Effect of bond coat surface roughness on oxidation behaviour of air plasma sprayed thermal barrier coatings

被引：25
|
作者：
Che, C. [1 ]
Wu, G. Q. [1 ]
Qi, H. Y. [2 ]
Huang, Z. [1 ]
Yang, X. G. [2 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[2] Beijing Univ Aeronaut & Astronaut, Sch Jet Prop, Beijing 100083, Peoples R China
来源：
SURFACE ENGINEERING | 2008年 / 24卷 / 04期
关键词：
thermal barrier coating; MCrAIY; oxidation; roughness; lifetime; failure;
D O I：
10.1179/026708408X329470
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Two layered thermal barrier coatings (TBCs) with different bond coat surface roughnesses were produced by air plasma spraying. Isothermal oxidation test was carried out to evaluate the durability and oxidation behaviour of these systems. The results show that the roughness of bond coat significantly affects the lifetime of TBCs. With the increase in bond coat roughness, the lifetime decreases exponentially. The durability is enhanced by surface grinding treatments that decrease diffusion paths on the surface of the bond coat and diminish Al depletion rate. The shape and path of cracks at failure are also affected by the bond coat surface roughness.
引用
收藏
页码：276 / 279
页数：4
相关论文
共 50 条
  • [41] Effect of bond coat processes and surface characteristics on the failure mechanism of thermal barrier coatings
    Ding, ZX
    Knight, R
    Smith, RW
    THERMAL SPRAY 2001: NEW SURFACES FOR A NEW MILLENNIUM, 2001, : 173 - 177
  • [42] An investigation on the microstructure and oxidation behavior of laser remelted air plasma sprayed thermal barrier coatings
    Zhu, C.
    Li, P.
    Javed, A.
    Liang, G. Y.
    Xiao, P.
    SURFACE & COATINGS TECHNOLOGY, 2012, 206 (18): : 3739 - 3746
  • [43] Effect of Suspension Plasma-Sprayed YSZ Columnar Microstructure and Bond Coat Surface Preparation on Thermal Barrier Coating Properties
    Bernard, Benjamin
    Quet, Aurelie
    Bianchi, Luc
    Schick, Vincent
    Joulia, Aurelien
    Malie, Andre
    Remy, Benjamin
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2017, 26 (06) : 1025 - 1037
  • [44] Effect of Suspension Plasma-Sprayed YSZ Columnar Microstructure and Bond Coat Surface Preparation on Thermal Barrier Coating Properties
    Benjamin Bernard
    Aurélie Quet
    Luc Bianchi
    Vincent Schick
    Aurélien Joulia
    André Malié
    Benjamin Rémy
    Journal of Thermal Spray Technology, 2017, 26 : 1025 - 1037
  • [45] BOND COAT DEVELOPMENT FOR THERMAL BARRIER COATINGS
    WORTMAN, DJ
    DUDERSTADT, EC
    NELSON, WA
    JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 1990, 112 (04): : 527 - 530
  • [46] Effect of Vanadium Contaminated Fuel on Bond Coat and Bond Coat/Top Coat Interface of Thermal Barrier Coatings
    Khalid, Adeel
    Gasem, Zuhair M.
    MECHANICAL AND AEROSPACE ENGINEERING, PTS 1-7, 2012, 110-116 : 886 - 891
  • [47] Mechanical characterization and thermal behavior of HVOF-sprayed bond coat in thermal barrier coatings (TBCs)
    Jang, HJ
    Park, DH
    Jung, YG
    Jang, JC
    Choi, SC
    Paik, U
    SURFACE & COATINGS TECHNOLOGY, 2006, 200 (14-15): : 4355 - 4362
  • [48] Thermal Failure of Nanostructured Thermal Barrier Coatings with Cold-Sprayed Nanostructured NiCrAlY Bond Coat
    Zhang, Qiang
    Li, Chang-Jiu
    Li, Yong
    Zhang, Shao-Ling
    Wang, Xiu-Ru
    Yang, Guan-Jun
    Li, Cheng-Xin
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2008, 17 (5-6) : 838 - 845
  • [49] Thermal Failure of Nanostructured Thermal Barrier Coatings with Cold-Sprayed Nanostructured NiCrAlY Bond Coat
    Qiang Zhang
    Chang-Jiu Li
    Yong Li
    Shao-Ling Zhang
    Xiu-Ru Wang
    Guan-Jun Yang
    Cheng-Xin Li
    Journal of Thermal Spray Technology, 2008, 17 : 838 - 845
  • [50] Defining optimal morphology of the bond coat-thermal barrier coating interface of air-plasma sprayed thermal barrier coating systems
    Weeks, Matthew D.
    Subramanian, Ramesh
    Vaidya, Anirudha
    Mumm, Daniel R.
    SURFACE & COATINGS TECHNOLOGY, 2015, 273 : 50 - 59
12345