Effect of bond coat surface roughness on oxidation behaviour of air plasma sprayed thermal barrier coatings

被引：25
|
作者：
Che, C. [1 ]
Wu, G. Q. [1 ]
Qi, H. Y. [2 ]
Huang, Z. [1 ]
Yang, X. G. [2 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[2] Beijing Univ Aeronaut & Astronaut, Sch Jet Prop, Beijing 100083, Peoples R China
来源：
SURFACE ENGINEERING | 2008年 / 24卷 / 04期
关键词：
thermal barrier coating; MCrAIY; oxidation; roughness; lifetime; failure;
D O I：
10.1179/026708408X329470
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Two layered thermal barrier coatings (TBCs) with different bond coat surface roughnesses were produced by air plasma spraying. Isothermal oxidation test was carried out to evaluate the durability and oxidation behaviour of these systems. The results show that the roughness of bond coat significantly affects the lifetime of TBCs. With the increase in bond coat roughness, the lifetime decreases exponentially. The durability is enhanced by surface grinding treatments that decrease diffusion paths on the surface of the bond coat and diminish Al depletion rate. The shape and path of cracks at failure are also affected by the bond coat surface roughness.
引用
收藏
页码：276 / 279
页数：4
相关论文
共 50 条
  • [31] Phase transformation and bond coat oxidation behavior of plasma-sprayed zirconia thermal barrier coating
    Lee, CH
    Kim, HK
    Choi, HS
    Ahn, HS
    SURFACE & COATINGS TECHNOLOGY, 2000, 124 (01): : 1 - 12
  • [32] Thermal cyclic oxidation performance of plasma sprayed zirconia thermal barrier coatings with modified high velocity oxygen fuel sprayed bond coatings
    Tsai, Pi-Chuen
    Tseng, Chun-Feng
    Yang, Chung-Wei
    Kuo, Iang-Chuen
    Chou, Yia-Ling
    Lee, Jyh-Wei
    SURFACE & COATINGS TECHNOLOGY, 2013, 228 : S11 - S14
  • [33] The effect of bond coat creep on residual stresses and debonding in plasma sprayed thermal barrier systems
    Tsu, YC
    Thompson, JA
    Clyne, TW
    THERMAL SPRAY, VOLS 1 AND 2: MEETING THE CHALLENGES OF THE 21ST CENTURY, 1998, : 1565 - 1570
  • [34] Thermal shock resistance of air plasma sprayed thermal barrier coatings
    Fleck, N. A.
    Cocks, A. C. F.
    Lampenscherf, S.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (11) : 2687 - 2694
  • [35] The surface cracking behavior in air plasma sprayed thermal barrier coating system incorporating interface roughness effect
    Zhang, W. X.
    Fan, X. L.
    Wang, T. J.
    APPLIED SURFACE SCIENCE, 2011, 258 (02) : 811 - 817
  • [36] Explanation of the effect of rapid cycling on oxidation, rumpling, microcracking and lifetime of air plasma sprayed thermal barrier coatings
    Ahmadian, Shayan
    Jordan, Eric H.
    SURFACE & COATINGS TECHNOLOGY, 2014, 244 : 109 - 116
  • [37] Improvement of EB-PVD thermal barrier coatings by treatments of a vacuum plasma-sprayed bond coat
    Schulz, U.
    Bernardi, O.
    Ebach-Stahl, A.
    Vassen, R.
    Sebold, D.
    SURFACE & COATINGS TECHNOLOGY, 2008, 203 (1-2): : 160 - 170
  • [38] Air Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading
    Poursaeidi, E.
    Torkashvand, K.
    Mohammadi, M.
    INTERNATIONAL JOURNAL OF ENGINEERING, 2019, 32 (06): : 872 - 876
  • [39] Effect of bond coating surface roughness on properties of high temperature oxidation and mechanical properties in thermal barrier coatings
    Zhang, Xiaofeng
    Zhou, Kesong
    Song, Jinbing
    Zhang, Jifu
    Deng, Chunming
    Liu, Min
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2013, 41 (12): : 1674 - 1678
  • [40] Thermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
    Lu, Zhe
    Myoung, Sang-Won
    Jung, Yeon-Gil
    Balakrishnan, Govindasamy
    Lee, Jeongseung
    Paik, Ungyu
    MATERIALS, 2013, 6 (08) : 3387 - 3403
12345