Deweighting and Mechanical Properties of PTT/PA6 Bicomponent Filament Yarns

被引：0
|
作者：
Guo, Jing [1 ]
Xiang, Heng-xue [2 ]
Chen, Ying-tao [2 ]
Wang, Qian-qian
机构：
[1] Dalian Polytech Univ, Sch Chem Engn & Mat Sci, Dalian, Liaoning, Peoples R China
[2] Donghua Univ, Shanghai, Peoples R China
来源：
AATCC REVIEW | 2012年 / 12卷 / 02期
关键词：
Alkaline Hydrolysis; Deweighting; Drawn Textured Yarn; PET; Polyamide; 6; PTT; Splitting;
D O I：
暂无
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Polytrimethylene terephthalate/polyamide 6 drawn-textured yarn was split by alkaline hydrolysis to produce superfine filaments with triangular cross-sections. Alkali deweighting, splitting morphology, mechanical property, heat shrinkage property, and crimping performance of this yarn were tested and results compared to PET/polyamide 6 drawn textured and drawn twist yarns. Results showed that alkali deweighting rate of this new yarn increased with alkali concentration and temperature. Alkali deweighting was less than that of the PET/polyamide 6 yarns studied. Both breaking strength and breaking work decreased as alkali concentration increased. Heat shrinkage and crimp shrinkage of the new yarn was also determined and compared with the PET/polyamide 6 yarns.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [21] Investigating the role of PA6/GO interactions on the morphological, rheological, and mechanical properties of PA6/ABS/GO nanocomposites
    Dadashi, P.
    Babaei, A.
    Khoshnood, M.
    POLYMER-PLASTICS TECHNOLOGY AND MATERIALS, 2023, 62 (06): : 756 - 770
  • [22] PA6/NBR blends: improvement of processability and mechanical properties
    Gomes, Ana C. O.
    Soares, Bluma G.
    Oliveira, Marcia G.
    Oliveira, Marcelo F. L.
    Paranhos, Caio M.
    E-POLYMERS, 2009,
  • [23] Effect of PA6 addition on the mechanical properties of PMMA blends
    Li, Zhenhua
    MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 : 509 - 512
  • [24] PA6/NBR blends: Improvement of processability and mechanical properties
    Gomes, Ana C. O.
    Soares, Bluma G.
    Oliveira, Marcia G.
    Oliveira, Marcelo F. L.
    Paranhos, Caio M.
    E-Polymers, 2009,
  • [25] The Mechanical Properties of Nanocomposites Reinforced with PA6 Electrospun Nanofibers
    Lasenko, Inga
    Sanchaniya, Jaymin Vrajlal
    Kanukuntla, Sai Pavan
    Ladani, Yagnik
    Viluma-Gudmona, Arta
    Kononova, Olga
    Lusis, Vitalijs
    Tipans, Igors
    Selga, Turs
    POLYMERS, 2023, 15 (03)
  • [26] Moisture transport in PA6 and its influence on the mechanical properties
    P. Sharma
    A. Sambale
    M. Stommel
    M. Maisl
    H.-G. Herrmann
    S. Diebels
    Continuum Mechanics and Thermodynamics, 2020, 32 : 307 - 325
  • [27] Moisture transport in PA6 and its influence on the mechanical properties
    Sharma, P.
    Sambale, A.
    Stommel, M.
    Maisl, M.
    Herrmann, H-G
    Diebels, S.
    CONTINUUM MECHANICS AND THERMODYNAMICS, 2020, 32 (02) : 307 - 325
  • [28] Flame retardancy, thermal, and mechanical properties of flame retardant PA6/SGF and PPS/PA6/SGF composites
    Yu, Zhixing
    Ye, Yingchun
    Zhang, Yuhong
    Jia, Zhenlong
    Lu, Yiqing
    Li, Yingcheng
    JOURNAL OF APPLIED POLYMER SCIENCE, 2025, 142 (05)
  • [29] The Research of Alkali Treatment and Dyeability of PTT/PA6 Conjugate Fiber
    Guo Jing
    Yuan Guo-bao
    Wang Hong
    2010 INTERNATIONAL FORUM ON BIOMEDICAL TEXTILE MATERIALS, PROCEEDINGS, 2010, : 275 - 279
  • [30] Mechanical, Chemical, Thermal, and Rheological Properties of Recycled PA6/ABS Binary and PA6/PA66/ABS Ternary Blends
    Kuram, Emel
    Sarac, Levent
    Ozcelik, Babur
    Yilmaz, Faruk
    JOURNAL OF APPLIED POLYMER SCIENCE, 2014, 131 (18) : 9603 - 9610
12345