Research on high temperature wear resistance mechanism of CrN/CrAlN multilayer coatings

被引：17

作者：

Wang, Di ^{[1
,2
]}

Lin, Song-sheng ^{[2
]}

Lu, Jin-de ^{[2
]}

Huang, Shu-qi ^{[2
]}

Yin, Zhi-fu ^{[1
]}

Yang, Hong-zhi ^{[2
]}

Bian, Pei-ying ^{[1
]}

Zhang, Yun-liang ^{[1
]}

Dai, Ming-jiang ^{[2
]}

Zhou, Ke-song ^{[2
]}

机构：

[1] Xian Univ, Xian Key Lab Intelligent Addit Mfg Technol, Shaanxi Key Lab Surface Engn & Remfg, Xian 710065, Peoples R China

[2] Guangdong Acad Sci, Inst New Mat, Natl Engn Lab Modern Mat Surface Engn Technol, Key Lab Guangdong Modern Surface Engn Technol, Guangzhou 510651, Peoples R China

来源：

TRIBOLOGY INTERNATIONAL | 2023年 / 180卷

关键词：

Multilayer coating; High-temperature wear resistance; Oxidative wear; Failure mechanism; CRALN COATINGS; MICROSTRUCTURE;

D O I：

10.1016/j.triboint.2022.108184

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper, a 16 mu m CrN/CrAlN multilayer coating is prepared on the titanium alloy surface via arc ion plating. Since titanium alloys are susceptible to wear in a high-temperature environment, high-temperature wear performance and mechanism after coating are investigated. The results show that the friction coefficient of the CrN/CrAlN multilayer coating decreases with an increase in temperature during wear tests at room temperature, 300 degrees C, 500 degrees C, and 700 degrees C. Moreover, the friction coefficient decreases from 0.9 at room temperature to 0.4 at 700 degrees C. The wear rate increases with the temperature, more specifically from 1.32 x 10(-5) mm(3)/(N.m) at room temperature to 6.45 x 10(-5) mm(3)/(N.m) at 700 degrees C.

引用

页数：8

共 50 条

[31] Thermal shock resistance of Cr/CrN/Cr/CrAlN multilayer anti-erosion coating
Wang, Di
Lin, Song-sheng
Duan, Dan-yuzi
Liu, Ming-xia
Yin, Zhi-fu
Qiu, Yun
Ye, Fang-xia
Dai, Ming-jiang
Yang, Hong-zhi
Zhou, Ke-song
SURFACE & COATINGS TECHNOLOGY, 2023, 470
[32] Effect of Annealing Temperature on Tribological Properties and Material Transfer Phenomena of CrN and CrAlN Coatings
Wang, Linlin
Nie, X.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (02) : 560 - 571
[33] Self-lubricating CrAlN/VN multilayer coatings at room temperature
Qiu, Yuexiu
Zhang, Sam
Lee, Jyh-Wei
Li, Bo
Wang, Yuxi
Zhao, Dongliang
APPLIED SURFACE SCIENCE, 2013, 279 : 189 - 196
[34] High temperature tribological performance of CrAlYN/CrN nanoscale multilayer coatings deposited on γ-TiAl
Walker, J. C.
Ross, I. M.
Reinhard, C.
Rainforth, W. M.
Hovsepian, P. Eh.
WEAR, 2009, 267 (5-8) : 965 - 975
[35] Thermal stability and oxidation resistance of TiAlN/CrN multilayer coatings
Sheffield Hallam Univ, Sheffield, United Kingdom
Surf Coat Technol, 1-3 (315-321):
[36] Architecture of Multilayer Cr/CrN Coatings for Wear Protection in Seawater: Cr/CrN Ratio and Total Thickness
Shan, Lei
Wang, Yongxin
Li, Jinlong
Jiang, Xin
Chen, Jianmin
TRIBOLOGY TRANSACTIONS, 2015, 58 (05) : 914 - 923
[37] High temperature tribology of CrN and multilayered Cr/CrN coatings
Polcar, T.
Martinez, R.
Vitu, T.
Kopecky, L.
Rodriguez, R.
Cavaleiro, A.
SURFACE & COATINGS TECHNOLOGY, 2009, 203 (20-21): : 3254 - 3259
[38] Effect of Ni Content on Wear Resistance Performance of CrN Coatings
Zhou S.
Zhou X.
Wang Z.
Wang R.
Ma G.
Wang A.
Ke P.
Surface Technology, 2024, 53 (11): : 45 - 58
[39] Oxidation resistance of TiN, CrN, TiAlN and CrAlN coatings deposited by lateral rotating cathode arc
Chim, Y. C.
Ding, X. Z.
Zeng, X. T.
Zhang, S.
THIN SOLID FILMS, 2009, 517 (17) : 4845 - 4849
[40] WEAR RESISTANCE OF STELLITE 6 COATINGS AT HIGH TEMPERATURE
Kumar, Mukund
Kumar, Satish
SURFACE REVIEW AND LETTERS, 2024, 31 (12)

← 1 2 3 4 5 →