Choosing modes for thermal treatment of deposited coatings based on chromium steel with carbide-boride-nitride doping

被引：0
|
作者：
Eremin, E. N. [1 ]
Losev, A. S. [1 ]
Borodikhin, S. A. [1 ]
Ponomarev, I. A. [1 ]
Matalasova, A. E. [1 ]
机构：
[1] Omsk State Tech Univ, 11 Mira Ave, Omsk 644050, Russia
来源：
MECHANICAL SCIENCE AND TECHNOLOGY UPDATE (MSTU-2018) | 2018年 / 1050卷
基金：
俄罗斯科学基金会;
关键词：
D O I：
10.1088/1742-6596/1050/1/012024
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This work explores the regimes of thermal treatment of corrosion-resistant coatings obtained by surfacing with a flux-cored wire with carbide-boride-nitride doping. It was found that tempering at a temperature of 800 degrees Celsius reduces the hardness of the metal to acceptable values for machining. To increase the hardness of the metal after tempering, it was suggested to perform quenching at a temperature of 1020 degrees Celsius. Carrying out such heat treatment ensures the hardness of the metal practically coinciding with the hardness of the metal after surfacing.
引用
收藏
页数：5
相关论文
共 46 条
  • [21] Formation of chromium carbide coatings on HT250 steel by thermal diffusion processes in fluoride molten salt bath
    Su, Xingzhi
    Zhao, Sufang
    Hou, Juan
    Yu, Guojun
    Chen, Yanjun
    Sun, Hua
    Zhang, Peng
    Xie, Leidong
    VACUUM, 2018, 155 : 219 - 223
  • [22] Wear resistance of KhVG tool steel hardened with composite coatings based on titanium-chromium double carbide
    A. P. Umanskii
    V. P. Konoval
    I. A. Podchernyaeva
    A. D. Panasyuk
    Ya. N. Gladkii
    O. N. Makovkin
    Journal of Superhard Materials, 2007, 29 (4) : 250 - 255
  • [23] The effect of rapid thermal processing (RTP) on TiN coatings deposited by PVD and the steel-turning performance of coated cemented carbide
    Perry, AJ
    Matossian, JN
    Bull, SJ
    Proskurovsky, DI
    Rice-Evans, PC
    Page, TF
    Geist, DE
    Taylor, J
    Vajo, JJ
    Doty, RE
    Rotshtein, V
    Markov, AB
    SURFACE & COATINGS TECHNOLOGY, 1999, 120 : 337 - 342
  • [24] Corrosion Behavior of Ni-Based Coatings Reinforced with Chromium Carbide Particles Deposited by Plasma Transferred Arc in a Hydrochloric Acid Solution
    L. Fan
    S. S. Liu
    H. Y. Chen
    H. L. Du
    Strength of Materials, 2021, 53 : 106 - 115
  • [25] Corrosion Behavior of Ni-Based Coatings Reinforced with Chromium Carbide Particles Deposited by Plasma Transferred Arc in a Hydrochloric Acid Solution
    Fan, L.
    Liu, S. S.
    Chen, H. Y.
    Du, H. L.
    STRENGTH OF MATERIALS, 2021, 53 (01) : 106 - 115
  • [26] Carbide-based thermal spray coatings: A review on performance characteristics and post-treatment
    Govande, Akshay R.
    Chandak, Aayush
    Sunil, B. Ratna
    Dumpala, Ravikumar
    International Journal of Refractory Metals and Hard Materials, 2022, 103
  • [27] Carbide-based thermal spray coatings: A review on performance characteristics and post-treatment
    Govande, Akshay R.
    Chandak, Aayush
    Sunil, B. Ratna
    Dumpala, Ravikumar
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2022, 103
  • [28] On the plastic deformation of chromium-based nitride hard coatings deposited by hybrid dcMS/HPPMS: A fundamental study using nanoscratch test
    Bobzin, K.
    Broegelmann, T.
    Kruppe, N. C.
    Arghavani, M.
    Mayer, J.
    Weirich, T. E.
    SURFACE & COATINGS TECHNOLOGY, 2016, 308 : 298 - 306
  • [29] Surface Characterization and Mechanical Properties’ Evaluation of Boride-Dispersed Nickel-Based Coatings Deposited on Copper Through Thermal Spray Routes
    Prashant Sharma
    Jyotsna Dutta Majumdar
    Journal of Thermal Spray Technology, 2012, 21 : 800 - 809
  • [30] Surface Characterization and Mechanical Properties' Evaluation of Boride-Dispersed Nickel-Based Coatings Deposited on Copper Through Thermal Spray Routes
    Sharma, Prashant
    Majumdar, Jyotsna Dutta
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2012, 21 (05) : 800 - 809
12345