Fretting corrosion-induced microstructural evolution of Alloy 690TT tube in high temperature pressurised water

被引：11
|
作者：
Zhang, Yusheng [1 ,2 ]
Wu, Bin [1 ,2 ]
Ming, Hongliang [1 ,2 ]
Li, Yifeng [3 ]
Zhang, Zhiming [4 ]
Wang, Jianqiu [1 ,4 ]
Han, En-Hou [1 ,4 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
[3] Shanghai Univ, Instrumental Anal & Res Ctr, 99 Shangda Rd, Shanghai 200444, Peoples R China
[4] Inst Corros Sci & Technol, Guangzhou 510530, Peoples R China
来源：
CORROSION SCIENCE | 2022年 / 209卷
基金：
中国国家自然科学基金;
关键词：
Fretting corrosion; Alloy; 690TT; High temperature pressurised water; Oxidation; Microstructure; TRIBOLOGICALLY TRANSFORMED STRUCTURE; 405; STAINLESS-STEEL; NICKEL-BASE ALLOYS; WEAR BEHAVIOR; DYNAMIC RECRYSTALLIZATION; DELAMINATION THEORY; MECHANISM; AMORPHIZATION; AMPLITUDE; XPS;
D O I：
10.1016/j.corsci.2022.110774
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The friction-induced microstructural evolution of Alloy 690TT tubes submerged in a high temperature pres-surised water was investigated. Two typical local regions characterised by significantly different worn mor-phologies (resulting from the stress field and material couple) were investigated in detail. A thin third-body layer and a thick Fe-rich layer were observed and their oxidation behaviour was analysed. Moreover, the main oxide was spinel, whereas the amorphous band was only observed in the Fe-rich layer. The tribologically transformed structure is formed by the mechanism of discontinuous dynamic recrystallisation. Finally, the microstructural evolution of the two areas during fretting corrosion is discussed.
引用
收藏
页数：17
相关论文
共 50 条
  • [21] Fretting Wear Characteristics of 690TT Alloy Tube Under Gross Slip Conditions
    Tan W.
    Tian C.
    Tianjin Daxue Xuebao (Ziran Kexue yu Gongcheng Jishu Ban)/Journal of Tianjin University Science and Technology, 2022, 55 (09): : 895 - 902
  • [22] The Evolution of Fretting Wear Behavior and Damage Mechanism in Alloy 690TT with Cycle Number
    Xin, Long
    Han, Yongming
    Ling, Ligong
    Zhang, Weidong
    Lu, Yonghao
    Shoji, Tetsuo
    MATERIALS, 2020, 13 (10)
  • [23] Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water
    Li, Z. H.
    Lu, Y. H.
    Hong, C.
    Zhao, Y. G.
    Han, Y. M.
    Shoji, T.
    CORROSION SCIENCE, 2023, 212
  • [24] Electrochemical Corrosion Performance of Mechanically Polished Alloy 690TT at High-Temperature Water (200°C)
    Arjmand, Farzin
    Zhang, Lefu
    CORROSION, 2015, 71 (12) : 1481 - 1489
  • [25] The damage mechanism of Alloy 690TT against Alloy 600 caused by fretting wear in room temperature pure water
    Xin, Long
    Huang, Qian
    Han, Yongming
    Lu, Yonghao
    Zhang, Weidong
    Shoji, Tetsuo
    MATERIALS CHARACTERIZATION, 2020, 161 (161)
  • [26] Stress corrosion behavior of scratched Alloy 690TT steam generator tube in chlorine-containing high-temperature pressurized water
    Wu, Bin
    Meng, Fanjiang
    Zhang, Zhiming
    Li, Rongbo
    Ming, Hongliang
    Wang, Jianqiu
    Han, En-Hou
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (10): : 1563 - 1574
  • [27] The impact fretting corrosion behavior and damage mechanism of Inconel 690TT under different impact forces in high temperature pressurized water
    Bian, W. W.
    Lu, Y. H.
    Kang, L. Z.
    Zhang, X. F.
    Xin, L.
    Shoji, T.
    CORROSION SCIENCE, 2024, 240
  • [28] Study on the SCC behavior induced by creep cavities on scratched surface of Alloy 690TT in high temperature water
    Wang, X. Y.
    Shang, C. G.
    Li, Z. H.
    Bai, Y. K.
    Liu, T. G.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2022, 196
  • [29] The role of hydrogen on lead-induced localized corrosion of Alloy 690TT
    Li, Weipeng
    Mi, Zhishan
    He, Yang
    Han, Yaolei
    Shi, Fangjie
    Peng, Qunjia
    Qiao, Lijie
    CORROSION SCIENCE, 2024, 240
  • [30] MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING
    Meng Fanjiang
    Wang Jianqiu
    Han En-Hou
    Shoji, Testuo
    Ke Wei
    ACTA METALLURGICA SINICA, 2011, 47 (07) : 839 - 846
12345