InGaN/GaN LEDs grown on Si(111): dependence of device performance on threading dislocation density and emission wavelength

We demonstrate the growth of crack-free blue and green-emitting LED structures grown on 2-inch and 6-inch Si(111) substrates by metalorganic vapour phase epitaxy (MOVPE), using AlN nucleation layers and AlGaN buffer layers for stress management. LED device performance and its dependence on threading dislocation (TD) density and emission wavelength were studied. Despite the inherently low light extraction efficiency, an output power of 1.2 mW at 50 mA was measured from a 500 mu m square planar device, emitting at 455 nm. The light output decreases dramatically as the emission wavelength increases from 455 nm to 510 nm. For LED devices emitting at similar wavelength, the light output was more than doubled when the TD density was reduced from 5x10(9) cm(-2) to 2x10(9) cm(-2). Our results clearly show that high TD density is detrimental to the overall light output, highlighting the need for further TD reduction for structures grown on Si. (C) 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim