Deweighting and Mechanical Properties of PTT/PA6 Bicomponent Filament Yarns

被引：0
|
作者：
Guo, Jing [1 ]
Xiang, Heng-xue [2 ]
Chen, Ying-tao [2 ]
Wang, Qian-qian
机构：
[1] Dalian Polytech Univ, Sch Chem Engn & Mat Sci, Dalian, Liaoning, Peoples R China
[2] Donghua Univ, Shanghai, Peoples R China
来源：
AATCC REVIEW | 2012年 / 12卷 / 02期
关键词：
Alkaline Hydrolysis; Deweighting; Drawn Textured Yarn; PET; Polyamide; 6; PTT; Splitting;
D O I：
暂无
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
Polytrimethylene terephthalate/polyamide 6 drawn-textured yarn was split by alkaline hydrolysis to produce superfine filaments with triangular cross-sections. Alkali deweighting, splitting morphology, mechanical property, heat shrinkage property, and crimping performance of this yarn were tested and results compared to PET/polyamide 6 drawn textured and drawn twist yarns. Results showed that alkali deweighting rate of this new yarn increased with alkali concentration and temperature. Alkali deweighting was less than that of the PET/polyamide 6 yarns studied. Both breaking strength and breaking work decreased as alkali concentration increased. Heat shrinkage and crimp shrinkage of the new yarn was also determined and compared with the PET/polyamide 6 yarns.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [11] Multinanolayered PA6/Cloisite and PE/PA6/Cloisite composites: Structure, mechanical and barrier properties
    Marais, Stephane
    Lozay, Quentin
    Follain, Nadege
    Soulestin, Jeremie
    Couvrat, Nicolas
    Dargent, Eric
    COMPOSITES PART B-ENGINEERING, 2024, 271
  • [12] The Crystallinity and Oritetation Structure and Crimp Properties of PET/PTT Bicomponent Filament
    Xiao, Hong
    Shi, Meiwu
    Liu, Lili
    Dai, Guoliang
    ADVANCES IN TEXTILE ENGINEERING AND MATERIALS, 2013, 627 : 110 - +
  • [13] Influence of reactive compatibilizers on the rheometrical and mechanical properties of PA6/LDPE and PA6/HDPE blends
    Pankaj Agrawal
    André. W. B. Rodrigues
    Edcleide M. Araújo
    Tomás J. A. Mélo
    Journal of Materials Science, 2010, 45 : 496 - 502
  • [14] Influence of reactive compatibilizers on the rheometrical and mechanical properties of PA6/LDPE and PA6/HDPE blends
    Agrawal, Pankaj
    Rodrigues, Andre W. B.
    Araujo, Edcleide M.
    Melo, Tomas J. A.
    JOURNAL OF MATERIALS SCIENCE, 2010, 45 (02) : 496 - 502
  • [15] Study on the process technology of PA6/PET bicomponent fiber
    Lin, Y., 2001, Editorial Board of Journal of Dong Hua University (18):
  • [16] Study on the Process Technology of PA6/PET Bicomponent Fiber
    林耀
    Journal of DongHua University, 2001, (04) : 31 - 35
  • [17] Morphology and Mechanical Properties of PA6/ABS blends
    Guo, Jianbing
    Zhang, Kaizhou
    Qin, Shuhao
    ADVANCED ENGINEERING MATERIALS II, PTS 1-3, 2012, 535-537 : 2600 - 2605
  • [18] MECHANICAL PROPERTIES OF NANOCOMPOSITES BASED ON PA6 BLENDS
    Agrawal, Pankaj
    Brito, Gustavo F.
    Cunha, Bartira B.
    Cavalcanti, Shirley N.
    Araujo, Edcleide M.
    Melo, Tomas J. A.
    TMS 2012 141ST ANNUAL MEETING & EXHIBITION - SUPPLEMENTAL PROCEEDINGS, VOL 2: MATERIALS PROPERTIES, CHARACTERIZATION, AND MODELING, 2012, : 613 - 619
  • [19] Mechanical properties and morphology of PA6/EVA blends
    Bhattacharyya, AR
    Maiti, SN
    Misra, A
    JOURNAL OF APPLIED POLYMER SCIENCE, 2002, 85 (08) : 1593 - 1606
  • [20] Fibre reinforced nanocomposites: Mechanical properties of PA6/clay and glass fibre/PA6/clay nanocomposites
    Clifford, Mike J.
    Wan, Tong
    POLYMER, 2010, 51 (02) : 535 - 539
12345