Low-Temperature Synthesis of Calcium Hexaboride Powder via Transient Boron Carbide Formation

被引：21
|
作者：
Kakiage, Masaki [1 ]
Shiomi, Shuhei [1 ]
Yanase, Ikuo [1 ]
Kobayashi, Hidehiko [1 ]
机构：
[1] Saitama Univ, Grad Sch Sci & Engn, Dept Appl Chem, Sakura Ku, Saitama 3388570, Japan
来源：
JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2015年 / 98卷 / 09期
关键词：
ACID-GLYCERIN PRODUCT; PRECURSOR; CAB6;
D O I：
10.1111/jace.13771
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Calcium hexaboride (CaB6) powder was synthesized by carbothermal reduction using a low-temperature synthesis method for boron carbide (B4C) powder. A B4C precursor consisting of boron oxide (B2O3) and carbon components was prepared from a condensed boric acid (H3BO3)-poly(vinyl alcohol) (PVA) product by thermal decomposition in air, which was then mixed with calcium carbonate (CaCO3) powder. CaB6 was formed via the transient formation of calcium borate (Ca3B2O6) and B4C, which were in close contact owing to the finely dispersed B2O3/carbon structure of the B4C precursor. CaB6 powder with fine particles was synthesized by heat treatment at 1400 degrees C for 10h in an Ar flow.
引用
收藏
页码：2724 / 2727
页数：4
相关论文
共 50 条
  • [41] Nanotube formation from a sodium titanate powder via low-temperature acid treatment
    Tsai, Chien-Cheng
    Teng, Hsisheng
    LANGMUIR, 2008, 24 (07) : 3434 - 3438
  • [42] Low-temperature synthetic route for boron carbide powder from boric acid-citric acid gel precursor
    Kosanovic, Dj.
    Milovanovic, Lj.
    Milovanovic, S.
    Saponjic, A.
    RESEARCH TRENDS IN CONTEMPORARY MATERIALS SCIENCE, 2007, 555 : 255 - +
  • [43] Microstructure in precursor formed by controlling composition of condensed boric acid-poly(vinyl alcohol) product for low-temperature synthesis of boron carbide powder
    Kakiage, Masaki
    Tahara, Naoki
    Watanabe, Rie
    Yanase, Ikuo
    Kobayashi, Hidehiko
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2013, 121 (1409) : 40 - 44
  • [44] Synthesis and properties of ultrafine YAG powder via low-temperature microwave hydrothermal method
    Liu, Yue
    Song, Jieguang
    Chen, Lin
    Luo, Huihui
    Lin, Guojian
    Chen, Peng
    Wei, Chenhui
    Liu, Jingjing
    JOURNAL OF CERAMIC PROCESSING RESEARCH, 2020, 21 (04): : 488 - 494
  • [45] Synthesis of boron carbide powder from hexagonal boron nitride
    Zeng, Hong
    Kan, Yan-Mei
    Zhang, Guo-Jun
    MATERIALS LETTERS, 2010, 64 (18) : 2000 - 2002
  • [46] LOW-TEMPERATURE SYNTHESIS METHOD OF ALUMINUM NITRIDE POWDER
    Yun, Kyyoul
    Takahashi, Yuya
    Yanase, Shunji
    PROCESSING AND PROPERTIES OF ADVANCED CERAMICS AND COMPOSITES VII, 2015, 252 : 229 - 233
  • [47] LOW-TEMPERATURE HOT-PRESSING OF BORON-CARBIDE AND ITS PROPERTIES
    VASILOS, T
    DUTTA, SK
    AMERICAN CERAMIC SOCIETY BULLETIN, 1974, 53 (05): : 453 - 454
  • [48] Physicochemical Transformations During Low-Temperature Synthesis of Zirconium Carbide
    Shishkin, R. A.
    Kudyakova, V. S.
    Zhirenkina, N. V.
    REFRACTORIES AND INDUSTRIAL CERAMICS, 2019, 60 (01) : 105 - 108
  • [49] Effect of low temperature on formation mechanism of calcium phosphate nano powder via precipitation method
    Moghimian, P.
    Najafi, A.
    Afshar, S.
    Javadpour, J.
    ADVANCED POWDER TECHNOLOGY, 2012, 23 (06) : 744 - 751
  • [50] ε-Iron carbide as a low-temperature Fischer–Tropsch synthesis catalyst
    Ke Xu
    Bo Sun
    Jun Lin
    Wen Wen
    Yan Pei
    Shirun Yan
    Minghua Qiao
    Xiaoxin Zhang
    Baoning Zong
    Nature Communications, 5
12345