Research on high temperature wear resistance mechanism of CrN/CrAlN multilayer coatings

被引:17
|
作者
Wang, Di [1 ,2 ]
Lin, Song-sheng [2 ]
Lu, Jin-de [2 ]
Huang, Shu-qi [2 ]
Yin, Zhi-fu [1 ]
Yang, Hong-zhi [2 ]
Bian, Pei-ying [1 ]
Zhang, Yun-liang [1 ]
Dai, Ming-jiang [2 ]
Zhou, Ke-song [2 ]
机构
[1] Xian Univ, Xian Key Lab Intelligent Addit Mfg Technol, Shaanxi Key Lab Surface Engn & Remfg, Xian 710065, Peoples R China
[2] Guangdong Acad Sci, Inst New Mat, Natl Engn Lab Modern Mat Surface Engn Technol, Key Lab Guangdong Modern Surface Engn Technol, Guangzhou 510651, Peoples R China
关键词
Multilayer coating; High-temperature wear resistance; Oxidative wear; Failure mechanism; CRALN COATINGS; MICROSTRUCTURE;
D O I
10.1016/j.triboint.2022.108184
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
In this paper, a 16 mu m CrN/CrAlN multilayer coating is prepared on the titanium alloy surface via arc ion plating. Since titanium alloys are susceptible to wear in a high-temperature environment, high-temperature wear performance and mechanism after coating are investigated. The results show that the friction coefficient of the CrN/CrAlN multilayer coating decreases with an increase in temperature during wear tests at room temperature, 300 degrees C, 500 degrees C, and 700 degrees C. Moreover, the friction coefficient decreases from 0.9 at room temperature to 0.4 at 700 degrees C. The wear rate increases with the temperature, more specifically from 1.32 x 10(-5) mm(3)/(N.m) at room temperature to 6.45 x 10(-5) mm(3)/(N.m) at 700 degrees C.
引用
收藏
页数:8
相关论文
共 50 条
  • [41] Preparation and Wear Properties of Cr/CrAlN Coatings with Different Multilayer Structures on the Titanium Alloy Surface
    Zhang X.
    Cai X.
    Cai F.
    Zhang S.
    Chen L.
    Cailiao Daobao/Materials Reports, 2022, 36 (15):
  • [42] Investigation of high temperature wear resistance of TiCrAlCN/TiAlN multilayer coatings over M2 steel
    Sukuroglu, E. E.
    Baran, O.
    Totik, Y.
    Efeoglu, I.
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2018, 32 (13) : 1428 - 1436
  • [43] Evaluating mechanical properties and crack resistance of CrN, CrTiN, CrAlN and CrTiAlN coatings by nanoindentation and scratch tests
    Wang, Qianzhi
    Zhou, Fei
    Yan, Jiwang
    SURFACE & COATINGS TECHNOLOGY, 2016, 285 : 203 - 213
  • [44] Microstructure and high temperature tribological properties of arc ion plated CrN and CrAlN coatings on AISI H13 steel
    Zhang, Long
    Zhang, Kaiwei
    Kong, Dejun
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2025, 77 (02) : 271 - 280
  • [45] Evaluation of wear resistance of CrN, CrAlN, and TiAlN coatings deposited by multi-arc ion plating on spinning die of Cr12MoV
    Lin, Rongchuan
    Sun, Shilong
    You, Bin
    Dong, Tianlei
    Sui, Yusheng
    Wei, Shasha
    MATERIALS RESEARCH EXPRESS, 2024, 11 (09)
  • [46] Impact wear and abrasion resistance of CrN, AlCrN and AlTiN PVD coatings
    Mo, J. L.
    Zhu, M. H.
    Leyland, A.
    Matthews, A.
    SURFACE & COATINGS TECHNOLOGY, 2013, 215 : 170 - 177
  • [47] The Improvement of CrN Coatings Wear Resistance by Adjusting the Cycle Number of Electrochemical
    Wang, Xin
    Wang, Qianzhi
    Zhou, Fei
    Kong, Jizhou
    Zhou, Zhifeng
    LUBRICANTS, 2024, 12 (08)
  • [48] The effect of duty cycle on the mechanical and electrochemical corrosion properties of multilayer CrN/CrAlN coatings produced by cathodic arc evaporation
    Baseri, Niloofar Arab
    Mohammadi, Majid
    Ghatee, Mojtaba
    Abassi-Firouzjah, Marzieh
    Elmkhah, Hassan
    SURFACE ENGINEERING, 2021, 37 (02) : 253 - 262
  • [49] Corrosion-wear behaviour of PVD Cr/CrN multilayer coatings for gear applications
    Bayon, R.
    Igartua, A.
    Fernandez, X.
    Martinez, R.
    Rodriguez, R. J.
    Garcia, J. A.
    de Frutos, A.
    Arenas, M. A.
    de Damborenea, J.
    TRIBOLOGY INTERNATIONAL, 2009, 42 (04) : 591 - 599
  • [50] Research of high hardness and wear resistance arc sprayed coatings
    Fang, Jian-Jun
    Qin, Hao
    Li, Zhuo-Xin
    Jiang, Jian-Min
    Shi, Yao-Wu
    Cailiao Gongcheng/Journal of Materials Engineering, 2008, (02): : 27 - 30