Accelerated corrosion of Ni-based alloys in molten chloride salts, due to Ni2Cr phase formation

被引：0
|
作者：
Teng, Fei [1 ]
Copeland-Johnson, Trishelle M. [1 ,2 ]
Tucker, Julie D. [3 ]
Cao, Guoping [4 ]
机构：
[1] Idaho Natl Lab, Div Characterizat & Postirradiat Examinat, Idaho Falls, ID 83415 USA
[2] Idaho Natl Lab, Glenn T Seaborg Inst, Idaho Falls, ID 83415 USA
[3] Oregon State Univ, Sch Mech Ind & Mfg Engn, Corvallis, OR 97331 USA
[4] Idaho Natl Lab, Div Fuel Cycle Sci & Technol, Idaho Falls, ID 83415 USA
来源：
MATERIALIA | 2023年 / 31卷
关键词：
Nickel-based alloys; Long-range ordering; Molten salt corrosion; LONG-RANGE ORDER; MATERIALS CHALLENGES; CR; MO; CHROMIUM; STRESS; PRECIPITATION; STABILITY;
D O I：
10.1016/j.mtla.2023.101875
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
To understand how the precipitation of long-range ordering (LRO) in alloys affects molten salt corrosion, two NiCr model alloys-one in as-received (AR) condition, the other isothermally aged to contain MoPt2-type Ni2Crordered precipitates, and both featuring the same Ni-33at%Cr composition-were tested for 500 hours in molten NaCl-MgCl2 salt at 550 degrees C. Post-corrosion weight loss analysis and advanced microstructural characterization of the corroded alloys revealed (through comparison with the AR specimens) that the ordered phase significantly accelerated the corrosion process. This suggests that the loss of Cr atoms in the corroded Ni2Cr-ordered superlattice structure, which creates extra weakness for molten salt corrosion. In terms of high-temperature corrosion resistance, the results of this study emphasize the importance of phase stability when designing alloys for moltensalt applications.
引用
收藏
页数：7
相关论文
共 50 条
  • [41] In-depth corrosion mechanisms of Fe- and Ni-based alloys in molten solar salt with varying extents of chloride and sulfate impurities
    Oskay, C.
    Gregoire, B.
    Meissner, T. M.
    Burek, B. O.
    Solimani, A.
    Galetz, M. C.
    CORROSION SCIENCE, 2025, 247
  • [42] Investigation on corrosion behavior of Ni-based alloys in molten fluoride salt using synchrotron radiation techniques
    Liu, Min
    Zheng, Junyi
    Lu, Yanling
    Li, Zhijun
    Zou, Yang
    Yu, Xiaohan
    Zhou, Xingtai
    JOURNAL OF NUCLEAR MATERIALS, 2013, 440 (1-3) : 124 - 128
  • [43] SUBSTRUCTURES OBSERVED AFTER LASER IRRADIATION OF THE NI2CR AND NI3FE ORDERED ALLOYS
    RICHARD, MF
    EYMERY, JP
    GAREM, H
    JOURNAL DE MICROSCOPIE ET DE SPECTROSCOPIE ELECTRONIQUES, 1981, 6 (03): : 323 - &
  • [44] Corrosion behavior of Ni-based amorphous alloys and their crystalline counterparts
    Wang, A. P.
    Chang, X. C.
    Hou, W. L.
    Wang, J. Q.
    CORROSION SCIENCE, 2007, 49 (06) : 2628 - 2635
  • [45] Hot Corrosion Behaviors of Ni-14%Cr Alloys in Molten Sulfate
    Lu Xudong Tian Sugui Shui Li Yu Xingfu Shenyang University of Technology Shenyang China Shenyang Ligong University Shenyang China
    稀有金属材料与工程, 2009, 38(S3) (S3) : 17 - 19
  • [46] Hot Corrosion Behaviors of Ni-14%Cr Alloys in Molten Sulfate
    Lu Xudong
    Tian Sugui
    Shui Li
    Yu Xingfu
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 17 - 19
  • [47] Combined effect of molten fluoride salt and irradiation on Ni-based alloys
    Bakai, A. S.
    MATERIALS ISSUES FOR GENERATION IV SYSTEMS: STATUS, OPEN QUESTIONS AND CHALLENGES, 2008, : 537 - +
  • [48] Corrosion Behavior of Pure Cr, Ni, and Fe Exposed to Molten Salts at High Temperature
    Sotelo-Mazon, O.
    Cuevas-Arteaga, C.
    Porcayo-Calderon, J.
    Salinas Bravo, V. M.
    Izquierdo-Montalvo, G.
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2014, 2014
  • [49] Corrosion of pure Ni and two Ni-based alloys in presence of ZnCl2-KCl salt deposit
    Li, Y.S.
    Wang, F.G.
    Niu, Y.
    Wu, W.T.
    2001, Rare Metals Materials and Engineering Press (30):
  • [50] Corrosion of pure Ni and two Ni-based alloys in presence of ZnCl2-KCl salt deposit
    Li, YS
    Wang, FG
    Niu, Y
    Wu, WT
    RARE METAL MATERIALS AND ENGINEERING, 2001, 30 (05) : 376 - 379
12345