Structure Formation in Friction Welding of Eutectic AlSi Alloys.

被引：0
|
作者：
Tensi, H.M.
Schwalm, M.
Welz, W.
机构：
来源：
Metall | 1983年 / 37卷 / 06期
关键词：
WELDING; -; Friction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The formation and development of friction welding structures have been investigated on samples of an eutectic aluminum-silicon alloy. Structure formation zones were identified by studying the morphology of the friction surfaces and by temperature measurements. Silicon plates were revealed which influence the mechanical properties of friction welds.
引用
收藏
页码：593 / 597
相关论文
共 50 条
  • [21] Spot Mig Welding of Aluminum Alloys.
    Andric, Simun
    1984, (27)
  • [22] Fusion Welding of Aluminium and Aluminium Alloys.
    Cramer, Karl
    1600, (118):
  • [23] WELDING OF COPPER AND COPPER BASE ALLOYS.
    Dawson, R.J.C.
    Welding Research Council Bulletin, 1983,
  • [24] Application of Projection Welding to Aluminum Alloys.
    Opprecht, J.
    Aluminium Dusseldorf, 1980, 56 (11): : 723 - 725
  • [25] ROLL WELDING GRIDS OF TITANIUM ALLOYS.
    Tret'yakov, A.F.
    Polushkin, G.P.
    Kharitonova, L.K.
    Borisov, A.Ya.
    Gertsik, M.A.
    Vlasov, E.V.
    Welding Production (English translation of Svarochnoe Proizvodstvo), 1984, 31 (07): : 35 - 37
  • [26] HOT PRESSURE WELDING OF ALUMINUM ALLOYS.
    Metzger, G.E.
    Welding Journal (Miami, Fla), 1978, 57 (01): : 37 - 43
  • [27] PLASMA WELDING OF COPPER AND ITS ALLOYS.
    Bolotnikov, A.L.
    Danilov, A.I.
    Soviet electrical engineering, 1982, 53 (05): : 22 - 29
  • [28] The inner structure of alloys.
    Rosenhain, W
    JOURNAL OF THE INSTITUTE OF METALS, 1923, 30 (01): : 3 - 26
  • [29] DIRECTIONAL SOLIDIFICATION OF EUTECTIC ALLOYS WITH LAMELLAR STRUCTURE FORMATION
    PETUKHOV, II
    DOKLADY AKADEMII NAUK SSSR, 1981, 257 (04): : 867 - 871
  • [30] PECULIARITIES OF THE FINE STRUCTURE AND COMPOSITION OF THE EUTECTIC gamma prime -PHASE IN HIGH NICKEL ALLOYS.
    Kishkin, S.T.
    Kuleshova, Ye.A.
    Logunov, A.V.
    Sorokina, L.P.
    Astaf'eva, Ye.V.
    Physics of Metals and Metallography, 1984, 57 (05): : 106 - 110
12345