The role of hydrogen on lead-induced localized corrosion of Alloy 690TT

被引：0
|
作者：
Li, Weipeng [1 ,2 ]
Mi, Zhishan [1 ]
He, Yang [1 ]
Han, Yaolei [2 ]
Shi, Fangjie [2 ]
Peng, Qunjia [2 ]
Qiao, Lijie [1 ]
机构：
[1] Univ Sci & Technol Beijing, Beijing Adv Innovat Ctr Mat Genome Engn, Beijing 100083, Peoples R China
[2] Suzhou Nucl Power Res Inst, Suzhou 215004, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Lead; Hydrogen; Nickel-based alloy; Passive film; Localized corrosion; DFT calculation; INDUCED PASSIVITY-DEGRADATION; GENERATOR TUBING ALLOY; PROBE FORCE MICROSCOPY; ELECTRON WORK FUNCTION; POTENTIAL-PH DIAGRAMS; HIGH-TEMPERATURE; CAUSTIC SOLUTION; IN-SITU; BEHAVIOR; CRACKING;
D O I：
10.1016/j.corsci.2024.112469
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The vital role of hydrogen on lead-induced localized corrosion of Alloy 690TT in the simulated secondary crevice chemistries of pressurized water reactor at 25 degrees C is investigated by using surface analysis techniques and calculations. Density functional theory (DFT) calculation reveals that there is a coupling effect between lead and hydrogen on inhibiting the kinetic diffusion of oxygen vacancies. Experimental results show that hydrogen causes the change of most easily-corroded location from the grain/carbide interface to the TiN/nucleus interface in the lead-induced corrosion process, which provides a new interpreting sight as for lead-induced stress corrosion cracking mode of nickel-based Alloys.
引用
收藏
页数：13
相关论文
共 50 条
  • [1] Lead-induced stress corrosion cracking (PbSCC) initiation in alloy 690TT in caustic environment
    Mazzei, G. B.
    Burke, M. G.
    Horner, D. A.
    Scenini, F.
    CORROSION SCIENCE, 2022, 206
  • [2] Localized corrosion behavior of scratches on nickel-base Alloy 690TT
    Meng, Fanjiang
    Han, En-Hou
    Wang, Jianqiu
    Zhang, Zhiming
    Me, Wei
    ELECTROCHIMICA ACTA, 2011, 56 (04) : 1781 - 1785
  • [3] Lead-induced stress corrosion behavior of Alloy 690
    Li, C.-T. (lctslj0630@hotmail.com), 1600, University of Science and Technology Beijing (35):
  • [4] The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead
    Hou Qiang
    Liu Zhiyong
    Li Chengtao
    Li Xiaogang
    CORROSION SCIENCE, 2017, 128 : 154 - 163
  • [5] MICROSTRUCTURE NEAR SCRATCH ON ALLOY 690TT AND STRESS CORROSION INDUCED BY SCRATCHING
    Meng Fanjiang
    Wang Jianqiu
    Han En-Hou
    Shoji, Testuo
    Ke Wei
    ACTA METALLURGICA SINICA, 2011, 47 (07) : 839 - 846
  • [6] Stress corrosion cracking behavior and mechanism of scratched Alloy 690TT in lead-containing caustic solution
    Li, Z. H.
    You, L.
    Wang, L.
    Zhang, X. F.
    Su, Y.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2025, 245
  • [7] Effects of dissolved hydrogen on general corrosion behavior and oxide films of alloy 690TT in PWR primary water
    Jeon, Soon-Hyeok
    Lee, Eun-Hee
    Hur, Do Haeng
    JOURNAL OF NUCLEAR MATERIALS, 2017, 485 : 113 - 121
  • [8] Microstructural characteristics of Alloy 690TT subjected to fretting corrosion in high temperature water
    Xin, Long
    Yang, Beibei
    Li, Jie
    Lu, Yonghao
    Shoji, Tetsuo
    CORROSION SCIENCE, 2017, 123 : 116 - 128
  • [9] Influence of surface roughness on the corrosion behavior of Alloy 690TT in PWR primary water
    Seo, Myung Ji
    Shim, Hee-Sang
    Kim, Kyung Mo
    Hong, Sun-Ig
    Hur, Do Haeng
    NUCLEAR ENGINEERING AND DESIGN, 2014, 280 : 62 - 68
  • [10] Effect of Surface Scratch on Corrosion Behavior of Alloy 690TT Heat Exchanger Tubes
    Meng F.
    Wu B.
    Lv Y.
    Ming H.
    Bao Y.
    Wang J.
    Han E.-H.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2021, 35 (11): : 827 - 834
12345