Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

被引:5
|
作者
Lu, Yuxian [1 ,2 ]
Zhang, Hao [1 ]
Xue, Peng [1 ]
Wu, Lihui [1 ]
Liu, Fengchao [1 ]
Jia, Luanluan [3 ]
Ni, Dingrui [1 ]
Xiao, Bolv [1 ]
Ma, Zongyi [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China
[3] Binzhou Inst Technol, Shandong Key Lab Adv Aluminum Mat & Technol, Weiqiao UCAS Sci & Technol Pk, Binzhou 256606, Peoples R China
基金
中国国家自然科学基金;
关键词
additive manufacturing; laser powder bed fusion; Al-Mg-Sc-Zr alloy; fine grain strengthening; solution strengthening; MECHANICAL-PROPERTIES; GRAIN-REFINEMENT; ENERGY DENSITY; AL-12SI ALLOY; LASER; STRENGTH; PRECIPITATION; EVOLUTION; PARAMETER; BEHAVIOR;
D O I
10.3390/cryst13060913
中图分类号
O7 [晶体学];
学科分类号
0702 ; 070205 ; 0703 ; 080501 ;
摘要
Laser powder bed fusion (LPBF) is a typical additive manufacturing technology that offers significant advantages in the production of complex components. With the rapid heating and cooling characteristics of LPBF, a large amount of solid solution of alloying elements in the matrix can be achieved to form supersaturated solid solutions, thus enhancing the properties of LPBF alloys. For the unique microstructure, the heat treatment process needs to be adjusted accordingly. In this work, a Zr/Sc-modified Al-Mg alloy processed by laser powder bed fusion (LPBF) with relatively low cost and good mechanical properties was investigated. The fine microstructure was obtained under rapid solidification conditions. The nanoscale Al-3(Sc,Zr) particles precipitated at the molten pool boundary during solidification. These particles, as effective heterogeneous nucleators, further refined the & alpha;-Al grains and improved the mechanical properties of the alloy. As a result, the alloy exhibited a heterogeneous microstructure consisting of columnar grains in the center of the molten pool and equiaxed grains at the boundaries. The rapid solidification resulted in the supersaturation of solute atoms in the & alpha;-Al matrix, which significantly enhanced the solid solution strengthening effect. With the LPBF processing parameters of a combination of a laser power of 250 W, a laser scanning speed of 833 mm/s, and stripe scanning mode, the tensile strength of the alloy reached 401.4 & PLUSMN; 5.7 MPa, which was significantly higher than that of the cast alloys with aging treatment (281.1 & PLUSMN; 1.3 MPa). The heat treatment promoted the formation of secondary Al-3(Sc,Zr), Mn/Mg-rich phases. The ultimate tensile strength and elongation at fracture after aging at 325 & DEG;C for 2 h were 536.0 & PLUSMN; 1.7 MPa and 14.8 & PLUSMN; 0.8%, respectively. The results provide insight into the preparation of aluminum alloys with relatively low cost and excellent mechanical properties.
引用
收藏
页数:14
相关论文
共 50 条
  • [1] Recrystallization of Al-Mg-Sc-Zr alloys
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2002, 31 (03):
  • [2] Recrystallization of Al-Mg-Sc-Zr alloys
    Zhang, YH
    Yin, ZM
    Zhang, J
    Pan, QL
    Peng, ZH
    RARE METAL MATERIALS AND ENGINEERING, 2002, 31 (03) : 167 - 170
  • [3] Evolution of texture, microstructure, tensile strength and corrosion properties of annealed Al-Mg-Sc-Zr alloys
    Fang, Hongjie
    Liu, Hui
    Yan, Yang
    Luo, Xier
    Xu, Xiangchun
    Chu, Xin
    Lu, Yujiao
    Yu, Kun
    Wang, Diangang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 804
  • [4] MECHANICAL PROPERTIES OF AL-MG-SC-ZR ALLOYS AT CRYOGENIC AND AMBIENT TEMPERATURES
    Zhemchuzhnikova, Darya
    Mogucheva, Anna
    Kaibyshev, Rustam
    PROCEEDINGS OF THE 13TH INTERNATIONAL CONFERENCE ON ALUMINUM ALLOYS (ICAA13), 2012, : 879 - 884
  • [5] Microstructure of differently treated Al-Mg-Sc-Zr alloys
    Central South Univ of Technology, Changsha, China
    J Cent South Univ Technol Eng Ed, 1 (24-27):
  • [6] Microstructure of differently treated Al-Mg-Sc-Zr alloys
    Jie Zhang
    Zhimin Yin
    Yonghong Zhang
    Yongzheng Gao
    Qinglin Pan
    Journal of Central South University of Technology, 1997, 4 (1): : 24 - 27
  • [7] Tensile property of Al-Mg-Sc-Zr alloy at cryogenic temperature
    Zhao, W. T.
    Yan, D. S.
    Li, X. Y.
    Rong, L. J.
    Li, Y. Y.
    ADVANCES IN CRYOGENIC ENGINEERING, VOL 52A & 52B, 2006, 824 : 169 - +
  • [8] Study on Microstructure and High-Temperature Mechanical Properties of Al-Mg-Sc-Zr Alloy Processed by LPBF
    Ren, Zhihao
    Zhang, Hao
    Shu, Xuedao
    Xu, Haijie
    Chen, Siyuan
    Ding, Yaoyao
    Liang, Liwen
    Qiu, Zixiang
    Yang, Yang
    Zheng, Yongjian
    METALS, 2024, 14 (08)
  • [9] Properties and Microstructure of Novel Al-Mg-Sc-Zr Alloy
    Guo Q.
    Xu G.
    Huang J.
    Yin Z.
    Deng Y.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2019, 43 (03): : 255 - 264
  • [10] Effects of Al3(Sc,Zr) and Shear Band Formation on the Tensile Properties and Fracture Behavior of Al-Mg-Sc-Zr Alloy
    Hongfeng Huang
    Feng Jiang
    Jiang Zhou
    Lili Wei
    Jiping Qu
    Lele Liu
    Journal of Materials Engineering and Performance, 2015, 24 : 4244 - 4252