Fretting-fatigue of shrink fit lug-bush assemblies: Interference-fit effect

被引:4
|
作者
Le Falher, M. [1 ,2 ,3 ]
Fouvry, S. [1 ]
Arnaud, P. [2 ]
Maurel, V. [2 ]
Antoni, N. [4 ]
Billardon, R. [3 ]
机构
[1] Ecole Cent Lyon, Lab Tribol & Dynam Syst LTDS, Ecully, France
[2] Mines Paris ParisTech, Ctr Mat, Evry, France
[3] Safran Transmiss Syst, Colombes, France
[4] Safran Landing Syst, Velizy Villacoublay, France
关键词
Fretting; Fatigue; Lug-bush; Interference-fit; Ti-6Al-4V; MAXIMUM EQUIVALENT STRESS; PIN-LOADED LUG; FAILURE-MECHANISM; TI-6AL-4V; WEAR; FRICTION; JOINTS; LIFE;
D O I
10.1016/j.triboint.2023.108581
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
The fretting-fatigue behaviour of shrink fit lug-bush assemblies is investigated. In this paper, experimental fa-tigue tests are carried out on lug-bush specimens with three different levels of interference fit. It is observed that the relative movements of fretting induce tribo-oxidation phenomena at the shrink-fit interface and that the crack initiation sites correspond well to the oxides formation spots. The increase in the fatigue life with interference fit is consistent with stress analysis considering the SWT multiaxial fatigue criterion, but the predicted fatigue life is not conservative relative to material reference data. In order to account for fretting surface damage, different approaches are investigated considering homogeneous and heterogeneous distributions of the coefficient of friction.
引用
收藏
页数:18
相关论文
共 48 条
  • [21] Effect of CF/PEEK plasticity behavior on the mechanical performance of interference-fit joint
    Yao, Chenxi
    Qi, Zhenchao
    Chen, Wenliang
    Zhang, Chenqun
    POLYMER COMPOSITES, 2021, 42 (05) : 2574 - 2588
  • [22] Fretting behaviors of interface between CFRP and coated titaniumalloy in composite interference-fit joints under service condition
    Hu, Junshan
    Zhang, Kaifu
    Yang, Qingda
    Cheng, Hui
    Liu, Shunuan
    Yang, Yu
    MATERIALS & DESIGN, 2017, 134 : 91 - 102
  • [23] Fretting fatigue tests on shrink-fit specimens and investigations into the strength enhancement induced by deep rolling
    Bertini, L.
    Santus, C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 81 : 179 - 190
  • [24] Fatigue performance of bonded crack retarders in the presence of cold worked holes and interference-fit fasteners
    Syed, Abdul Khadar
    Zhang, Xiang
    Moffatt, James E.
    Maziarz, Robert
    Castelletti, Luigi
    Fitzpatrick, Michael E.
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 105 : 111 - 118
  • [25] Effect of Laser Surface Texturing on Fretting Damage of Interference Fit Interface
    Yin, Chaochao
    Huang, Haihong
    Zhou, Dan
    Liu, Zhifeng
    Mocaxue Xuebao/Tribology, 2023, 43 (12): : 1478 - 1485
  • [26] Predicting fretting-fatigue endurance of rotating bending shrink-fitted assemblies using a sequential RUIZ-SWT approach: The effect of entrapped debris layer
    Dieu, B.
    Fouvry, S.
    Doquet, V.
    Bridier, F.
    TRIBOLOGY INTERNATIONAL, 2023, 186
  • [27] Fatigue life of cold-expanded fastener holes with interference-fit fasteners at short edge margins
    Vallieres, G. M.
    Duquesnay, D. L.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (05) : 574 - 582
  • [28] Fatigue enhancement by interference-fit in a pin-loaded glass fibre-reinforced plastics laminate
    Kim, S-Y
    Hennigan, D. J.
    Kim, D.
    Seok, C-S
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART C-JOURNAL OF MECHANICAL ENGINEERING SCIENCE, 2012, 226 (C6) : 1437 - 1446
  • [29] Multiaxial fatigue analysts of interference-fit steel fasteners in aluminum at 2024-T3 specimens
    Shatil, G
    Page, AG
    FATIGUE AND FRACTURE MECHANICS: 33RD VOLUME, 2003, 1417 : 192 - 208
  • [30] Effect of radial interference on torque capacity of press- and shrink-fit gears
    Chu, S. J.
    Jeong, T. K.
    Jung, E. H.
    INTERNATIONAL JOURNAL OF AUTOMOTIVE TECHNOLOGY, 2016, 17 (05) : 763 - 768