Activation Energy of thermal Degradation of Tetrafluoroethylene-Propylene Elastomer

被引：0
|
作者：
Ito, Masayuki [1 ]
Nozaki, Masahide [1 ]
Kosaka, Tomomi [1 ]
机构：
[1] Tokyo Gakugei Univ, 4-1-4 Nukuikitamachi, Koganei, Tokyo 1848501, Japan
来源：
KGK-KAUTSCHUK GUMMI KUNSTSTOFFE | 2022年 / 75卷 / 06期
关键词：
Polyoxymethylene ISO 11358-2; ISO; 11358-3; Tetrafluoroethylene-propylene Elastomer; thermal Degradation; Activation Energy; Thermogravimetry;
D O I：
暂无
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
The effect of the pre-aging at 250 degrees C before the measurement of thermogravimetry of tetrafluoroethylene-propylene elastomer was studied. The longer the pre-aging time, the more the linearity of the analyzed line with reference to ISO 11358-2 was improved. The activation energy of the sample aged 240 h was from 159 kJ/mol to 164 Id/mol, which was depending on the weight retained. The value obtained with reference to ISO 11358-3 was from 149 kJ/mol to 159 kJ/mol.
引用
收藏
页码：47 / 51
页数：5
相关论文
共 50 条
  • [21] NUCLEAR MAGNETIC-RESONANCE MICROSTRUCTURE ANALYSIS OF TETRAFLUOROETHYLENE-PROPYLENE COPOLYMERS
    BRAME, EG
    HARRELL, JR
    FERGUSON, RC
    MACROMOLECULES, 1975, 8 (05) : 604 - 607
  • [22] Effects of MPBM on crosslinking density and mechanical properties of Tetrafluoroethylene-Propylene copolymer
    Lu, JiangRong
    Wang, YuFeng
    Yan, PuXuan
    Han, FeiXue
    CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING III, PTS 1-3, 2014, 881-883 : 897 - 900
  • [23] TETRAFLUOROETHYLENE-PROPYLENE CO-POLYMER (AFLAS) - NEW TECHNOLOGY, NEW USES
    HULL, DE
    ELASTOMERICS, 1983, 115 (10): : 40 - &
  • [24] F-19 NUCLEAR MAGNETIC-RESONANCE SPECTRA OF TETRAFLUOROETHYLENE-PROPYLENE COPOLYMERS
    ISHIGURE, K
    TABATA, Y
    OSHIMA, K
    MACROMOLECULES, 1973, 6 (04) : 584 - 588
  • [25] APPLICATION OF TGA/FTIR TO THE THERMAL-DEGRADATION MECHANISM OF TETRAFLUOROETHYLENE PROPYLENE COPOLYMERS
    SCHILD, HG
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 1993, 31 (06) : 1629 - 1632
  • [26] F-19-NMR AND H-1-NMR SPECTRA OF TETRAFLUOROETHYLENE-PROPYLENE COPOLYMERS
    KOJIMA, G
    WACHI, H
    ISHIGURE, K
    TABATA, Y
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 1976, 14 (06) : 1317 - 1330
  • [27] NEW TYPE OF FLUOROELASTOMER (TETRAFLUOROETHYLENE-PROPYLENE COPOLYMER) PROVIDES IMPROVED RESISTANCE TO SOME AUTOMOTIVE MEDIA
    HULL, D
    KOJIMA, G
    WACHI, H
    RUBBER CHEMISTRY AND TECHNOLOGY, 1986, 59 (01): : 163 - 163
  • [28] ALFAS - A UNIQUE ELASTOMER BASED ON A REGULARLY ALTERNATING STRUCTURE OF TETRAFLUOROETHYLENE AND PROPYLENE
    HULL, DE
    UCHIJIMA, K
    MOROZUMI, M
    RUBBER CHEMISTRY AND TECHNOLOGY, 1982, 55 (01): : 266 - 267
  • [29] Influence of Thermal Ageing on Surface Degradation of Ethylene-Propylene-Diene Elastomer
    Nevshupa, R.
    Martinez, L.
    Alvarez, L.
    Lopez, M. F.
    Huttel, Y.
    Mendez, J.
    Roman, E.
    JOURNAL OF APPLIED POLYMER SCIENCE, 2011, 119 (01) : 242 - 251
  • [30] Stability of PUSS crosslinks and aggregates in tetrafluoroethylene-propylene elastomers/OVPOSS composites exposed to hydrochloric acid solution
    Cong, Chuanbo
    Cui, Cancan
    Meng, Xiaoyu
    Zhou, Qiong
    POLYMER DEGRADATION AND STABILITY, 2014, 100 : 29 - 36
12345