MELTING AND CASTING CONDITIONS NECESSARY FOR ROSETTE GRAPHITE FORMATION IN GRAY CAST IRON.

被引：0
|
作者：
Kikuchi, Masao
Ohsawa, Yoshiaki
Kasai, Hiroshi
Toyoda, Atsushi
机构：
来源：
Transactions of National Research Institute for Metals (Tokyo) | 1986年 / 28卷 / 01期
关键词：
FOUNDRY PRACTICE - Casting;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Experinmental work was done to determine the melting and casting conditions necessary for the formation of B-type rosette graphite groupings in gray cast iron. The results gained are summarized as follows. (1) The optimum chemical composition of the five main components to obtain rosette graphites was 3. 45%C, 2. 25%Si, 0. 40%Mn, 0. 54%P and 0. 12%S. (2) More rosette graphite were found in specimens with lower maximum melting temperatures and lower pouring temperatures. (3) The distance between each rosette graphite grouping was increased due to a vanadium addition.
引用
收藏
页码：40 / 50
相关论文
共 50 条
  • [1] MELTING AND CASTING CONDITIONS NECESSARY FOR ROSETTE GRAPHITE FORMATION IN GRAY CAST-IRON
    KIKUCHI, M
    OHSAWA, Y
    KASAI, H
    TOYODA, A
    TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1986, 28 (01): : 40 - 50
  • [2] FORMATION OF SPHEROIDAL GRAPHITE IN CAST IRON.
    Anikin, A.A.
    Kireev, N.N.
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1984, 26 (11-12): : 839 - 842
  • [3] Influence of Hypereutectic Graphite on the Solidification of Gray Cast Iron.
    Sun, G.X
    Loper Jr., C.R.
    Giessereipraxis, 1985, (07): : 89 - 95
  • [4] GRAPHITE FORMATION PROCESSES IN SYNTHETIC CAST IRON.
    Kogan, L.B.
    Ivakhnenko, I.S.
    1600,
  • [5] LASER SURFACE MELTING TREATMENT OF NODULAR GRAPHITE CAST IRON.
    Xie Shum-ing
    Fan Yi
    Huang Man-hui
    Jinshu Rechuli/Heat Treatment of Metals, 1987, (11): : 19 - 23
  • [6] NORMALIZATION OF GRAY CAST IRON.
    Savinovskii, G.K.
    Chuchuchina, M.A.
    Kokhov, S.F.
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1984, 26 (1-2): : 151 - 152
  • [7] BRAZING OF GRAY CAST IRON.
    Riad, S.M.
    El-Naggar, A.
    Welding Journal (Miami, Fla), 1981, 60 (10): : 22 - 24
  • [8] Rotary Drum Furnace for Melting and Duplexing of Gray and Malleable Cast Iron.
    Mittmann, Edwin
    Giesserei, 1979, 66 (04): : 85 - 88
  • [9] GRAPHITE GROWTH IN CAST IRON.
    McSwain, R.H.
    Bates, C.E.
    AFS International Cast Metals Journal, 1976, 1 (01): : 53 - 57
  • [10] Properties of gray cast iron as affected by casting conditions
    Saeger, CM
    Ash, EJ
    BUREAU OF STANDARDS JOURNAL OF RESEARCH, 1934, 13 (4/6): : 573 - 577
12345