Change in Wear Behaviour of Ti and Ti6Al4V after Plasma Immersion Ion Implantation

被引：5
|
作者：
Ducherow, Marlen [1 ]
Fleischer, Alexander [1 ]
Maendl, Stephan [1 ]
机构：
[1] Leibniz Inst Oberflachenmodifizierung, D-04318 Leipzig, Germany
来源：
PLASMA PROCESSES AND POLYMERS | 2007年 / 4卷
关键词：
diffusion; PIII; titanium; wear;
D O I：
10.1002/ppap.200731414
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
The influence of the layer thickness and the microstructure of Ti and Ti6Al4V treated with oxygen plasma immersion ion implantation (PIII) on the respective wear rates are investigated. The implantation temperature was varied from 250 up to 550 degrees C at fluences between 6 and 18 x 10 17 at. . cm(-2). The wear tests were performed in a rotating ball-on-disc tribometer with an alumina ball. No difference in the wear rate was observed between Ti and Ti6AlV at higher temperatures, while significant differences were presented at lower temperatures, which were not solely correlated with the layer thickness.
引用
收藏
页码：S602 / S606
页数：5
相关论文
共 50 条
  • [1] Plasma immersion ion implantation of Ti6Al4V
    Wang, J.S.
    Chen, Y.R.
    Chen, Q.W.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2001, 15 (02): : 225 - 229
  • [2] Wear resistance of plasma immersion ion implanted Ti6Al4V
    Johns, SM
    Bell, T
    Samandi, M
    Collins, GA
    SURFACE & COATINGS TECHNOLOGY, 1996, 85 (1-2): : 7 - 14
  • [3] High temperature plasma immersion ion implantation of Ti6Al4V
    Ueda, M.
    Silva, M. M.
    Lepienski, C. M.
    Soares, P. C., Jr.
    Goncalves, J. A. N.
    Reuther, H.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (9-11): : 4953 - 4956
  • [4] Improvement of tribological properties of Ti6Al4V by nitrogen plasma immersion ion implantation
    Ueda, M
    Silva, MM
    Otani, C
    Reuther, H
    Yatsuzuka, M
    Lepienski, CM
    Berni, LA
    SURFACE & COATINGS TECHNOLOGY, 2003, 169 : 408 - 410
  • [5] Wear and corrosion behaviors of Ti6Al4V alloy biomedical materials by silver plasma immersion ion implantation process
    Liu, Hongxi
    Xu, Qian
    Zhang, Xiaowei
    Wang, Chuanqi
    Tang, Baoyin
    THIN SOLID FILMS, 2012, 521 : 89 - 93
  • [6] Study on surface properties of Ti6Al4V alloy by oxygen plasma immersion ion implantation
    Xin, Guoqiang
    Yang, Xueqin
    Dong, Nan
    Tian, Xiubo
    Yang, Shiqin
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2008, 37 (02): : 316 - 319
  • [7] Study on surface properties of Ti6Al4V alloy by oxygen plasma immersion ion implantation
    Xin Guoqiang
    Yang Xueqin
    Dong Nan
    Tian Xiubo
    Yang Shiqin
    RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (02) : 316 - 319
  • [8] Effect of plasma immersion ion implantation on wear behavior of Ti-6Al-4V alloy
    Resende, Fabricia Assis
    Silva, Maria Margareth
    Oliveira, Rogerio de Moares
    Silva, Carla
    Pichon, Luc
    Radi, Polyana Alves
    dos Reis, Adriano Goncalves
    Reis, Danieli Aparecida Pereira
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2023, 11 (01)
  • [9] Effects of plasma immersion ion implantation of oxygen on mechanical properties and microstructure of Ti6Al4V
    Loinaz, A
    Rinner, M
    Alonso, F
    Onate, JI
    Ensinger, W
    SURFACE & COATINGS TECHNOLOGY, 1998, 104 : 262 - 267
  • [10] Depth distributions and wear behaviour of ion implanted Ti6Al4V
    Schmidt, H.
    Baumann, H.
    Rueck, D.M.
    Materials Science Forum, 1997, 248-249 : 209 - 212
12345