Lead-induced stress corrosion behavior of Alloy 690

被引：0
|
作者：
机构：
[1] Liu, Fei-Hua
[2] Li, Cheng-Tao
[3] Zhang, Xin
[4] Li, Yan
[5] Ren, Ai
来源：
Li, C.-T. (lctslj0630@hotmail.com) | 1600年 / University of Science and Technology Beijing卷 / 35期
关键词：
Cracks - Scanning electron microscopy - High temperature corrosion - Nickel alloys - Nuclear power plants - Corrosive effects - Nuclear fuels - Residual stresses;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [1] Lead-induced stress corrosion cracking behavior of mechanically surface-treated alloy 690
    Li, Nana
    Shi, San-Qiang
    Luo, Jingli
    Lu, Jian
    Wang, Ning
    MATERIALS RESEARCH LETTERS, 2016, 4 (03): : 180 - 184
  • [2] The role of hydrogen on lead-induced localized corrosion of Alloy 690TT
    Li, Weipeng
    Mi, Zhishan
    He, Yang
    Han, Yaolei
    Shi, Fangjie
    Peng, Qunjia
    Qiao, Lijie
    CORROSION SCIENCE, 2024, 240
  • [3] Lead-induced stress corrosion cracking (PbSCC) initiation in alloy 690TT in caustic environment
    Mazzei, G. B.
    Burke, M. G.
    Horner, D. A.
    Scenini, F.
    CORROSION SCIENCE, 2022, 206
  • [4] Condition for Lead-Induced Corrosion of Alloy 690 in an Alkaline Steam Generator Crevice Solution
    Lu, B. T.
    Luo, J. L.
    Peng, B.
    Palani, A.
    Lu, Y. C.
    CORROSION, 2009, 65 (09) : 601 - 610
  • [5] A parametric study of the lead-induced SCC of alloy 690
    Sarver, JM
    Miglin, BP
    McIlree, AR
    PROCEEDINGS OF THE EIGHTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS - WATER REACTORS, VOLS 1 AND 2, 1997, : 208 - 215
  • [6] Effect of lead on the corrosion behavior of Alloy 690
    Li, Chengtao
    Fei, Kexun
    Song, Lijun
    Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University, 2015, 36 (07): : 1001 - 1005
  • [7] Lead assisted stress corrosion cracking of Alloy 690
    Psaila-Dombrowski, MJ
    Hua, FH
    Doherty, PE
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 703 - 710
  • [8] Stress Corrosion Cracking Behavior of Alloy 690 in Crevice Environment (Pb
    Shin, Jung-Ho
    Lim, Sang-Yeop
    Kim, Dong-Jin
    CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2018, 17 (03): : 116 - 122
  • [9] Stress corrosion cracking behavior and mechanism of scratched Alloy 690TT in lead-containing caustic solution
    Li, Z. H.
    You, L.
    Wang, L.
    Zhang, X. F.
    Su, Y.
    Lu, Y. H.
    Shoji, T.
    CORROSION SCIENCE, 2025, 245
  • [10] Stress corrosion behavior of alloy 690 in primary water of a nuclear power plant
    Ren, A. (renai@cgnpc.com.cn), 1600, Editorial Board of Journal of Harbin Engineering (34):
12345