Effect of bond coat surface roughness on oxidation behaviour of air plasma sprayed thermal barrier coatings

被引：25
|
作者：
Che, C. [1 ]
Wu, G. Q. [1 ]
Qi, H. Y. [2 ]
Huang, Z. [1 ]
Yang, X. G. [2 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
[2] Beijing Univ Aeronaut & Astronaut, Sch Jet Prop, Beijing 100083, Peoples R China
来源：
SURFACE ENGINEERING | 2008年 / 24卷 / 04期
关键词：
thermal barrier coating; MCrAIY; oxidation; roughness; lifetime; failure;
D O I：
10.1179/026708408X329470
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Two layered thermal barrier coatings (TBCs) with different bond coat surface roughnesses were produced by air plasma spraying. Isothermal oxidation test was carried out to evaluate the durability and oxidation behaviour of these systems. The results show that the roughness of bond coat significantly affects the lifetime of TBCs. With the increase in bond coat roughness, the lifetime decreases exponentially. The durability is enhanced by surface grinding treatments that decrease diffusion paths on the surface of the bond coat and diminish Al depletion rate. The shape and path of cracks at failure are also affected by the bond coat surface roughness.
引用
收藏
页码：276 / 279
页数：4
相关论文
共 50 条
  • [1] Effect of bond-coat surface roughness on failure mechanism and lifetime of air plasma spraying thermal barrier coatings
    LI ShaoLin
    QI HongYu
    SONG JiaNan
    YANG XiaoGuang
    CHE Chang
    Science China(Technological Sciences), 2019, (06) : 989 - 995
  • [2] Effect of bond-coat surface roughness on failure mechanism and lifetime of air plasma spraying thermal barrier coatings
    Li ShaoLin
    Qi HongYu
    Song JiaNan
    Yang XiaoGuang
    Che Chang
    SCIENCE CHINA-TECHNOLOGICAL SCIENCES, 2019, 62 (06) : 989 - 995
  • [3] Effect of bond-coat surface roughness on failure mechanism and lifetime of air plasma spraying thermal barrier coatings
    ShaoLin Li
    HongYu Qi
    JiaNan Song
    XiaoGuang Yang
    Chang Che
    Science China Technological Sciences, 2019, 62 : 989 - 995
  • [4] Effect of bond-coat surface roughness on failure mechanism and lifetime of air plasma spraying thermal barrier coatings
    LI ShaoLin
    QI HongYu
    SONG JiaNan
    YANG XiaoGuang
    CHE Chang
    Science China(Technological Sciences), 2019, 62 (06) : 989 - 995
  • [5] Effect of bond coat surface roughness on the thermal cyclic behavior of thermal barrier coatings
    Zhang, Dongbo
    Gong, Shengkai
    Xu, Huibin
    Wu, Zhongyou
    SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4): : 649 - 653
  • [6] Effects of temperature on oxidation behaviour of air plasma sprayed thermal barrier coatings
    Che, C.
    Wu, G. Q.
    Xu, H. M.
    Qi, H. Y.
    Huang, Z.
    Yang, X. G.
    MATERIALS AT HIGH TEMPERATURES, 2009, 26 (04) : 365 - 368
  • [7] Role of internal oxidation on the failure of air plasma sprayed thermal barrier coatings with a double-layered bond coat
    Zou, Zhonghua
    Jia, Libing
    Yang, Lixia
    Shan, Xiao
    Luo, Lirong
    Guo, Fangwei
    Zhao, Xiaofeng
    Xiao, Ping
    SURFACE & COATINGS TECHNOLOGY, 2017, 319 : 370 - 377
  • [8] Effect of bond coat topography on the fracture mechanics and lifetime of air-plasma sprayed thermal barrier coatings
    Martins, Joao P.
    Yu, Hanyang
    Chen, Ying
    Brewster, G.
    McIntyre, R.
    Xiao, Ping
    SURFACE & COATINGS TECHNOLOGY, 2021, 421
  • [9] CRITICAL LOCATIONS IN PLASMA SPRAYED THERMAL BARRIER COATINGS DUE TO IRREGULARITIES OF BOND COAT SURFACE
    Slamecka, Karel
    Skalka, Petr
    Jech, David
    Klakurkova, Lenka
    Celko, Ladislav
    IRF2016: 5TH INTERNATIONAL CONFERENCE INTEGRITY-RELIABILITY-FAILURE, 2016, : 1115 - 1116
  • [10] Influence of Heat Treatment on the Bond Coat Cyclic Oxidation Behaviour in an Air-plasma-sprayed Thermal Barrier Coating System
    B.R. Marple
    P.C. Patnaik
    材料热处理学报, 2004, (05) : 923 - 929
12345