INFLUENCE OF GRAPHITE FORM ON HYDRAULIC SOUNDNESS OF CAST IRON.

被引：0

作者：

Chernyshova, N.V.

Ezhov, G.I.

Boiko, G.G.

机构：

来源：

Soviet Castings Technology (English Translation of Liteinoe Proizvodstvo) | 1986年 / 02期

关键词：

CASTINGS - Physical Properties - STEEL TESTING - Fracture;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Comparative hydraulic soundness tests have been carried out on iron castings with different graphite forms, produced by the in-mold treatment process using 0. 2-1% of master alloy ZhKMK-4R, which contains 8. 3% Mg, 9. 2% Ca, 6. 7% REM, 47% Si, and remainder Fe. The original steelmaking pig iron contained 4. 13% C, 1. 05% Si, 1. 04% Mn, 0. 087% P, 0. 031% S, and melts were made in an acid-lined induction furnace of capacity 60 kg. The bath was heated to 1500 degree C and the molds were poured at 1450 degree C. The cylindrical castings - 30-mm diameter test bars of length 200 mm - were made in baked clay-bonded sand molds. The nodular graphite form ensures maximum hydraulic soundness.

引用

页码：31 / 32

共 50 条

[41] Tests with cast iron.
Bach, C
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1908, 52 : 2061 - 2065
[42] CHART OF FATIGUE CRACK PROPAGATION MECHANISM FOR NODULAR GRAPHITE CAST IRON.
Hu, Zhizhong
Guo, Dazhan
An, Renje
Jinshu Xuebao/Acta Metallurgica Sinica, 1986, 22 (01):
[43] Twelfth Annual Summary of Recent Literature on Nodular Graphite Cast Iron.
Wolters, Diether
Giesserei, 1975, 62 (15): : 404 - 415
[44] SOLUTION OF GRAPHITE IN GAMMA PHASE DURING INDUCTION HEATING OF CAST IRON.
Yakovlev, F.I.
Metal Science and Heat Treatment, 1975, 17 (11-12) : 1033 - 1034
[45] MANUFACTURE OF METALLURGICAL INGOT MOLDS FROM SPHEROIDAL GRAPHITE CAST IRON.
Senkevich, Yu.I.
Lerner, Yu.S.
Lysak, V.I.
Soviet Castings Technology (English Translation of Liteinoe Proizvodstvo), 1987, (09): : 47 - 50
[46] EFFECTS OF SULFUR ON THE NUCLEATION AND GROWTH OF GRAPHITE OUT OF RESIDUAL GRAPHITE PARTICLES IN MOLTEN CAST IRON.
Kayama, Nobutaro
Suzuki, Katsumi
Report of the Castings Research Laboratory, Waseda University, 1981, (32): : 25 - 31
[47] MECHANISM BY WHICH SURFACE-ACTIVE ELEMENTS INFLUENCE FORM OF GRAPHITE IN CAST IRON
SIDORENKO, RA
RUSSIAN METALLURGY-METALLY-USSR, 1967, (02): : 77 - +
[48] Influence of Over-Cooling the Nodular Cast Iron to the Graphite Form in the Surface Layer
Hosadyna, M.
Dobosz, St. M.
Kusinski, J.
ARCHIVES OF FOUNDRY ENGINEERING, 2012, 12 (01) : 43 - 46
[49] COMPARISON OF MECHANICAL PROPERTIES OF CAST IRON WITH SPHEROIDAL GRAPHITE AND MAGNESIUM-TREATED MALLEABLE IRON.
Lepand, H.
Komp, V.
Jahnkow, H.
International cast metals journal, 1980, 5 (01): : 60 - 65
[50] MELTING AND CASTING CONDITIONS NECESSARY FOR ROSETTE GRAPHITE FORMATION IN GRAY CAST IRON.
Kikuchi, Masao
Ohsawa, Yoshiaki
Kasai, Hiroshi
Toyoda, Atsushi
Transactions of National Research Institute for Metals (Tokyo), 1986, 28 (01): : 40 - 50

← 1 2 3 4 5 →