 条
  • [31] Uniaxial creep and stress relaxation behavior of modified 9Cr-1Mo steel
    Guguloth, Krishna
    Swaminathan, J.
    Roy, Nilima
    Ghosh, R. N.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 684 : 683 - 696
  • [32] Effect of normalization temperature on the creep strength of modified 9Cr-1Mo steel
    Totemeier, T. C.
    Tian, H.
    Simpson, J. A.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (05): : 1519 - 1525
  • [33] Effects of Simulated Microstructure on the Creep Rupture of the Modified 9Cr-1Mo Steel
    T. H. Hsiao
    T. C. Chen
    S. L. Jeng
    T. J. Chung
    L. W. Tsay
    Journal of Materials Engineering and Performance, 2016, 25 : 4317 - 4325
  • [34] Ratcheting Fatigue Behavior of Modified 9Cr-1Mo Steel at Room Temperature
    Mishra, Prerna
    Rajpurohit, R. S.
    Srinivas, N. C. Santhi
    Sastry, G. V. S.
    Singh, Vakil
    METALS AND MATERIALS INTERNATIONAL, 2021, 27 (12) : 4922 - 4936
  • [35] Effect of test temperature on fracture toughness of modified 9Cr-1Mo steel
    Dutt, B. Shashank
    Babu, M. Nani
    Venugopal, S.
    Sasikala, G.
    Bhaduri, A. K.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (10) : 1527 - 1533
  • [36] Evaluation of creep damage in a welded joint of modified 9Cr-1Mo steel
    Li, Yongkui
    Monma, Yoshio
    Hongo, Hiromichi
    Tabuchi, Masaaki
    JOURNAL OF NUCLEAR MATERIALS, 2010, 405 (01) : 44 - 49
  • [37] Study of high-temperature oxidation of modified 9Cr-1Mo steel
    Peña-Ballesteros, Darío Yesid
    Vásquez-Quintero, Custodio
    Ingenieria y Universidad, 2011, 15 (02): : 359 - 372
  • [38] The evaluation of material degradation in modified 9Cr-1Mo steel by the electrochemical technique
    Hyun, Y
    Lee, J
    Kim, I
    ADVANCES IN NONDESTRUCTIVE EVALUATION, PT 1-3, 2004, 270-273 : 1206 - 1211
  • [39] Cyclic Deformation Behavior of Modified 9Cr-1Mo Steel at Elevated Temperatures
    Singh, Vakil
    Verma, Preeti
    MECHANICAL AND CREEP BEHAVIOR OF ADVANCED MATERIALS, 2017, : 195 - 206
  • [40] Effects of Simulated Microstructure on the Creep Rupture of the Modified 9Cr-1Mo Steel
    Hsiao, T. H.
    Chen, T. C.
    Jeng, S. L.
    Chung, T. J.
    Tsay, L. W.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (10) : 4317 - 4325
12345