Change in Wear Behaviour of Ti and Ti6Al4V after Plasma Immersion Ion Implantation

被引：5
|
作者：
Ducherow, Marlen [1 ]
Fleischer, Alexander [1 ]
Maendl, Stephan [1 ]
机构：
[1] Leibniz Inst Oberflachenmodifizierung, D-04318 Leipzig, Germany
来源：
PLASMA PROCESSES AND POLYMERS | 2007年 / 4卷
关键词：
diffusion; PIII; titanium; wear;
D O I：
10.1002/ppap.200731414
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The influence of the layer thickness and the microstructure of Ti and Ti6Al4V treated with oxygen plasma immersion ion implantation (PIII) on the respective wear rates are investigated. The implantation temperature was varied from 250 up to 550 degrees C at fluences between 6 and 18 x 10 17 at. . cm(-2). The wear tests were performed in a rotating ball-on-disc tribometer with an alumina ball. No difference in the wear rate was observed between Ti and Ti6AlV at higher temperatures, while significant differences were presented at lower temperatures, which were not solely correlated with the layer thickness.
引用
收藏
页码：S602 / S606
页数：5
相关论文
共 50 条
  • [31] Corrosion behavior of Ti-6Al-4V alloy treated by plasma immersion ion implantation process
    da Silva, L. L. G.
    Ueda, M.
    Silva, M. M.
    Codaro, E. N.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (19-20): : 8136 - 8139
  • [32] Plasma immersion ion implantation (PIII) influence on Ti-6Al-4V alloy: Frequency effect
    Oliveira, V. M. C. A.
    Cioffi, M. O. H.
    Barboza, M. J. R.
    Landers, R.
    Schmitt, B.
    Tapia, D. C. A. R.
    Voorwald, H. J. C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 109 : 157 - 165
  • [33] A comparison of the surface characteristics and ion release of Ti6Al4V and heat-treated Ti6Al4V
    Lee, TM
    Chang, E
    Yang, CY
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 2000, 50 (04): : 499 - 511
  • [34] Characteristics and Wear Performance of Nitrided Ti6Al4V
    Siyahjani, Farid
    Cimenoglub, Huseyin
    DIFFUSION IN SOLIDS AND LIQUIDS VII, 2012, 326-328 : 494 - 497
  • [35] Tribological performances of Ti6Al4V alloy modified by Ta ion implantation
    Leng Chongyan
    Zhang Xu
    Zhou Rong
    Zhang Huixing
    Wu Xianying
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (03) : 556 - 560
  • [36] Mechanisms of Premature Fracture in Modular Neck Stems Made of CoCrMo/Ti6Al4V and Ti6Al4V/Ti6Al4V Alloy
    Dolinar, Drago
    Gorensek, Miro
    Avsec, Klemen
    Batic, Barbara Setina
    Hocevar, Matej
    Godec, Matjaz
    Zuzek, Borut
    Debeljak, Mojca
    Jenko, Monika
    Grant, John T.
    Kocjancic, Bostjan
    COATINGS, 2023, 13 (07)
  • [37] Improved properties of Ti6Al4V by means of nitrogen high temperature plasma based ion implantation
    Oliveira, R. M.
    Mello, C. B.
    Silva, G.
    Goncalves, J. A. N.
    Ueda, M.
    Pichon, L.
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 : S111 - S114
  • [38] WEAR PERFORMANCE OF Ti6Al4V ALLOY MODIFIED BY Ag plus Ta DUAL-ION IMPLANTATION
    Leng Chongyan
    Zhou Rong
    Zhang Xu
    Lu Dehong
    Liu Hongxi
    ACTA METALLURGICA SINICA, 2009, 45 (06) : 764 - 768
  • [39] Structure and tribological performance by nitrogen and oxygen plasma based ion implantation on Ti6Al4V alloy
    Feng, Xingguo
    Sun, Mingren
    Ma, Xinxin
    Tang, Guangze
    APPLIED SURFACE SCIENCE, 2011, 257 (23) : 9904 - 9908
  • [40] Measurement and analysis of tool wear and surface characteristics in micro turning of SLM Ti6Al4V and wrought Ti6Al4V
    Airao, Jay
    Kishore, Hreetabh
    Nirala, Chandrakant K.
    MEASUREMENT, 2023, 206
12345